Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_70-2_2_367440_I1CHEj.cif"

There are 64 T-atoms per unit cell
There are 128 O-atoms per unit cell

Framework density = 14.63 T-atoms per nm^3
Material density = 1.460 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6229 Angstrom
T1  -- O4  = 1.6381 Angstrom
T1  -- O2  = 1.5522 Angstrom
T1  -- O3  = 1.6524 Angstrom
      mean = 1.6164 Angstrom
        t1 = 0.036710  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.023060  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.5407 Angstrom
T2  -- O3  = 1.6612 Angstrom
T2  -- O5  = 1.6080 Angstrom
T2  -- O4  = 1.6494 Angstrom
      mean = 1.6148 Angstrom
        t1 = 0.022341  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.017890  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5407 A <--> 1.6612 A
          Mean   = 1.6156 A
          StdDev = 0.0431 A

       t1 Range  = 0.0223 <-- 0.0295 --> 0.0367
       t2 Range  = 0.0179 <-- 0.0205 --> 0.0231

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O4  = 110.473 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 112.602 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 107.113 deg; O1  -- O3  = 3 A
O4  -- T1  -- O2  = 105.466 deg; O4  -- O2  = 3 A
O4  -- T1  -- O3  = 117.428 deg; O4  -- O3  = 3 A
O2  -- T1  -- O3  = 103.698 deg; O2  -- O3  = 3 A
       103.698 deg <-- 109.463 deg --> 117.428 deg

O2  -- T2  -- O3  = 108.332 deg; O2  -- O3  = 3 A
O2  -- T2  -- O5  = 110.687 deg; O2  -- O5  = 3 A
O2  -- T2  -- O4  = 109.613 deg; O2  -- O4  = 3 A
O3  -- T2  -- O5  = 106.165 deg; O3  -- O5  = 3 A
O3  -- T2  -- O4  = 112.888 deg; O3  -- O4  = 3 A
O5  -- T2  -- O4  = 109.117 deg; O5  -- O4  = 3 A
       106.165 deg <-- 109.467 deg --> 112.888 deg

        O-T-O SUMMARY
          Range  = 103.6980 deg <--> 117.4284 deg
          Mean   = 109.4651 deg
          StdDev = 3.5937 deg

        O--O SUMMARY
          Range  = 2.5208 A <--> 2.8120 A
          Mean   = 2.6375 A
          StdDev = 0.0796 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O4  - T2  = 114.154 deg; T1  -- T2  = 5.1757 A
T1  - O1  - T1  - O2  - T2  =  89.762 deg; T1  -- T2  = 4.3379 A
T1  - O1  - T1  - O3  - T2  =  89.762 deg; T1  -- T2  = 4.3379 A
T2  - O4  - T1  - O2  - T2  =  88.355 deg; T2  -- T2  = 4.0561 A
T2  - O4  - T1  - O3  - T2  = 155.613 deg; T2  -- T2  = 5.6890 A
T2  - O2  - T1  - O3  - T2  =  86.987 deg; T2  -- T2  = 3.9891 A

T1  - O2  - T2  - O3  - T2  =  90.238 deg; T1  -- T2  = 4.3379 A
T1  - O2  - T2  - O5  - T1  = 155.145 deg; T1  -- T1  = 5.6840 A
T1  - O2  - T2  - O4  - T1  =  93.011 deg; T1  -- T1  = 4.2045 A
T2  - O3  - T2  - O5  - T1  = 114.154 deg; T2  -- T1  = 5.1551 A
T2  - O3  - T2  - O4  - T1  =  90.238 deg; T2  -- T1  = 4.3379 A
T1  - O5  - T2  - O4  - T1  =  91.645 deg; T1  -- T1  = 4.1743 A

        T-T-T SUMMARY
          Range  = 86.9872 deg <--> 155.6125 deg
          Mean   = 104.9220 deg
          StdDev = 24.3002 deg

        T--T SUMMARY
          Range  = 3.9891 A <--> 5.6890 A
          Mean   = 4.6233 A
          StdDev = 0.5977 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 173.161 deg ; T1  -- T1   3.2400 A

T1  -- O2  -- T2  = 139.089 deg ; T1  -- T2   2.8979 A

T1  -- O3  -- T2  = 121.982 deg ; T1  -- T2   2.8979 A

T1  -- O4  -- T2  = 125.486 deg ; T1  -- T2   2.9225 A

T2  -- O5  -- T2  = 179.750 deg ; T2  -- T2   3.2160 A


        T-O-T SUMMARY
          Range  = 121.9821° <--> 179.7498 deg
          Mean   = 147.8935 deg
          StdDev = 24.1766 deg

        T--T SUMMARY
          Range  = 2.8979 A <--> 3.2400 A
          Mean   = 3.0349 A
          StdDev = 0.1586 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 32
Coordination Sequence =
    1 4 8 13 21 34 52 71 90 115 147 178 207 243 287 331 373
TD10 = 556
Circuit symbol = 4.4.4.6.4.6
Weight = 9
Vertex symbol  = 4.4.4.12.4.12_{2}
Weight = 33

T2 (Si): multiplicity = 32
Coordination Sequence =
    1 4 8 13 21 34 52 71 90 115 147 178 207 243 287 331 373
TD10 = 556
Circuit symbol = 4.4.4.6.4.6
Weight = 9
Vertex symbol  = 4.4.4.12.4.12_{2}
Weight = 33

<TD10> = 556.000
Average ring size = 5.6000