Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_70_2_790678_yMQPZ8.cif"

There are 40 T-atoms per unit cell
There are 80 O-atoms per unit cell

Framework density = 16.15 T-atoms per nm^3
Material density = 1.611 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6225 Angstrom
T1  -- O2  = 1.6225 Angstrom
T1  -- O3  = 1.6156 Angstrom
T1  -- O4  = 1.6055 Angstrom
      mean = 1.6165 Angstrom
        t1 = 0.007026  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004085  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6189 Angstrom
T2  -- O4  = 1.6189 Angstrom
T2  -- O4  = 1.6189 Angstrom
T2  -- O4  = 1.6189 Angstrom
      mean = 1.6189 Angstrom
        t1 = 0.006879  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003161  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6055 A <--> 1.6225 A
          Mean   = 1.6170 A
          StdDev = 0.0063 A

       t1 Range  = 0.0069 <-- 0.0070 --> 0.0070
       t2 Range  = 0.0032 <-- 0.0036 --> 0.0041

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.554 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.698 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.919 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.698 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.919 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 108.031 deg; O3  -- O4  = 3 A
       108.031 deg <-- 109.470 deg --> 109.919 deg

O4  -- T2  -- O4  = 110.410 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 109.004 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 109.004 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 109.004 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 109.003 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 110.410 deg; O4  -- O4  = 3 A
       109.003 deg <-- 109.473 deg --> 110.410 deg

        O-T-O SUMMARY
          Range  = 108.0312 deg <--> 110.4103 deg
          Mean   = 109.4458 deg
          StdDev = 0.7022 deg

        O--O SUMMARY
          Range  = 2.6065 A <--> 2.6589 A
          Mean   = 2.6407 A
          StdDev = 0.0139 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 126.121 deg; T1  -- T2  = 5.6147 A
T1  - O1  - T1  - O3  - T1  = 128.313 deg; T1  -- T1  = 5.6487 A
T1  - O1  - T1  - O4  - T1  = 128.313 deg; T1  -- T1  = 5.6487 A
T2  - O2  - T1  - O3  - T1  =  91.906 deg; T2  -- T1  = 4.3923 A
T2  - O2  - T1  - O4  - T1  =  91.906 deg; T2  -- T1  = 4.3923 A
T1  - O3  - T1  - O4  - T1  =  75.169 deg; T1  -- T1  = 3.7139 A

T1  - O4  - T2  - O4  - T1  =  74.541 deg; T1  -- T1  = 3.7139 A
T1  - O4  - T2  - O4  - T1  = 129.292 deg; T1  -- T1  = 5.5421 A
T1  - O4  - T2  - O4  - T1  = 129.292 deg; T1  -- T1  = 5.5421 A
T1  - O4  - T2  - O4  - T1  = 129.292 deg; T1  -- T1  = 5.5421 A
T1  - O4  - T2  - O4  - T1  = 129.292 deg; T1  -- T1  = 5.5421 A
T1  - O4  - T2  - O4  - T1  =  74.541 deg; T1  -- T1  = 3.7139 A

        T-T-T SUMMARY
          Range  = 74.5411 deg <--> 129.2922 deg
          Mean   = 108.0770 deg
          StdDev = 24.5351 deg

        T--T SUMMARY
          Range  = 3.7139 A <--> 5.6487 A
          Mean   = 4.8742 A
          StdDev = 0.8376 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 139.515 deg ; T1  -- T1   3.0445 A

T1  -- O2  -- T1  = 139.515 deg ; T1  -- T1   3.0445 A

T1  -- O3  -- T1  = 180.000 deg ; T1  -- T1   3.2312 A

T1  -- O4  -- T2  = 143.976 deg ; T1  -- T2   3.0664 A


        T-O-T SUMMARY
          Range  = 139.5149° <--> 180.0000 deg
          Mean   = 150.7515 deg
          StdDev = 17.0513 deg

        T--T SUMMARY
          Range  = 3.0445 A <--> 3.2312 A
          Mean   = 3.0967 A
          StdDev = 0.0785 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 19 35 52 78 106 139 179 213 266 318 366 439 501 553
TD10 = 835
Circuit symbol = 4.8_{2}.4.8_{2}.4_{2}.8_{4}
Weight = 19
Vertex symbol  = 4.8_{2}.4.8_{2}.4_{2}.8_{4}
Weight = 19

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 8 18 36 56 66 116 140 154 232 264 294 392 432 478 588
TD10 = 831
Circuit symbol = 4_{2}.4_{2}.8_{4}.8_{4}.8_{4}.8_{4}
Weight = 29
Vertex symbol  = 4_{2}.4_{2}.8_{4}.8_{4}.8_{4}.8_{4}
Weight = 29

<TD10> = 834.200
Average ring size = 6.1818