Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_74_3_901026_4gxmpj.cif"

There are 48 T-atoms per unit cell
There are 96 O-atoms per unit cell

Framework density = 24.47 T-atoms per nm^3
Material density = 2.442 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6553 Angstrom
T1  -- O2  = 1.6038 Angstrom
T1  -- O3  = 1.6041 Angstrom
T1  -- O4  = 1.6239 Angstrom
      mean = 1.6218 Angstrom
        t1 = 0.073870  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.066749  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6314 Angstrom
T2  -- O5  = 1.6240 Angstrom
T2  -- O6  = 1.6384 Angstrom
T2  -- O7  = 1.6285 Angstrom
      mean = 1.6306 Angstrom
        t1 = 0.015854  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006479  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6393 Angstrom
T3  -- O7  = 1.6261 Angstrom
T3  -- O8  = 1.6187 Angstrom
T3  -- O9  = 1.6155 Angstrom
      mean = 1.6249 Angstrom
        t1 = 0.013582  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006287  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6038 A <--> 1.6553 A
          Mean   = 1.6257 A
          StdDev = 0.0141 A

       t1 Range  = 0.0136 <-- 0.0344 --> 0.0739
       t2 Range  = 0.0063 <-- 0.0265 --> 0.0667

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 119.565 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 119.182 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.041 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 114.634 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  =  93.260 deg; O2  -- O4  = 2 A
O3  -- T1  -- O4  =  93.943 deg; O3  -- O4  = 2 A
       93.260 deg <-- 108.104 deg --> 119.565 deg

O4  -- T2  -- O5  = 109.328 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.676 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 110.001 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 107.993 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 107.895 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 111.880 deg; O6  -- O7  = 3 A
       107.895 deg <-- 109.462 deg --> 111.880 deg

O6  -- T3  -- O7  = 112.161 deg; O6  -- O7  = 3 A
O6  -- T3  -- O8  = 108.930 deg; O6  -- O8  = 3 A
O6  -- T3  -- O9  = 108.935 deg; O6  -- O9  = 3 A
O7  -- T3  -- O8  = 109.217 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 108.537 deg; O7  -- O9  = 3 A
O8  -- T3  -- O9  = 109.011 deg; O8  -- O9  = 3 A
       108.537 deg <-- 109.465 deg --> 112.161 deg

        O-T-O SUMMARY
          Range  = 93.2595 deg <--> 119.5651 deg
          Mean   = 108.1872 deg
          StdDev = 6.1902 deg

        O--O SUMMARY
          Range  = 2.3464 A <--> 2.8164 A
          Mean   = 2.6313 A
          StdDev = 0.1142 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  89.918 deg; T1  -- T1  = 4.0414 A
T1  - O1  - T1  - O3  - T2  = 108.177 deg; T1  -- T2  = 4.8291 A
T1  - O1  - T1  - O4  - T1  =  90.082 deg; T1  -- T1  = 4.0414 A
T1  - O2  - T1  - O3  - T2  =  90.790 deg; T1  -- T2  = 4.0332 A
T1  - O2  - T1  - O4  - T1  = 180.000 deg; T1  -- T1  = 5.3999 A
T2  - O3  - T1  - O4  - T1  =  89.210 deg; T2  -- T1  = 3.9723 A

T1  - O4  - T2  - O5  - T3  = 108.143 deg; T1  -- T3  = 4.9737 A
T1  - O4  - T2  - O6  - T2  = 108.176 deg; T1  -- T2  = 4.8014 A
T1  - O4  - T2  - O7  - T3  = 109.726 deg; T1  -- T3  = 5.0013 A
T3  - O5  - T2  - O6  - T2  = 106.827 deg; T3  -- T2  = 4.9462 A
T3  - O5  - T2  - O7  - T3  = 116.686 deg; T3  -- T3  = 5.3999 A
T2  - O6  - T2  - O7  - T3  = 106.969 deg; T2  -- T3  = 4.9295 A

T2  - O6  - T3  - O7  - T3  = 107.767 deg; T2  -- T3  = 5.0033 A
T2  - O6  - T3  - O8  - T3  = 115.798 deg; T2  -- T3  = 5.4254 A
T2  - O6  - T3  - O9  - T2  = 116.686 deg; T2  -- T2  = 5.3999 A
T3  - O7  - T3  - O8  - T3  =  90.000 deg; T3  -- T3  = 4.4057 A
T3  - O7  - T3  - O9  - T2  = 106.031 deg; T3  -- T2  = 4.9265 A
T3  - O8  - T3  - O9  - T2  = 116.026 deg; T3  -- T2  = 5.4102 A

        T-T-T SUMMARY
          Range  = 89.2095 deg <--> 180.0000 deg
          Mean   = 109.6597 deg
          StdDev = 20.5080 deg

        T--T SUMMARY
          Range  = 3.9723 A <--> 5.4254 A
          Mean   = 4.8615 A
          StdDev = 0.4858 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 130.560 deg ; T1  -- T1   3.0072 A

T1  -- O2  -- T1  = 114.363 deg ; T1  -- T1   2.6956 A

T1  -- O3  -- T1  = 114.906 deg ; T1  -- T1   2.7043 A

T1  -- O4  -- T2  = 130.405 deg ; T1  -- T2   2.9551 A

T2  -- O5  -- T2  = 132.509 deg ; T2  -- T2   2.9731 A

T2  -- O6  -- T3  = 152.671 deg ; T2  -- T3   3.1849 A

T2  -- O7  -- T3  = 152.143 deg ; T2  -- T3   3.1589 A

T3  -- O8  -- T3  = 136.536 deg ; T3  -- T3   3.0074 A

T3  -- O9  -- T3  = 170.381 deg ; T3  -- T3   3.2197 A


        T-O-T SUMMARY
          Range  = 114.3626° <--> 170.3811 deg
          Mean   = 137.1638 deg
          StdDev = 17.3646 deg

        T--T SUMMARY
          Range  = 2.6956 A <--> 3.2197 A
          Mean   = 2.9896 A
          StdDev = 0.1800 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.7043 Angstrom
T1  -- T1  = 2.6956 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 38 61 87 118 160 206 249 296 358 430 495 559 638
TD10 = 955
Circuit symbol = 4.6.4.6.6_{2}.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6_{2}
Weight = 19

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 12 25 40 63 95 129 161 198 255 316 365 419 491 577 652
TD10 = 983
Circuit symbol = 6.6_{2}.6.6_{2}.6_{2}.8_{4}
Weight = 29
Vertex symbol  = 6.6_{2}.6.6_{2}.6_{2}.8_{2}
Weight = 29

T3 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 24 43 66 90 121 165 212 253 298 363 437 498 560 643
TD10 = 990
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

<TD10> = 976.000
Average ring size = 5.7778