Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_74_3_1877488__GMeNl.cif"

There are 48 T-atoms per unit cell
There are 96 O-atoms per unit cell

Framework density = 19.08 T-atoms per nm^3
Material density = 1.904 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6384 Angstrom
T1  -- O2  = 1.6048 Angstrom
T1  -- O3  = 1.6253 Angstrom
T1  -- O4  = 1.6318 Angstrom
      mean = 1.6251 Angstrom
        t1 = 0.018769  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.010558  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6221 Angstrom
T2  -- O5  = 1.6254 Angstrom
T2  -- O7  = 1.6013 Angstrom
T2  -- O6  = 1.6333 Angstrom
      mean = 1.6205 Angstrom
        t1 = 0.019916  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.020301  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6369 Angstrom
T3  -- O8  = 1.6051 Angstrom
T3  -- O9  = 1.6330 Angstrom
T3  -- O7  = 1.6081 Angstrom
      mean = 1.6207 Angstrom
        t1 = 0.018688  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.014101  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6013 A <--> 1.6384 A
          Mean   = 1.6221 A
          StdDev = 0.0131 A

       t1 Range  = 0.0187 <-- 0.0191 --> 0.0199
       t2 Range  = 0.0106 <-- 0.0150 --> 0.0203

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 107.909 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.371 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 113.851 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.549 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 107.708 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.313 deg; O3  -- O4  = 3 A
       107.708 deg <-- 109.450 deg --> 113.851 deg

O4  -- T2  -- O5  = 110.137 deg; O4  -- O5  = 3 A
O4  -- T2  -- O7  = 106.131 deg; O4  -- O7  = 3 A
O4  -- T2  -- O6  = 113.441 deg; O4  -- O6  = 3 A
O5  -- T2  -- O7  = 109.512 deg; O5  -- O7  = 3 A
O5  -- T2  -- O6  = 110.761 deg; O5  -- O6  = 3 A
O7  -- T2  -- O6  = 106.642 deg; O7  -- O6  = 3 A
       106.131 deg <-- 109.437 deg --> 113.441 deg

O6  -- T3  -- O8  = 105.752 deg; O6  -- O8  = 3 A
O6  -- T3  -- O9  = 110.218 deg; O6  -- O9  = 3 A
O6  -- T3  -- O7  = 110.184 deg; O6  -- O7  = 3 A
O8  -- T3  -- O9  = 111.259 deg; O8  -- O9  = 3 A
O8  -- T3  -- O7  = 106.718 deg; O8  -- O7  = 3 A
O9  -- T3  -- O7  = 112.449 deg; O9  -- O7  = 3 A
       105.752 deg <-- 109.430 deg --> 112.449 deg

        O-T-O SUMMARY
          Range  = 105.7516 deg <--> 113.8510 deg
          Mean   = 109.4600 deg
          StdDev = 2.4279 deg

        O--O SUMMARY
          Range  = 2.5765 A <--> 2.7403 A
          Mean   = 2.6483 A
          StdDev = 0.0489 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.3784 A
T1  - O1  - T1  - O3  - T1  = 106.696 deg; T1  -- T1  = 4.9326 A
T1  - O1  - T1  - O4  - T2  = 107.995 deg; T1  -- T2  = 5.0799 A
T1  - O2  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.1967 A
T1  - O2  - T1  - O4  - T2  = 138.275 deg; T1  -- T2  = 5.6706 A
T1  - O3  - T1  - O4  - T2  = 118.418 deg; T1  -- T2  = 5.1764 A

T2  - O4  - T2  - O5  - T1  = 107.995 deg; T2  -- T1  = 4.9099 A
T2  - O4  - T2  - O7  - T3  = 109.935 deg; T2  -- T3  = 4.9486 A
T2  - O4  - T2  - O6  - T3  = 111.071 deg; T2  -- T3  = 4.8528 A
T1  - O5  - T2  - O7  - T3  = 141.415 deg; T1  -- T3  = 5.7888 A
T1  - O5  - T2  - O6  - T3  =  92.291 deg; T1  -- T3  = 4.3107 A
T3  - O7  - T2  - O6  - T3  =  80.669 deg; T3  -- T3  = 3.8530 A

T3  - O6  - T3  - O8  - T2  = 109.935 deg; T3  -- T2  = 4.9731 A
T3  - O6  - T3  - O9  - T2  = 111.071 deg; T3  -- T2  = 4.8778 A
T3  - O6  - T3  - O7  - T3  = 109.846 deg; T3  -- T3  = 4.9449 A
T2  - O8  - T3  - O9  - T2  =  85.237 deg; T2  -- T2  = 4.0304 A
T2  - O8  - T3  - O7  - T3  = 121.008 deg; T2  -- T3  = 5.2890 A
T2  - O9  - T3  - O7  - T3  = 117.650 deg; T2  -- T3  = 5.0644 A

        T-T-T SUMMARY
          Range  = 80.6694 deg <--> 141.4151 deg
          Mean   = 110.2213 deg
          StdDev = 15.7080 deg

        T--T SUMMARY
          Range  = 3.8530 A <--> 5.7888 A
          Mean   = 4.9068 A
          StdDev = 0.4939 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 128.064 deg ; T1  -- T1   2.9460 A

T1  -- O2  -- T1  = 170.836 deg ; T1  -- T1   3.1994 A

T1  -- O3  -- T1  = 133.714 deg ; T1  -- T1   2.9890 A

T1  -- O4  -- T2  = 142.300 deg ; T1  -- T2   3.0794 A

T2  -- O5  -- T2  = 133.732 deg ; T2  -- T2   2.9895 A

T2  -- O6  -- T3  = 138.090 deg ; T2  -- T3   3.0539 A

T2  -- O7  -- T3  = 128.946 deg ; T2  -- T3   2.8960 A

T3  -- O8  -- T3  = 140.644 deg ; T3  -- T3   3.0227 A

T3  -- O9  -- T3  = 135.210 deg ; T3  -- T3   3.0196 A


        T-O-T SUMMARY
          Range  = 128.0636° <--> 170.8360 deg
          Mean   = 139.0594 deg
          StdDev = 12.1467 deg

        T--T SUMMARY
          Range  = 2.8960 A <--> 3.1994 A
          Mean   = 3.0217 A
          StdDev = 0.0816 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 20 34 52 75 103 135 170 208 251 298 349 404 463 528
TD10 = 812
Circuit symbol = 4.6_{2}.4.6_{2}.6_{2}.8_{7}
Weight = 23
Vertex symbol  = 4.6_{2}.4.6_{2}.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 21 34 52 76 104 134 169 207 251 299 350 405 464 529
TD10 = 813
Circuit symbol = 4.6.6.6_{3}.6_{2}.6_{3}
Weight = 21
Vertex symbol  = 4.6.6.6_{3}.6_{2}.6_{3}
Weight = 21

T3 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 21 35 53 75 103 134 169 207 251 299 351 406 464 529
TD10 = 813
Circuit symbol = 4.6_{2}.6.6_{3}.6_{2}.6_{3}
Weight = 23
Vertex symbol  = 4.6_{2}.6.6_{3}.6_{2}.6_{3}
Weight = 23

<TD10> = 812.667
Average ring size = 5.7313