Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_74_3_884153__gJiTy.cif"

There are 48 T-atoms per unit cell
There are 96 O-atoms per unit cell

Framework density = 25.90 T-atoms per nm^3
Material density = 2.584 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6235 Angstrom
T1  -- O2  = 1.5427 Angstrom
T1  -- O3  = 1.6371 Angstrom
T1  -- O4  = 1.6301 Angstrom
      mean = 1.6084 Angstrom
        t1 = 0.055679  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.056174  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6344 Angstrom
T2  -- O5  = 1.6277 Angstrom
T2  -- O7  = 1.6878 Angstrom
T2  -- O6  = 1.5530 Angstrom
      mean = 1.6258 Angstrom
        t1 = 0.023888  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.016044  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.5541 Angstrom
T3  -- O7  = 1.6660 Angstrom
T3  -- O8  = 1.6732 Angstrom
T3  -- O9  = 1.6260 Angstrom
      mean = 1.6298 Angstrom
        t1 = 0.057376  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.045075  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5427 A <--> 1.6878 A
          Mean   = 1.6213 A
          StdDev = 0.0458 A

       t1 Range  = 0.0239 <-- 0.0456 --> 0.0574
       t2 Range  = 0.0160 <-- 0.0391 --> 0.0562

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 100.610 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  = 118.166 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 110.792 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 100.594 deg; O2  -- O3  = 2 A
O2  -- T1  -- O4  = 107.476 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 116.628 deg; O3  -- O4  = 3 A
       100.594 deg <-- 109.044 deg --> 118.166 deg

O4  -- T2  -- O5  = 107.795 deg; O4  -- O5  = 3 A
O4  -- T2  -- O7  = 104.039 deg; O4  -- O7  = 3 A
O4  -- T2  -- O6  = 110.673 deg; O4  -- O6  = 3 A
O5  -- T2  -- O7  = 109.494 deg; O5  -- O7  = 3 A
O5  -- T2  -- O6  = 108.401 deg; O5  -- O6  = 3 A
O7  -- T2  -- O6  = 116.121 deg; O7  -- O6  = 3 A
       104.039 deg <-- 109.421 deg --> 116.121 deg

O6  -- T3  -- O7  = 101.572 deg; O6  -- O7  = 2 A
O6  -- T3  -- O8  = 103.657 deg; O6  -- O8  = 3 A
O6  -- T3  -- O9  = 110.382 deg; O6  -- O9  = 3 A
O7  -- T3  -- O8  = 124.642 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 108.171 deg; O7  -- O9  = 3 A
O8  -- T3  -- O9  = 107.737 deg; O8  -- O9  = 3 A
       101.572 deg <-- 109.360 deg --> 124.642 deg

        O-T-O SUMMARY
          Range  = 100.5937 deg <--> 124.6415 deg
          Mean   = 109.5873 deg
          StdDev = 6.0465 deg

        O--O SUMMARY
          Range  = 2.4368 A <--> 2.9571 A
          Mean   = 2.6484 A
          StdDev = 0.1209 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 113.902 deg; T1  -- T2  = 4.8559 A
T1  - O1  - T1  - O3  - T1  =  91.641 deg; T1  -- T1  = 4.1991 A
T1  - O1  - T1  - O4  - T1  =  88.293 deg; T1  -- T1  = 4.1991 A
T2  - O2  - T1  - O3  - T1  = 106.295 deg; T2  -- T1  = 4.8001 A
T2  - O2  - T1  - O4  - T1  = 145.624 deg; T2  -- T1  = 5.8887 A
T1  - O3  - T1  - O4  - T1  =  98.527 deg; T1  -- T1  = 4.7165 A

T1  - O4  - T2  - O5  - T3  =  80.667 deg; T1  -- T3  = 3.9171 A
T1  - O4  - T2  - O7  - T2  = 113.008 deg; T1  -- T2  = 4.9375 A
T1  - O4  - T2  - O6  - T3  = 118.883 deg; T1  -- T3  = 4.8534 A
T3  - O5  - T2  - O7  - T2  = 112.464 deg; T3  -- T2  = 5.0150 A
T3  - O5  - T2  - O6  - T3  = 110.163 deg; T3  -- T3  = 4.7165 A
T2  - O7  - T2  - O6  - T3  = 116.229 deg; T2  -- T3  = 4.7700 A

T2  - O6  - T3  - O7  - T3  = 141.927 deg; T2  -- T3  = 6.0758 A
T2  - O6  - T3  - O8  - T3  = 111.562 deg; T2  -- T3  = 4.9163 A
T2  - O6  - T3  - O9  - T2  = 110.163 deg; T2  -- T2  = 4.7165 A
T3  - O7  - T3  - O8  - T3  =  90.000 deg; T3  -- T3  = 4.4032 A
T3  - O7  - T3  - O9  - T2  =  86.069 deg; T3  -- T2  = 4.1312 A
T3  - O8  - T3  - O9  - T2  = 115.155 deg; T3  -- T2  = 4.6662 A

        T-T-T SUMMARY
          Range  = 80.6668 deg <--> 145.6240 deg
          Mean   = 108.5672 deg
          StdDev = 17.7532 deg

        T--T SUMMARY
          Range  = 3.9171 A <--> 6.0758 A
          Mean   = 4.7823 A
          StdDev = 0.5515 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 120.765 deg ; T1  -- T1   2.8227 A

T1  -- O2  -- T1  = 158.068 deg ; T1  -- T1   3.0290 A

T1  -- O3  -- T1  = 154.583 deg ; T1  -- T1   3.1940 A

T1  -- O4  -- T2  = 130.913 deg ; T1  -- T2   2.9696 A

T2  -- O5  -- T2  = 130.057 deg ; T2  -- T2   2.9511 A

T2  -- O6  -- T3  = 118.027 deg ; T2  -- T3   2.6637 A

T2  -- O7  -- T3  = 133.455 deg ; T2  -- T3   3.0810 A

T3  -- O8  -- T3  = 177.489 deg ; T3  -- T3   3.3456 A

T3  -- O9  -- T3  = 123.357 deg ; T3  -- T3   2.8627 A


        T-O-T SUMMARY
          Range  = 118.0269° <--> 177.4893 deg
          Mean   = 138.5238 deg
          StdDev = 19.1542 deg

        T--T SUMMARY
          Range  = 2.6637 A <--> 3.3456 A
          Mean   = 2.9911 A
          StdDev = 0.1923 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T2  -- T3  = 2.6637 Angstrom
T3  -- T2  = 2.6637 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 38 61 87 118 160 206 249 296 358 430 495 559 638
TD10 = 955
Circuit symbol = 4.6.4.6.6_{2}.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6_{2}
Weight = 19

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 12 25 40 63 95 129 161 198 255 316 365 419 491 577 652
TD10 = 983
Circuit symbol = 6.6_{2}.6.6_{2}.6_{2}.8_{4}
Weight = 29
Vertex symbol  = 6.6_{2}.6.6_{2}.6_{2}.8_{2}
Weight = 29

T3 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 24 43 66 90 121 165 212 253 298 363 437 498 560 643
TD10 = 990
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

<TD10> = 976.000
Average ring size = 5.7778