Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_74_3_1812291_knR2vH.cif"

There are 48 T-atoms per unit cell
There are 96 O-atoms per unit cell

Framework density = 23.67 T-atoms per nm^3
Material density = 2.362 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6152 Angstrom
T1  -- O2  = 1.5987 Angstrom
T1  -- O3  = 1.6226 Angstrom
T1  -- O4  = 1.6237 Angstrom
      mean = 1.6151 Angstrom
        t1 = 0.009657  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006057  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6250 Angstrom
T2  -- O5  = 1.7146 Angstrom
T2  -- O6  = 1.6452 Angstrom
T2  -- O7  = 1.6784 Angstrom
      mean = 1.6658 Angstrom
        t1 = 0.057255  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.035396  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.7092 Angstrom
T3  -- O7  = 1.6469 Angstrom
T3  -- O8  = 1.6030 Angstrom
T3  -- O6  = 1.9075 Angstrom
T3  -- O7  = 2.0405 Angstrom
T3  -- O9  = 1.5411 Angstrom
      mean = 1.7414 Angstrom

        T-O SUMMARY
          Range  = 1.5411 A <--> 2.0405 A
          Mean   = 1.6837 A
          StdDev = 0.1288 A

       t1 Range  = 0.0097 <-- 0.0223 --> 0.0573
       t2 Range  = 0.0061 <-- 0.0138 --> 0.0354

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.195 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.554 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 111.082 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.017 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 108.136 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.826 deg; O3  -- O4  = 3 A
       108.136 deg <-- 109.468 deg --> 111.082 deg

O4  -- T2  -- O5  = 104.690 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 106.874 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 107.162 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 114.062 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 120.262 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 103.032 deg; O6  -- O7  = 3 A
       103.032 deg <-- 109.347 deg --> 120.262 deg

O6  -- T3  -- O7  =  71.903 deg; O6  -- O7  = 2 A
O6  -- T3  -- O8  = 123.636 deg; O6  -- O8  = 3 A
O6  -- T3  -- O6  =  85.666 deg; O6  -- O6  = 2 A
O6  -- T3  -- O7  = 129.776 deg; O6  -- O7  = 3 A
O6  -- T3  -- O9  = 111.558 deg; O6  -- O9  = 3 A
O7  -- T3  -- O8  =  64.189 deg; O7  -- O8  = 2 A
O7  -- T3  -- O6  = 145.807 deg; O7  -- O6  = 3 A
O7  -- T3  -- O7  = 116.545 deg; O7  -- O7  = 3 A
O7  -- T3  -- O9  = 107.204 deg; O7  -- O9  = 3 A
O8  -- T3  -- O6  = 112.276 deg; O8  -- O6  = 3 A
O8  -- T3  -- O7  =  55.021 deg; O8  -- O7  = 2 A
O8  -- T3  -- O9  = 113.847 deg; O8  -- O9  = 3 A
O6  -- T3  -- O7  =  59.787 deg; O6  -- O7  = 2 A
O6  -- T3  -- O9  = 104.898 deg; O6  -- O9  = 3 A
O7  -- T3  -- O9  = 111.898 deg; O7  -- O9  = 3 A
       55.021 deg <-- 100.934 deg --> 145.807 deg

        O-T-O SUMMARY
          Range  = 55.0211 deg <--> 145.8073 deg
          Mean   = 104.2440 deg
          StdDev = 21.0360 deg

        O--O SUMMARY
          Range  = 1.7271 A <--> 3.3982 A
          Mean   = 2.6443 A
          StdDev = 0.4208 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 174.149 deg ; T1  -- T1   3.2262 A

T1  -- O2  -- T1  = 161.279 deg ; T1  -- T1   3.1549 A

T1  -- O3  -- T1  = 130.030 deg ; T1  -- T1   2.9415 A

T1  -- O4  -- T2  = 143.567 deg ; T1  -- T2   3.0858 A

T2  -- O5  -- T2  = 165.482 deg ; T2  -- T2   3.4016 A

T2  -- O6  -- T3  = 151.079 deg ; T2  -- T3   3.2482 A
T3  -- O6  -- T3  =  39.979 deg ; T3  -- T3   1.2503 A
T2  -- O6  -- T3  = 120.711 deg ; T2  -- T3   3.0904 A

T2  -- O7  -- T3  = 145.403 deg ; T2  -- T3   3.1748 A
T3  -- O7  -- T3  =  37.774 deg ; T3  -- T3   1.2503 A
T2  -- O7  -- T3  = 107.847 deg ; T2  -- T3   3.0132 A

T3  -- O8  -- T3  =  45.909 deg ; T3  -- T3   1.2503 A

T3  -- O9  -- T3  = 146.444 deg ; T3  -- T3   2.9511 A


        T-O-T SUMMARY
          Range  = 37.7737° <--> 174.1487 deg
          Mean   = 120.7425 deg
          StdDev = 46.9073 deg

        T--T SUMMARY
          Range  = 1.2503 A <--> 3.4016 A
          Mean   = 2.6953 A
          StdDev = 0.8023 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O6  -- O7  = 1.9710 A
O7  -- O8  = 1.7271 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T2  has 7 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T2  = 3.1213 Angstrom
  T2  -- T2  = 3.4016 Angstrom
  T2  -- T3  = 3.0904 Angstrom
  T2  -- T1  = 3.0858 Angstrom
  T2  -- T3  = 3.2482 Angstrom
  T2  -- T3  = 3.1748 Angstrom
  T2  -- T3  = 3.0132 Angstrom
T3  has 6 oxygen-bridged T-atoms within 3.50 A
  T3  -- T3  = 2.9511 Angstrom
  T3  -- T2  = 3.2482 Angstrom
  T3  -- T2  = 3.1748 Angstrom
  T3  -- T3  = 1.2503 Angstrom
  T3  -- T2  = 3.0132 Angstrom
  T3  -- T2  = 3.0904 Angstrom