Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_74_3_773054_QR_pkI.cif"

There are 48 T-atoms per unit cell
There are 96 O-atoms per unit cell

Framework density = 20.50 T-atoms per nm^3
Material density = 2.046 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6273 Angstrom
T1  -- O2  = 1.6067 Angstrom
T1  -- O3  = 1.6281 Angstrom
T1  -- O4  = 1.6227 Angstrom
      mean = 1.6212 Angstrom
        t1 = 0.012652  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008184  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6149 Angstrom
T2  -- O5  = 1.6158 Angstrom
T2  -- O6  = 1.5957 Angstrom
T2  -- O7  = 1.6277 Angstrom
      mean = 1.6135 Angstrom
        t1 = 0.012217  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.012973  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.5937 Angstrom
T3  -- O9  = 1.6191 Angstrom
T3  -- O7  = 1.6266 Angstrom
T3  -- O8  = 1.6184 Angstrom
      mean = 1.6145 Angstrom
        t1 = 0.006498  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004987  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5937 A <--> 1.6281 A
          Mean   = 1.6164 A
          StdDev = 0.0115 A

       t1 Range  = 0.0065 <-- 0.0105 --> 0.0127
       t2 Range  = 0.0050 <-- 0.0087 --> 0.0130

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.947 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.015 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 110.947 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.783 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 107.334 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 110.735 deg; O3  -- O4  = 3 A
       107.334 deg <-- 109.460 deg --> 110.947 deg

O4  -- T2  -- O5  = 110.094 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 107.599 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 111.033 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 107.692 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 110.219 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 110.111 deg; O6  -- O7  = 3 A
       107.599 deg <-- 109.458 deg --> 111.033 deg

O6  -- T3  -- O9  = 109.440 deg; O6  -- O9  = 3 A
O6  -- T3  -- O7  = 109.042 deg; O6  -- O7  = 3 A
O6  -- T3  -- O8  = 109.242 deg; O6  -- O8  = 3 A
O9  -- T3  -- O7  = 109.974 deg; O9  -- O7  = 3 A
O9  -- T3  -- O8  = 109.794 deg; O9  -- O8  = 3 A
O7  -- T3  -- O8  = 109.330 deg; O7  -- O8  = 3 A
       109.042 deg <-- 109.470 deg --> 109.974 deg

        O-T-O SUMMARY
          Range  = 107.3340 deg <--> 111.0330 deg
          Mean   = 109.4726 deg
          StdDev = 1.1173 deg

        O--O SUMMARY
          Range  = 2.5908 A <--> 2.6776 A
          Mean   = 2.6388 A
          StdDev = 0.0276 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.2489 A
T1  - O1  - T1  - O3  - T2  = 122.710 deg; T1  -- T2  = 5.3920 A
T1  - O1  - T1  - O4  - T1  = 108.696 deg; T1  -- T1  = 5.0869 A
T1  - O2  - T1  - O3  - T2  = 117.021 deg; T1  -- T2  = 5.1544 A
T1  - O2  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.3588 A
T2  - O3  - T1  - O4  - T1  = 119.843 deg; T2  -- T1  = 5.4477 A

T1  - O4  - T2  - O5  - T3  =  97.620 deg; T1  -- T3  = 4.6629 A
T1  - O4  - T2  - O6  - T2  = 117.026 deg; T1  -- T2  = 5.3723 A
T1  - O4  - T2  - O7  - T3  =  98.593 deg; T1  -- T3  = 4.7134 A
T3  - O5  - T2  - O6  - T2  = 116.314 deg; T3  -- T2  = 5.3657 A
T3  - O5  - T2  - O7  - T3  = 109.375 deg; T3  -- T3  = 5.0869 A
T2  - O6  - T2  - O7  - T3  = 115.294 deg; T2  -- T3  = 5.3535 A

T2  - O6  - T3  - O9  - T3  = 115.898 deg; T2  -- T3  = 5.2164 A
T2  - O6  - T3  - O7  - T3  = 112.432 deg; T2  -- T3  = 5.1812 A
T2  - O6  - T3  - O8  - T2  = 109.375 deg; T2  -- T2  = 5.0869 A
T3  - O9  - T3  - O7  - T3  =  90.000 deg; T3  -- T3  = 4.3671 A
T3  - O9  - T3  - O8  - T2  = 115.711 deg; T3  -- T2  = 5.2290 A
T3  - O7  - T3  - O8  - T2  = 112.273 deg; T3  -- T2  = 5.1938 A

        T-T-T SUMMARY
          Range  = 90.0000 deg <--> 122.7098 deg
          Mean   = 108.4664 deg
          StdDev = 10.1130 deg

        T--T SUMMARY
          Range  = 4.2489 A <--> 5.4477 A
          Mean   = 5.0316 A
          StdDev = 0.3652 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 139.557 deg ; T1  -- T1   3.0541 A

T1  -- O2  -- T1  = 171.816 deg ; T1  -- T1   3.2052 A

T1  -- O3  -- T1  = 130.235 deg ; T1  -- T1   2.9540 A

T1  -- O4  -- T2  = 145.262 deg ; T1  -- T2   3.0899 A

T2  -- O5  -- T2  = 166.599 deg ; T2  -- T2   3.2096 A

T2  -- O6  -- T3  = 153.800 deg ; T2  -- T3   3.1064 A

T2  -- O7  -- T3  = 147.891 deg ; T2  -- T3   3.1274 A

T3  -- O8  -- T3  = 140.663 deg ; T3  -- T3   3.0480 A

T3  -- O9  -- T3  = 149.942 deg ; T3  -- T3   3.1274 A


        T-O-T SUMMARY
          Range  = 130.2346° <--> 171.8161 deg
          Mean   = 149.5295 deg
          StdDev = 12.4156 deg

        T--T SUMMARY
          Range  = 2.9540 A <--> 3.2096 A
          Mean   = 3.1025 A
          StdDev = 0.0754 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 38 61 87 118 160 206 249 296 358 430 495 559 638
TD10 = 955
Circuit symbol = 4.6.4.6.6_{2}.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6_{2}
Weight = 19

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 12 25 40 63 95 129 161 198 255 316 365 419 491 577 652
TD10 = 983
Circuit symbol = 6.6_{2}.6.6_{2}.6_{2}.8_{4}
Weight = 29
Vertex symbol  = 6.6_{2}.6.6_{2}.6_{2}.8_{2}
Weight = 29

T3 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 24 43 66 90 121 165 212 253 298 363 437 498 560 643
TD10 = 990
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

<TD10> = 976.000
Average ring size = 5.7778