Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_82_2_13911_fbNDEx.cif"

There are 10 T-atoms per unit cell
There are 20 O-atoms per unit cell

Framework density = 15.71 T-atoms per nm^3
Material density = 1.567 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5998 Angstrom
T1  -- O2  = 1.6185 Angstrom
T1  -- O3  = 1.6399 Angstrom
T1  -- O2  = 1.6185 Angstrom
      mean = 1.6192 Angstrom
        t1 = 0.022025  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.025041  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6270 Angstrom
T2  -- O3  = 1.6270 Angstrom
T2  -- O3  = 1.6270 Angstrom
T2  -- O3  = 1.6270 Angstrom
      mean = 1.6270 Angstrom
        t1 = 0.010987  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002344  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5998 A <--> 1.6399 A
          Mean   = 1.6207 A
          StdDev = 0.0132 A

       t1 Range  = 0.0110 <-- 0.0165 --> 0.0220
       t2 Range  = 0.0023 <-- 0.0137 --> 0.0250

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.507 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 104.078 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 108.507 deg; O1  -- O2  = 3 A
O2  -- T1  -- O3  = 112.570 deg; O2  -- O3  = 3 A
O2  -- T1  -- O2  = 110.285 deg; O2  -- O2  = 3 A
O3  -- T1  -- O2  = 112.570 deg; O3  -- O2  = 3 A
       104.078 deg <-- 109.419 deg --> 112.570 deg

O3  -- T2  -- O3  = 110.167 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 109.124 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 109.124 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 109.124 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 109.124 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 110.167 deg; O3  -- O3  = 3 A
       109.124 deg <-- 109.472 deg --> 110.167 deg

        O-T-O SUMMARY
          Range  = 104.0777 deg <--> 112.5700 deg
          Mean   = 109.4456 deg
          StdDev = 2.0978 deg

        O--O SUMMARY
          Range  = 2.5544 A <--> 2.7104 A
          Mean   = 2.6497 A
          StdDev = 0.0411 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  59.601 deg; T1  -- T2  = 2.9709 A
T1  - O1  - T1  - O3  - T1  = 131.491 deg; T1  -- T1  = 5.5957 A
T1  - O1  - T1  - O2  - T1  = 131.491 deg; T1  -- T1  = 5.5957 A
T2  - O2  - T1  - O3  - T1  = 129.550 deg; T2  -- T1  = 5.5200 A
T2  - O2  - T1  - O2  - T1  = 129.550 deg; T2  -- T1  = 5.5200 A
T1  - O3  - T1  - O2  - T1  =  82.981 deg; T1  -- T1  = 4.1480 A

T1  - O3  - T2  - O3  - T1  =  60.798 deg; T1  -- T1  = 3.0066 A
T1  - O3  - T2  - O3  - T1  = 138.068 deg; T1  -- T1  = 5.5484 A
T1  - O3  - T2  - O3  - T1  = 138.068 deg; T1  -- T1  = 5.5484 A
T1  - O3  - T2  - O3  - T1  = 138.068 deg; T1  -- T1  = 5.5484 A
T1  - O3  - T2  - O3  - T1  = 138.068 deg; T1  -- T1  = 5.5484 A
T1  - O3  - T2  - O3  - T1  =  60.798 deg; T1  -- T1  = 3.0066 A

        T-T-T SUMMARY
          Range  = 59.6008 deg <--> 138.0683 deg
          Mean   = 111.5443 deg
          StdDev = 32.9880 deg

        T--T SUMMARY
          Range  = 2.9709 A <--> 5.5957 A
          Mean   = 4.7964 A
          StdDev = 1.1144 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 140.000 deg ; T1  -- T1   3.0066 A

T1  -- O2  -- T1  = 150.527 deg ; T1  -- T1   3.1305 A

T1  -- O3  -- T2  = 130.839 deg ; T1  -- T2   2.9709 A


        T-O-T SUMMARY
          Range  = 130.8387° <--> 150.5271 deg
          Mean   = 140.4553 deg
          StdDev = 8.2172 deg

        T--T SUMMARY
          Range  = 2.9709 A <--> 3.1305 A
          Mean   = 3.0360 A
          StdDev = 0.0699 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 19 40 55 80 115 138 183 229 260 328 382 421 515 574
TD10 = 873
Circuit symbol = 3.4.8.9_{5}.8.9_{5}
Weight = 31
Vertex symbol  = 3.4.8.9_{4}.8.9_{4}
Weight = 31

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 8 20 40 52 82 116 132 184 236 252 322 396 416 500 592
TD10 = 875
Circuit symbol = 3.3.9_{4}.9_{4}.9_{4}.9_{4}
Weight = 37
Vertex symbol  = 3.3.9_{4}.9_{4}.9_{4}.9_{4}
Weight = 37

<TD10> = 873.400
Average ring size = 7.0714