Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_72_2_3541_DRZp70.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 18.27 T-atoms per nm^3
Material density = 1.823 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6156 Angstrom
T1  -- O2  = 1.6162 Angstrom
T1  -- O3  = 1.6147 Angstrom
T1  -- O4  = 1.6209 Angstrom
      mean = 1.6169 Angstrom
        t1 = 0.004550  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002180  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6146 Angstrom
T2  -- O4  = 1.6210 Angstrom
T2  -- O5  = 1.6202 Angstrom
T2  -- O6  = 1.6160 Angstrom
      mean = 1.6180 Angstrom
        t1 = 0.005088  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001626  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6146 A <--> 1.6210 A
          Mean   = 1.6174 A
          StdDev = 0.0026 A

       t1 Range  = 0.0045 <-- 0.0048 --> 0.0051
       t2 Range  = 0.0016 <-- 0.0019 --> 0.0022

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.392 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.147 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.473 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.895 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.390 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.529 deg; O3  -- O4  = 3 A
       109.147 deg <-- 109.471 deg --> 109.895 deg

O3  -- T2  -- O4  = 109.537 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.158 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.874 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 109.484 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.391 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 109.382 deg; O5  -- O6  = 3 A
       109.158 deg <-- 109.471 deg --> 109.874 deg

        O-T-O SUMMARY
          Range  = 109.1474 deg <--> 109.8948 deg
          Mean   = 109.4787 deg
          StdDev = 0.2287 deg

        O--O SUMMARY
          Range  = 2.6323 A <--> 2.6466 A
          Mean   = 2.6414 A
          StdDev = 0.0040 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  =  89.991 deg; T2  -- T2  = 4.3610 A
T2  - O1  - T1  - O3  - T1  = 123.273 deg; T2  -- T1  = 5.5974 A
T2  - O1  - T1  - O4  - T1  =  89.997 deg; T2  -- T1  = 4.4858 A
T2  - O2  - T1  - O3  - T1  = 120.818 deg; T2  -- T1  = 5.4410 A
T2  - O2  - T1  - O4  - T1  = 114.471 deg; T2  -- T1  = 5.2471 A
T1  - O3  - T1  - O4  - T1  = 112.909 deg; T1  -- T1  = 5.3614 A

T1  - O3  - T2  - O4  - T1  =  90.009 deg; T1  -- T1  = 4.3617 A
T1  - O3  - T2  - O5  - T2  = 137.106 deg; T1  -- T2  = 5.7690 A
T1  - O3  - T2  - O6  - T2  =  90.003 deg; T1  -- T2  = 4.4858 A
T1  - O4  - T2  - O5  - T2  = 108.930 deg; T1  -- T2  = 4.9586 A
T1  - O4  - T2  - O6  - T2  = 114.471 deg; T1  -- T2  = 5.2468 A
T2  - O5  - T2  - O6  - T2  = 114.209 deg; T2  -- T2  = 5.2650 A

        T-T-T SUMMARY
          Range  = 89.9909 deg <--> 137.1064 deg
          Mean   = 109.4626 deg
          StdDev = 15.0673 deg

        T--T SUMMARY
          Range  = 4.3610 A <--> 5.7690 A
          Mean   = 5.0698 A
          StdDev = 0.4799 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 172.863 deg ; T1  -- T1   3.2250 A

T1  -- O2  -- T1  = 165.812 deg ; T1  -- T1   3.2078 A

T1  -- O3  -- T2  = 152.362 deg ; T1  -- T2   3.1358 A

T1  -- O4  -- T2  = 138.454 deg ; T1  -- T2   3.0311 A

T2  -- O5  -- T2  = 141.827 deg ; T2  -- T2   3.0623 A

T2  -- O6  -- T2  = 165.868 deg ; T2  -- T2   3.2074 A


        T-O-T SUMMARY
          Range  = 138.4539° <--> 172.8627 deg
          Mean   = 156.1975 deg
          StdDev = 12.9761 deg

        T--T SUMMARY
          Range  = 3.0311 A <--> 3.2250 A
          Mean   = 3.1449 A
          StdDev = 0.0758 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 37 57 81 110 143 180 223 269 319 375 435 499 567
TD10 = 867
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 24
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 24

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 37 57 81 110 143 180 223 269 319 375 435 499 567
TD10 = 867
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 24
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 24

<TD10> = 867.000
Average ring size = 5.8182