Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_73_2_83266_ybMzli.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 24.31 T-atoms per nm^3
Material density = 2.425 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6210 Angstrom
T1  -- O3  = 1.6251 Angstrom
T1  -- O4  = 1.6278 Angstrom
T1  -- O2  = 1.6029 Angstrom
      mean = 1.6192 Angstrom
        t1 = 0.015351  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.011740  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6049 Angstrom
T2  -- O3  = 1.6274 Angstrom
T2  -- O4  = 1.6296 Angstrom
T2  -- O5  = 1.6216 Angstrom
      mean = 1.6209 Angstrom
        t1 = 0.016086  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.009241  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6029 A <--> 1.6296 A
          Mean   = 1.6200 A
          StdDev = 0.0098 A

       t1 Range  = 0.0154 <-- 0.0157 --> 0.0161
       t2 Range  = 0.0092 <-- 0.0105 --> 0.0117

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 111.579 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 110.864 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 105.641 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 109.446 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 109.474 deg; O3  -- O2  = 3 A
O4  -- T1  -- O2  = 109.765 deg; O4  -- O2  = 3 A
       105.641 deg <-- 109.461 deg --> 111.579 deg

O2  -- T2  -- O3  = 109.693 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 109.652 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 105.492 deg; O2  -- O5  = 3 A
O3  -- T2  -- O4  = 109.584 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 110.650 deg; O3  -- O5  = 3 A
O4  -- T2  -- O5  = 111.688 deg; O4  -- O5  = 3 A
       105.492 deg <-- 109.460 deg --> 111.688 deg

        O-T-O SUMMARY
          Range  = 105.4920 deg <--> 111.6880 deg
          Mean   = 109.4606 deg
          StdDev = 1.9060 deg

        O--O SUMMARY
          Range  = 2.5682 A <--> 2.6904 A
          Mean   = 2.6451 A
          StdDev = 0.0382 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O3  - T2  =  83.713 deg; T2  -- T2  = 4.0387 A
T2  - O1  - T1  - O4  - T1  = 119.227 deg; T2  -- T1  = 5.2622 A
T2  - O1  - T1  - O2  - T2  =  96.851 deg; T2  -- T2  = 4.5698 A
T2  - O3  - T1  - O4  - T1  = 114.788 deg; T2  -- T1  = 5.1343 A
T2  - O3  - T1  - O2  - T2  = 139.138 deg; T2  -- T2  = 5.7193 A
T1  - O4  - T1  - O2  - T2  = 100.572 deg; T1  -- T2  = 4.7314 A

T1  - O2  - T2  - O3  - T1  = 138.968 deg; T1  -- T1  = 5.7211 A
T1  - O2  - T2  - O4  - T2  = 114.900 deg; T1  -- T2  = 5.1416 A
T1  - O2  - T2  - O5  - T1  =  83.760 deg; T1  -- T1  = 4.0405 A
T1  - O3  - T2  - O4  - T2  = 100.241 deg; T1  -- T2  = 4.7198 A
T1  - O3  - T2  - O5  - T1  =  97.294 deg; T1  -- T1  = 4.5815 A
T2  - O4  - T2  - O5  - T1  = 119.550 deg; T2  -- T1  = 5.2660 A

        T-T-T SUMMARY
          Range  = 83.7132 deg <--> 139.1385 deg
          Mean   = 109.0835 deg
          StdDev = 17.8403 deg

        T--T SUMMARY
          Range  = 4.0387 A <--> 5.7211 A
          Mean   = 4.9105 A
          StdDev = 0.5395 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 142.638 deg ; T1  -- T1   3.0712 A

T1  -- O2  -- T2  = 147.479 deg ; T1  -- T2   3.0796 A

T1  -- O3  -- T2  = 137.267 deg ; T1  -- T2   3.0289 A

T1  -- O4  -- T2  = 136.317 deg ; T1  -- T2   3.0236 A

T2  -- O5  -- T2  = 142.464 deg ; T2  -- T2   3.0708 A


        T-O-T SUMMARY
          Range  = 136.3171° <--> 147.4792 deg
          Mean   = 141.2331 deg
          StdDev = 4.0852 deg

        T--T SUMMARY
          Range  = 3.0236 A <--> 3.0796 A
          Mean   = 3.0548 A
          StdDev = 0.0237 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 24 43 68 102 139 183 230 283 343 410 479 555 638 727
TD10 = 1088
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 24 43 68 102 139 183 230 283 343 410 479 555 638 727
TD10 = 1088
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

<TD10> = 1088.000
Average ring size = 5.6000