Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_72_2_2586_0vEDzT.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 17.59 T-atoms per nm^3
Material density = 1.755 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6187 Angstrom
T1  -- O2  = 1.6157 Angstrom
T1  -- O3  = 1.6154 Angstrom
T1  -- O4  = 1.6196 Angstrom
      mean = 1.6174 Angstrom
        t1 = 0.004868  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001256  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6161 Angstrom
T2  -- O4  = 1.6199 Angstrom
T2  -- O5  = 1.6180 Angstrom
T2  -- O6  = 1.6158 Angstrom
      mean = 1.6175 Angstrom
        t1 = 0.005154  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002190  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6154 A <--> 1.6199 A
          Mean   = 1.6174 A
          StdDev = 0.0017 A

       t1 Range  = 0.0049 <-- 0.0050 --> 0.0052
       t2 Range  = 0.0013 <-- 0.0017 --> 0.0022

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.552 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.324 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.723 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.262 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.306 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.659 deg; O3  -- O4  = 3 A
       109.262 deg <-- 109.471 deg --> 109.723 deg

O3  -- T2  -- O4  = 109.994 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.082 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.238 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 109.135 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.631 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 109.748 deg; O5  -- O6  = 3 A
       109.082 deg <-- 109.471 deg --> 109.994 deg

        O-T-O SUMMARY
          Range  = 109.0818 deg <--> 109.9938 deg
          Mean   = 109.4549 deg
          StdDev = 0.2784 deg

        O--O SUMMARY
          Range  = 2.6343 A <--> 2.6507 A
          Mean   = 2.6410 A
          StdDev = 0.0054 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 116.378 deg; T2  -- T1  = 5.2549 A
T2  - O1  - T1  - O3  - T2  =  81.123 deg; T2  -- T2  = 4.0034 A
T2  - O1  - T1  - O4  - T1  = 128.181 deg; T2  -- T1  = 5.6763 A
T1  - O2  - T1  - O3  - T2  = 116.397 deg; T1  -- T2  = 5.2473 A
T1  - O2  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.4754 A
T2  - O3  - T1  - O4  - T1  = 127.889 deg; T2  -- T1  = 5.6607 A

T1  - O3  - T2  - O4  - T2  = 130.184 deg; T1  -- T2  = 5.6644 A
T1  - O3  - T2  - O5  - T2  = 110.611 deg; T1  -- T2  = 5.1926 A
T1  - O3  - T2  - O6  - T1  =  76.071 deg; T1  -- T1  = 3.7933 A
T2  - O4  - T2  - O5  - T2  =  97.476 deg; T2  -- T2  = 4.8065 A
T2  - O4  - T2  - O6  - T1  = 130.937 deg; T2  -- T1  = 5.6729 A
T2  - O5  - T2  - O6  - T1  = 111.099 deg; T2  -- T1  = 5.2001 A

        T-T-T SUMMARY
          Range  = 76.0705 deg <--> 130.9365 deg
          Mean   = 109.3280 deg
          StdDev = 19.3507 deg

        T--T SUMMARY
          Range  = 3.7933 A <--> 5.6763 A
          Mean   = 5.0382 A
          StdDev = 0.6545 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 146.578 deg ; T1  -- T1   3.1007 A

T1  -- O2  -- T1  = 174.117 deg ; T1  -- T1   3.2272 A

T1  -- O3  -- T2  = 145.125 deg ; T1  -- T2   3.0830 A

T1  -- O4  -- T2  = 143.152 deg ; T1  -- T2   3.0735 A

T2  -- O5  -- T2  = 155.456 deg ; T2  -- T2   3.1621 A

T2  -- O6  -- T2  = 180.000 deg ; T2  -- T2   3.2317 A


        T-O-T SUMMARY
          Range  = 143.1521° <--> 180.0000 deg
          Mean   = 157.4045 deg
          StdDev = 14.5951 deg

        T--T SUMMARY
          Range  = 3.0735 A <--> 3.2317 A
          Mean   = 3.1464 A
          StdDev = 0.0655 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 23 41 60 87 121 154 192 240 292 348 407 465 536 617
TD10 = 933
Circuit symbol = 4.4.6_{2}.8_{4}.6_{2}.8_{4}
Weight = 28
Vertex symbol  = 4.4.6_{2}.8_{2}.6_{2}.8_{2}
Weight = 28

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 21 39 60 89 118 153 195 240 293 341 403 474 539 613
TD10 = 931
Circuit symbol = 4.5_{2}.5.8_{5}.5.8_{5}
Weight = 26
Vertex symbol  = 4.5_{2}.5.8_{3}.5.8_{3}
Weight = 26

<TD10> = 932.000
Average ring size = 6.0577