Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_70-2_2_200671_EHwQUG.cif"

There are 64 T-atoms per unit cell
There are 128 O-atoms per unit cell

Framework density = 26.01 T-atoms per nm^3
Material density = 2.596 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6163 Angstrom
T1  -- O3  = 1.6249 Angstrom
T1  -- O4  = 1.6225 Angstrom
T1  -- O2  = 1.6252 Angstrom
      mean = 1.6222 Angstrom
        t1 = 0.009459  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.007560  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6241 Angstrom
T2  -- O3  = 1.6257 Angstrom
T2  -- O4  = 1.6224 Angstrom
T2  -- O5  = 1.6162 Angstrom
      mean = 1.6221 Angstrom
        t1 = 0.009383  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005452  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6162 A <--> 1.6257 A
          Mean   = 1.6222 A
          StdDev = 0.0036 A

       t1 Range  = 0.0094 <-- 0.0094 --> 0.0095
       t2 Range  = 0.0055 <-- 0.0065 --> 0.0076

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 109.454 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.051 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 109.928 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 110.565 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 108.940 deg; O3  -- O2  = 3 A
O4  -- T1  -- O2  = 109.893 deg; O4  -- O2  = 3 A
       108.051 deg <-- 109.472 deg --> 110.565 deg

O2  -- T2  -- O3  = 109.088 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 110.420 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.419 deg; O2  -- O5  = 3 A
O3  -- T2  -- O4  = 109.951 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.963 deg; O3  -- O5  = 3 A
O4  -- T2  -- O5  = 107.987 deg; O4  -- O5  = 3 A
       107.987 deg <-- 109.471 deg --> 110.420 deg

        O-T-O SUMMARY
          Range  = 107.9871 deg <--> 110.5652 deg
          Mean   = 109.4716 deg
          StdDev = 0.7973 deg

        O--O SUMMARY
          Range  = 2.6198 A <--> 2.6693 A
          Mean   = 2.6489 A
          StdDev = 0.0149 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O3  - T2  = 103.010 deg; T1  -- T2  = 4.7600 A
T1  - O1  - T1  - O4  - T2  = 139.915 deg; T1  -- T2  = 5.7008 A
T1  - O1  - T1  - O2  - T2  =  93.552 deg; T1  -- T2  = 4.4208 A
T2  - O3  - T1  - O4  - T2  = 114.090 deg; T2  -- T2  = 5.0565 A
T2  - O3  - T1  - O2  - T2  = 116.485 deg; T2  -- T2  = 5.1225 A
T2  - O4  - T1  - O2  - T2  =  83.478 deg; T2  -- T2  = 4.0018 A

T1  - O2  - T2  - O3  - T2  =  93.561 deg; T1  -- T2  = 4.4161 A
T1  - O2  - T2  - O4  - T1  = 116.495 deg; T1  -- T1  = 5.1242 A
T1  - O2  - T2  - O5  - T1  =  83.917 deg; T1  -- T1  = 4.0189 A
T2  - O3  - T2  - O4  - T1  = 102.474 deg; T2  -- T1  = 4.7356 A
T2  - O3  - T2  - O5  - T1  = 140.405 deg; T2  -- T1  = 5.7001 A
T1  - O4  - T2  - O5  - T1  = 114.007 deg; T1  -- T1  = 5.0528 A

        T-T-T SUMMARY
          Range  = 83.4775 deg <--> 140.4046 deg
          Mean   = 108.4491 deg
          StdDev = 18.1379 deg

        T--T SUMMARY
          Range  = 4.0018 A <--> 5.7008 A
          Mean   = 4.8425 A
          StdDev = 0.5394 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 142.604 deg ; T1  -- T1   3.0619 A

T1  -- O2  -- T2  = 135.402 deg ; T1  -- T2   3.0063 A

T1  -- O3  -- T2  = 135.143 deg ; T1  -- T2   3.0047 A

T1  -- O4  -- T2  = 137.065 deg ; T1  -- T2   3.0198 A

T2  -- O5  -- T2  = 141.697 deg ; T2  -- T2   3.0535 A


        T-O-T SUMMARY
          Range  = 135.1428° <--> 142.6039 deg
          Mean   = 138.3821 deg
          StdDev = 3.1699 deg

        T--T SUMMARY
          Range  = 3.0047 A <--> 3.0619 A
          Mean   = 3.0292 A
          StdDev = 0.0240 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 32
Coordination Sequence =
    1 4 11 24 43 68 102 139 183 230 283 343 410 479 555 638 727
TD10 = 1088
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 32
Coordination Sequence =
    1 4 11 24 43 68 102 139 183 230 283 343 410 479 555 638 727
TD10 = 1088
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

<TD10> = 1088.000
Average ring size = 5.6000