Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_82_2_13792_okoyr6.cif"

There are 10 T-atoms per unit cell
There are 20 O-atoms per unit cell

Framework density = 15.84 T-atoms per nm^3
Material density = 1.580 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6243 Angstrom
T1  -- O2  = 1.6145 Angstrom
T1  -- O2  = 1.6145 Angstrom
T1  -- O3  = 1.6335 Angstrom
      mean = 1.6217 Angstrom
        t1 = 0.007787  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002672  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6227 Angstrom
T2  -- O3  = 1.6227 Angstrom
T2  -- O3  = 1.6227 Angstrom
T2  -- O3  = 1.6227 Angstrom
      mean = 1.6227 Angstrom
        t1 = 0.010436  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005259  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6145 A <--> 1.6335 A
          Mean   = 1.6219 A
          StdDev = 0.0072 A

       t1 Range  = 0.0078 <-- 0.0091 --> 0.0104
       t2 Range  = 0.0027 <-- 0.0040 --> 0.0053

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.166 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 109.196 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.368 deg; O1  -- O3  = 3 A
O2  -- T1  -- O2  = 110.638 deg; O2  -- O2  = 3 A
O2  -- T1  -- O3  = 109.772 deg; O2  -- O3  = 3 A
O2  -- T1  -- O3  = 109.660 deg; O2  -- O3  = 3 A
       108.368 deg <-- 109.467 deg --> 110.638 deg

O3  -- T2  -- O3  = 107.926 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 110.249 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 110.249 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 110.249 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 110.249 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 107.926 deg; O3  -- O3  = 3 A
       107.926 deg <-- 109.475 deg --> 110.249 deg

        O-T-O SUMMARY
          Range  = 107.9263 deg <--> 110.6384 deg
          Mean   = 109.4708 deg
          StdDev = 0.9208 deg

        O--O SUMMARY
          Range  = 2.6244 A <--> 2.6626 A
          Mean   = 2.6490 A
          StdDev = 0.0139 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 131.988 deg; T1  -- T1  = 5.5726 A
T1  - O1  - T1  - O2  - T2  =  60.144 deg; T1  -- T2  = 2.9740 A
T1  - O1  - T1  - O3  - T1  = 132.967 deg; T1  -- T1  = 5.5936 A
T1  - O2  - T1  - O2  - T2  = 126.171 deg; T1  -- T2  = 5.4510 A
T1  - O2  - T1  - O3  - T1  =  84.956 deg; T1  -- T1  = 4.2392 A
T2  - O2  - T1  - O3  - T1  = 126.617 deg; T2  -- T1  = 5.4618 A

T1  - O3  - T2  - O3  - T1  =  59.712 deg; T1  -- T1  = 2.9610 A
T1  - O3  - T2  - O3  - T1  = 138.779 deg; T1  -- T1  = 5.5672 A
T1  - O3  - T2  - O3  - T1  = 138.779 deg; T1  -- T1  = 5.5672 A
T1  - O3  - T2  - O3  - T1  = 138.779 deg; T1  -- T1  = 5.5672 A
T1  - O3  - T2  - O3  - T1  = 138.779 deg; T1  -- T1  = 5.5672 A
T1  - O3  - T2  - O3  - T1  =  59.712 deg; T1  -- T1  = 2.9610 A

        T-T-T SUMMARY
          Range  = 59.7124 deg <--> 138.7787 deg
          Mean   = 111.4486 deg
          StdDev = 33.0955 deg

        T--T SUMMARY
          Range  = 2.9610 A <--> 5.5936 A
          Mean   = 4.7902 A
          StdDev = 1.1184 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 131.416 deg ; T1  -- T1   2.9610 A

T1  -- O2  -- T1  = 152.836 deg ; T1  -- T1   3.1387 A

T1  -- O3  -- T2  = 131.938 deg ; T1  -- T2   2.9740 A


        T-O-T SUMMARY
          Range  = 131.4161° <--> 152.8359 deg
          Mean   = 138.7299 deg
          StdDev = 10.1913 deg

        T--T SUMMARY
          Range  = 2.9610 A <--> 3.1387 A
          Mean   = 3.0246 A
          StdDev = 0.0826 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 19 40 55 80 115 138 183 229 260 328 382 421 515 574
TD10 = 873
Circuit symbol = 3.4.8.9_{5}.8.9_{5}
Weight = 31
Vertex symbol  = 3.4.8.9_{4}.8.9_{4}
Weight = 31

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 8 20 40 52 82 116 132 184 236 252 322 396 416 500 592
TD10 = 875
Circuit symbol = 3.3.9_{4}.9_{4}.9_{4}.9_{4}
Weight = 37
Vertex symbol  = 3.3.9_{4}.9_{4}.9_{4}.9_{4}
Weight = 37

<TD10> = 873.400
Average ring size = 7.0714