Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_74_3_789172_i1ozC2.cif"

There are 48 T-atoms per unit cell
There are 96 O-atoms per unit cell

Framework density = 24.43 T-atoms per nm^3
Material density = 2.438 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6045 Angstrom
T1  -- O2  = 1.6049 Angstrom
T1  -- O3  = 1.6546 Angstrom
T1  -- O4  = 1.6239 Angstrom
      mean = 1.6220 Angstrom
        t1 = 0.073840  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.067000  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6242 Angstrom
T2  -- O6  = 1.6385 Angstrom
T2  -- O4  = 1.6316 Angstrom
T2  -- O7  = 1.6277 Angstrom
      mean = 1.6305 Angstrom
        t1 = 0.015611  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005906  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6358 Angstrom
T3  -- O7  = 1.6268 Angstrom
T3  -- O8  = 1.6191 Angstrom
T3  -- O9  = 1.6155 Angstrom
      mean = 1.6243 Angstrom
        t1 = 0.013142  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006125  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6045 A <--> 1.6546 A
          Mean   = 1.6256 A
          StdDev = 0.0135 A

       t1 Range  = 0.0131 <-- 0.0342 --> 0.0738
       t2 Range  = 0.0059 <-- 0.0263 --> 0.0670

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 114.756 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 119.327 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  93.696 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 119.310 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  =  93.452 deg; O2  -- O4  = 2 A
O3  -- T1  -- O4  = 108.087 deg; O3  -- O4  = 3 A
       93.452 deg <-- 108.105 deg --> 119.327 deg

O5  -- T2  -- O6  = 108.026 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 109.349 deg; O5  -- O4  = 3 A
O5  -- T2  -- O7  = 107.938 deg; O5  -- O7  = 3 A
O6  -- T2  -- O4  = 109.635 deg; O6  -- O4  = 3 A
O6  -- T2  -- O7  = 111.741 deg; O6  -- O7  = 3 A
O4  -- T2  -- O7  = 110.088 deg; O4  -- O7  = 3 A
       107.938 deg <-- 109.463 deg --> 111.741 deg

O6  -- T3  -- O7  = 112.197 deg; O6  -- O7  = 3 A
O6  -- T3  -- O8  = 109.091 deg; O6  -- O8  = 3 A
O6  -- T3  -- O9  = 108.606 deg; O6  -- O9  = 3 A
O7  -- T3  -- O8  = 109.198 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 108.716 deg; O7  -- O9  = 3 A
O8  -- T3  -- O9  = 108.981 deg; O8  -- O9  = 3 A
       108.606 deg <-- 109.465 deg --> 112.197 deg

        O-T-O SUMMARY
          Range  = 93.4522 deg <--> 119.3266 deg
          Mean   = 108.1879 deg
          StdDev = 6.1921 deg

        O--O SUMMARY
          Range  = 2.3509 A <--> 2.8131 A
          Mean   = 2.6310 A
          StdDev = 0.1139 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.0405 A
T1  - O1  - T1  - O3  - T2  =  89.258 deg; T1  -- T2  = 3.9764 A
T1  - O1  - T1  - O4  - T1  = 180.000 deg; T1  -- T1  = 5.4063 A
T1  - O2  - T1  - O3  - T2  = 108.243 deg; T1  -- T2  = 4.8295 A
T1  - O2  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.0447 A
T2  - O3  - T1  - O4  - T1  =  90.742 deg; T2  -- T1  = 4.0323 A

T1  - O5  - T2  - O6  - T3  = 109.336 deg; T1  -- T3  = 5.0214 A
T1  - O5  - T2  - O4  - T2  = 108.215 deg; T1  -- T2  = 4.8048 A
T1  - O5  - T2  - O7  - T3  = 108.288 deg; T1  -- T3  = 4.9501 A
T3  - O6  - T2  - O4  - T2  = 108.211 deg; T3  -- T2  = 5.0039 A
T3  - O6  - T2  - O7  - T3  = 116.732 deg; T3  -- T3  = 5.4063 A
T2  - O4  - T2  - O7  - T3  = 105.738 deg; T2  -- T3  = 4.8867 A

T2  - O6  - T3  - O7  - T3  = 106.843 deg; T2  -- T3  = 4.9806 A
T2  - O6  - T3  - O8  - T3  = 115.628 deg; T2  -- T3  = 5.4347 A
T2  - O6  - T3  - O9  - T2  = 116.732 deg; T2  -- T2  = 5.4063 A
T3  - O7  - T3  - O8  - T3  =  90.000 deg; T3  -- T3  = 4.4048 A
T3  - O7  - T3  - O9  - T2  = 107.102 deg; T3  -- T2  = 4.9506 A
T3  - O8  - T3  - O9  - T2  = 116.037 deg; T3  -- T2  = 5.4073 A

        T-T-T SUMMARY
          Range  = 89.2577 deg <--> 180.0000 deg
          Mean   = 109.7085 deg
          StdDev = 20.4621 deg

        T--T SUMMARY
          Range  = 3.9764 A <--> 5.4347 A
          Mean   = 4.8663 A
          StdDev = 0.4844 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 114.569 deg ; T1  -- T1   2.7000 A

T1  -- O2  -- T1  = 114.944 deg ; T1  -- T1   2.7063 A

T1  -- O3  -- T1  = 130.546 deg ; T1  -- T1   3.0059 A

T1  -- O4  -- T2  = 130.326 deg ; T1  -- T2   2.9544 A

T2  -- O5  -- T2  = 132.790 deg ; T2  -- T2   2.9766 A

T2  -- O6  -- T3  = 155.250 deg ; T2  -- T3   3.1983 A

T2  -- O7  -- T3  = 151.082 deg ; T2  -- T3   3.1514 A

T3  -- O8  -- T3  = 135.977 deg ; T3  -- T3   3.0021 A

T3  -- O9  -- T3  = 172.082 deg ; T3  -- T3   3.2233 A


        T-O-T SUMMARY
          Range  = 114.5687° <--> 172.0820 deg
          Mean   = 137.5072 deg
          StdDev = 17.8710 deg

        T--T SUMMARY
          Range  = 2.7000 A <--> 3.2233 A
          Mean   = 2.9909 A
          StdDev = 0.1802 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.7000 Angstrom
T1  -- T1  = 2.7063 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 38 61 87 118 160 206 249 296 358 430 495 559 638
TD10 = 955
Circuit symbol = 4.6.4.6.6_{2}.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6_{2}
Weight = 19

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 12 25 40 63 95 129 161 198 255 316 365 419 491 577 652
TD10 = 983
Circuit symbol = 6.6_{2}.6.6_{2}.6_{2}.8_{4}
Weight = 29
Vertex symbol  = 6.6_{2}.6.6_{2}.6_{2}.8_{2}
Weight = 29

T3 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 24 43 66 90 121 165 212 253 298 363 437 498 560 643
TD10 = 990
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

<TD10> = 976.000
Average ring size = 5.7778