Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_72_2_918_cMeY2s.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 22.40 T-atoms per nm^3
Material density = 2.235 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6190 Angstrom
T1  -- O2  = 1.6174 Angstrom
T1  -- O4  = 1.6197 Angstrom
T1  -- O3  = 1.6196 Angstrom
      mean = 1.6189 Angstrom
        t1 = 0.005683  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000908  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6204 Angstrom
T2  -- O4  = 1.6204 Angstrom
T2  -- O5  = 1.6209 Angstrom
T2  -- O6  = 1.6234 Angstrom
      mean = 1.6213 Angstrom
        t1 = 0.007241  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001376  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6174 A <--> 1.6234 A
          Mean   = 1.6201 A
          StdDev = 0.0016 A

       t1 Range  = 0.0057 <-- 0.0065 --> 0.0072
       t2 Range  = 0.0009 <-- 0.0011 --> 0.0014

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.988 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 109.348 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 109.430 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 109.435 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 109.234 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 109.392 deg; O4  -- O3  = 3 A
       109.234 deg <-- 109.471 deg --> 109.988 deg

O3  -- T2  -- O4  = 109.330 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.341 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.376 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 109.214 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.934 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 109.631 deg; O5  -- O6  = 3 A
       109.214 deg <-- 109.471 deg --> 109.934 deg

        O-T-O SUMMARY
          Range  = 109.2136 deg <--> 109.9876 deg
          Mean   = 109.4402 deg
          StdDev = 0.2227 deg

        O--O SUMMARY
          Range  = 2.6390 A <--> 2.6561 A
          Mean   = 2.6451 A
          StdDev = 0.0046 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 105.307 deg; T2  -- T1  = 4.8847 A
T2  - O1  - T1  - O4  - T1  = 128.932 deg; T2  -- T1  = 5.6157 A
T2  - O1  - T1  - O3  - T2  = 113.106 deg; T2  -- T2  = 5.0860 A
T1  - O2  - T1  - O4  - T1  =  83.231 deg; T1  -- T1  = 4.1589 A
T1  - O2  - T1  - O3  - T2  = 127.009 deg; T1  -- T2  = 5.4895 A
T1  - O4  - T1  - O3  - T2  =  98.618 deg; T1  -- T2  = 4.7115 A

T1  - O3  - T2  - O4  - T1  = 106.359 deg; T1  -- T1  = 4.8795 A
T1  - O3  - T2  - O5  - T2  = 127.435 deg; T1  -- T2  = 5.4891 A
T1  - O3  - T2  - O6  - T2  = 109.176 deg; T1  -- T2  = 4.9363 A
T1  - O4  - T2  - O5  - T2  = 112.593 deg; T1  -- T2  = 5.0842 A
T1  - O4  - T2  - O6  - T2  = 109.245 deg; T1  -- T2  = 4.9298 A
T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.2942 A

        T-T-T SUMMARY
          Range  = 83.2309 deg <--> 128.9319 deg
          Mean   = 110.3052 deg
          StdDev = 13.6527 deg

        T--T SUMMARY
          Range  = 4.1589 A <--> 5.6157 A
          Mean   = 4.9973 A
          StdDev = 0.4214 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 145.377 deg ; T1  -- T1   3.0913 A

T1  -- O2  -- T1  = 157.095 deg ; T1  -- T1   3.1703 A

T1  -- O3  -- T2  = 139.777 deg ; T1  -- T2   3.0424 A

T1  -- O4  -- T2  = 140.874 deg ; T1  -- T2   3.0530 A

T2  -- O5  -- T2  = 142.413 deg ; T2  -- T2   3.0690 A

T2  -- O6  -- T2  = 135.368 deg ; T2  -- T2   3.0037 A


        T-O-T SUMMARY
          Range  = 135.3681° <--> 157.0946 deg
          Mean   = 143.4841 deg
          StdDev = 6.8229 deg

        T--T SUMMARY
          Range  = 3.0037 A <--> 3.1703 A
          Mean   = 3.0716 A
          StdDev = 0.0518 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 24 42 64 94 129 170 214 259 316 379 444 513 589 671
TD10 = 1012
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 24 42 67 97 129 167 212 264 319 378 443 513 591 672
TD10 = 1018
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

<TD10> = 1015.000
Average ring size = 5.6000