Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_74_2_4174_t6aQhI.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 17.48 T-atoms per nm^3
Material density = 1.744 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6169 Angstrom
T1  -- O2  = 1.6154 Angstrom
T1  -- O3  = 1.6173 Angstrom
T1  -- O3  = 1.6173 Angstrom
      mean = 1.6167 Angstrom
        t1 = 0.006196  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004246  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6170 Angstrom
T2  -- O3  = 1.6173 Angstrom
T2  -- O3  = 1.6173 Angstrom
T2  -- O5  = 1.6154 Angstrom
      mean = 1.6167 Angstrom
        t1 = 0.006201  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004252  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6154 A <--> 1.6173 A
          Mean   = 1.6167 A
          StdDev = 0.0008 A

       t1 Range  = 0.0062 <-- 0.0062 --> 0.0062
       t2 Range  = 0.0042 <-- 0.0042 --> 0.0043

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.344 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.637 deg; O1  -- O3  = 3 A
O1  -- T1  -- O3  = 108.637 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 109.691 deg; O2  -- O3  = 3 A
O2  -- T1  -- O3  = 109.691 deg; O2  -- O3  = 3 A
O3  -- T1  -- O3  = 110.811 deg; O3  -- O3  = 3 A
       108.637 deg <-- 109.468 deg --> 110.811 deg

O4  -- T2  -- O3  = 108.634 deg; O4  -- O3  = 3 A
O4  -- T2  -- O3  = 108.634 deg; O4  -- O3  = 3 A
O4  -- T2  -- O5  = 109.341 deg; O4  -- O5  = 3 A
O3  -- T2  -- O3  = 110.815 deg; O3  -- O3  = 3 A
O3  -- T2  -- O5  = 109.693 deg; O3  -- O5  = 3 A
O3  -- T2  -- O5  = 109.693 deg; O3  -- O5  = 3 A
       108.634 deg <-- 109.468 deg --> 110.815 deg

        O-T-O SUMMARY
          Range  = 108.6343 deg <--> 110.8146 deg
          Mean   = 109.4863 deg
          StdDev = 0.7947 deg

        O--O SUMMARY
          Range  = 2.6271 A <--> 2.6628 A
          Mean   = 2.6404 A
          StdDev = 0.0129 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 108.947 deg; T1  -- T2  = 5.1477 A
T1  - O1  - T1  - O3  - T1  =  97.347 deg; T1  -- T1  = 4.8018 A
T1  - O1  - T1  - O3  - T2  = 108.947 deg; T1  -- T2  = 5.1477 A
T2  - O2  - T1  - O3  - T1  = 130.150 deg; T2  -- T1  = 5.6741 A
T2  - O2  - T1  - O3  - T2  =  80.295 deg; T2  -- T2  = 3.9892 A
T1  - O3  - T1  - O3  - T2  = 130.150 deg; T1  -- T2  = 5.6741 A

T2  - O4  - T2  - O3  - T1  = 130.148 deg; T2  -- T1  = 5.6741 A
T2  - O4  - T2  - O3  - T1  = 130.148 deg; T2  -- T1  = 5.6741 A
T2  - O4  - T2  - O5  - T2  =  97.344 deg; T2  -- T2  = 4.8018 A
T1  - O3  - T2  - O3  - T1  =  80.300 deg; T1  -- T1  = 3.9894 A
T1  - O3  - T2  - O5  - T2  = 108.949 deg; T1  -- T2  = 5.1478 A
T1  - O3  - T2  - O5  - T2  = 108.949 deg; T1  -- T2  = 5.1478 A

        T-T-T SUMMARY
          Range  = 80.2955 deg <--> 130.1501 deg
          Mean   = 110.1864 deg
          StdDev = 18.5504 deg

        T--T SUMMARY
          Range  = 3.9892 A <--> 5.6741 A
          Mean   = 5.0864 A
          StdDev = 0.6114 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 156.005 deg ; T1  -- T1   3.1632 A

T1  -- O2  -- T1  = 180.000 deg ; T1  -- T1   3.2308 A

T1  -- O3  -- T2  = 146.033 deg ; T1  -- T2   3.0936 A

T2  -- O4  -- T2  = 156.006 deg ; T2  -- T2   3.1633 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2308 A


        T-O-T SUMMARY
          Range  = 146.0335° <--> 180.0000 deg
          Mean   = 163.6088 deg
          StdDev = 14.0465 deg

        T--T SUMMARY
          Range  = 3.0936 A <--> 3.2308 A
          Mean   = 3.1763 A
          StdDev = 0.0519 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 23 44 67 95 134 168 215 271 320 380 454 520 599 682
TD10 = 1033
Circuit symbol = 4.5_{2}.5.8_{4}.5.8_{4}
Weight = 28
Vertex symbol  = 4.5_{2}.5.8_{2}.5.8_{2}
Weight = 28

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 23 44 67 95 134 168 215 271 320 380 454 520 599 682
TD10 = 1033
Circuit symbol = 4.5_{2}.5.8_{4}.5.8_{4}
Weight = 28
Vertex symbol  = 4.5_{2}.5.8_{2}.5.8_{2}
Weight = 28

<TD10> = 1033.000
Average ring size = 5.8065