Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_74_3_2719806_UHuhj6.cif"

There are 40 T-atoms per unit cell
There are 80 O-atoms per unit cell

Framework density = 21.18 T-atoms per nm^3
Material density = 2.113 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6002 Angstrom
T1  -- O2  = 1.6303 Angstrom
T1  -- O3  = 1.6377 Angstrom
T1  -- O4  = 1.6114 Angstrom
      mean = 1.6199 Angstrom
        t1 = 0.017169  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.016831  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6020 Angstrom
T2  -- O5  = 1.6266 Angstrom
T2  -- O3  = 1.6304 Angstrom
T2  -- O6  = 1.6484 Angstrom
      mean = 1.6269 Angstrom
        t1 = 0.024789  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.022970  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O7  = 1.6086 Angstrom
T3  -- O8  = 1.6512 Angstrom
T3  -- O6  = 1.6307 Angstrom
T3  -- O6  = 1.6307 Angstrom
      mean = 1.6303 Angstrom
        t1 = 0.026076  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.019040  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6002 A <--> 1.6512 A
          Mean   = 1.6248 A
          StdDev = 0.0162 A

       t1 Range  = 0.0172 <-- 0.0227 --> 0.0261
       t2 Range  = 0.0168 <-- 0.0196 --> 0.0230

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.907 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 106.133 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 107.124 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.941 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 112.308 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 110.214 deg; O3  -- O4  = 3 A
       106.133 deg <-- 109.438 deg --> 112.308 deg

O4  -- T2  -- O5  = 108.862 deg; O4  -- O5  = 3 A
O4  -- T2  -- O3  = 105.875 deg; O4  -- O3  = 3 A
O4  -- T2  -- O6  = 106.022 deg; O4  -- O6  = 3 A
O5  -- T2  -- O3  = 110.796 deg; O5  -- O3  = 3 A
O5  -- T2  -- O6  = 110.965 deg; O5  -- O6  = 3 A
O3  -- T2  -- O6  = 113.967 deg; O3  -- O6  = 3 A
       105.875 deg <-- 109.415 deg --> 113.967 deg

O7  -- T3  -- O8  = 107.626 deg; O7  -- O8  = 3 A
O7  -- T3  -- O6  = 107.278 deg; O7  -- O6  = 3 A
O7  -- T3  -- O6  = 107.278 deg; O7  -- O6  = 3 A
O8  -- T3  -- O6  = 113.587 deg; O8  -- O6  = 3 A
O8  -- T3  -- O6  = 113.587 deg; O8  -- O6  = 3 A
O6  -- T3  -- O6  = 107.140 deg; O6  -- O6  = 3 A
       107.140 deg <-- 109.416 deg --> 113.587 deg

        O-T-O SUMMARY
          Range  = 105.8755 deg <--> 113.9672 deg
          Mean   = 109.4591 deg
          StdDev = 2.7443 deg

        O--O SUMMARY
          Range  = 2.5794 A <--> 2.7493 A
          Mean   = 2.6542 A
          StdDev = 0.0573 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 105.915 deg; T1  -- T1  = 4.8088 A
T1  - O1  - T1  - O3  - T2  = 106.878 deg; T1  -- T2  = 4.8239 A
T1  - O1  - T1  - O4  - T2  = 108.282 deg; T1  -- T2  = 4.6831 A
T1  - O2  - T1  - O3  - T2  = 124.084 deg; T1  -- T2  = 5.4132 A
T1  - O2  - T1  - O4  - T2  = 118.857 deg; T1  -- T2  = 5.0822 A
T2  - O3  - T1  - O4  - T2  =  91.502 deg; T2  -- T2  = 4.2165 A

T2  - O4  - T2  - O5  - T3  =  93.158 deg; T2  -- T3  = 4.2550 A
T2  - O4  - T2  - O3  - T1  = 106.878 deg; T2  -- T1  = 4.7541 A
T2  - O4  - T2  - O6  - T1  = 108.282 deg; T2  -- T1  = 4.6111 A
T3  - O5  - T2  - O3  - T1  = 156.001 deg; T3  -- T1  = 5.9174 A
T3  - O5  - T2  - O6  - T1  = 108.620 deg; T3  -- T1  = 4.7296 A
T1  - O3  - T2  - O6  - T1  =  77.974 deg; T1  -- T1  = 3.7050 A

T2  - O7  - T3  - O8  - T3  =  86.842 deg; T2  -- T3  = 4.2550 A
T2  - O7  - T3  - O6  - T2  = 118.330 deg; T2  -- T2  = 5.1428 A
T2  - O7  - T3  - O6  - T3  = 120.738 deg; T2  -- T3  = 5.4758 A
T3  - O8  - T3  - O6  - T2  =  86.842 deg; T3  -- T2  = 4.2550 A
T3  - O8  - T3  - O6  - T3  = 100.485 deg; T3  -- T3  = 4.9933 A
T2  - O6  - T3  - O6  - T3  = 120.738 deg; T2  -- T3  = 5.4758 A

        T-T-T SUMMARY
          Range  = 77.9741 deg <--> 156.0009 deg
          Mean   = 108.7951 deg
          StdDev = 17.5104 deg

        T--T SUMMARY
          Range  = 3.7050 A <--> 5.9174 A
          Mean   = 4.8359 A
          StdDev = 0.5482 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 147.641 deg ; T1  -- T1   3.0736 A

T1  -- O2  -- T1  = 129.606 deg ; T1  -- T1   2.9503 A

T1  -- O3  -- T2  = 138.374 deg ; T1  -- T2   3.0549 A

T1  -- O4  -- T2  = 123.251 deg ; T1  -- T2   2.8273 A

T2  -- O5  -- T2  = 123.232 deg ; T2  -- T2   2.8622 A

T2  -- O6  -- T3  = 131.924 deg ; T2  -- T3   2.9947 A

T3  -- O7  -- T3  = 165.718 deg ; T3  -- T3   3.1922 A

T3  -- O8  -- T3  = 180.000 deg ; T3  -- T3   3.3024 A


        T-O-T SUMMARY
          Range  = 123.2319° <--> 180.0000 deg
          Mean   = 138.1268 deg
          StdDev = 16.5584 deg

        T--T SUMMARY
          Range  = 2.8273 A <--> 3.3024 A
          Mean   = 3.0015 A
          StdDev = 0.1336 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 21 35 55 80 106 140 179 219 263 312 365 426 487 552
TD10 = 851
Circuit symbol = 4.6_{2}.6.6_{2}.6_{2}.6_{2}
Weight = 20
Vertex symbol  = 4.6_{2}.6.6_{2}.6_{2}.6_{2}
Weight = 20

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 20 36 55 80 109 139 175 219 262 312 368 424 488 558
TD10 = 848
Circuit symbol = 4.4.6.6_{3}.6_{3}.8_{5}
Weight = 20
Vertex symbol  = 4.4.6.6_{3}.6_{3}.8
Weight = 20

T3 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 22 36 55 80 109 140 173 212 262 314 367 426 490 556
TD10 = 842
Circuit symbol = 4.6.4.6.6.8_{8}
Weight = 24
Vertex symbol  = 4.6.4.6.8_{6}.10
Weight = 31

<TD10> = 848.000
Average ring size = 5.8175