Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_70-2_2_199966_BcRuaJ.cif"

There are 64 T-atoms per unit cell
There are 128 O-atoms per unit cell

Framework density = 27.60 T-atoms per nm^3
Material density = 2.754 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6013 Angstrom
T1  -- O4  = 1.6380 Angstrom
T1  -- O2  = 1.6366 Angstrom
T1  -- O3  = 1.6413 Angstrom
      mean = 1.6293 Angstrom
        t1 = 0.028555  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.023468  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6400 Angstrom
T2  -- O3  = 1.6331 Angstrom
T2  -- O5  = 1.6028 Angstrom
T2  -- O4  = 1.6405 Angstrom
      mean = 1.6291 Angstrom
        t1 = 0.025856  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.015250  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6013 A <--> 1.6413 A
          Mean   = 1.6292 A
          StdDev = 0.0159 A

       t1 Range  = 0.0259 <-- 0.0272 --> 0.0286
       t2 Range  = 0.0153 <-- 0.0194 --> 0.0235

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O4  = 106.408 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 106.159 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 112.463 deg; O1  -- O3  = 3 A
O4  -- T1  -- O2  = 116.511 deg; O4  -- O2  = 3 A
O4  -- T1  -- O3  = 109.372 deg; O4  -- O3  = 3 A
O2  -- T1  -- O3  = 106.038 deg; O2  -- O3  = 3 A
       106.038 deg <-- 109.492 deg --> 116.511 deg

O2  -- T2  -- O3  = 106.093 deg; O2  -- O3  = 3 A
O2  -- T2  -- O5  = 111.420 deg; O2  -- O5  = 3 A
O2  -- T2  -- O4  = 108.034 deg; O2  -- O4  = 3 A
O3  -- T2  -- O5  = 106.941 deg; O3  -- O5  = 3 A
O3  -- T2  -- O4  = 116.421 deg; O3  -- O4  = 3 A
O5  -- T2  -- O4  = 107.972 deg; O5  -- O4  = 3 A
       106.093 deg <-- 109.480 deg --> 116.421 deg

        O-T-O SUMMARY
          Range  = 106.0384 deg <--> 116.5108 deg
          Mean   = 109.4860 deg
          StdDev = 3.7115 deg

        O--O SUMMARY
          Range  = 2.5887 A <--> 2.7848 A
          Mean   = 2.6594 A
          StdDev = 0.0650 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O4  - T2  =  77.588 deg; T1  -- T2  = 3.7559 A
T1  - O1  - T1  - O2  - T2  = 124.944 deg; T1  -- T2  = 5.0015 A
T1  - O1  - T1  - O3  - T2  = 123.597 deg; T1  -- T2  = 5.0563 A
T2  - O4  - T1  - O2  - T2  = 106.077 deg; T2  -- T2  = 4.7186 A
T2  - O4  - T1  - O3  - T2  = 145.764 deg; T2  -- T2  = 5.7319 A
T2  - O2  - T1  - O3  - T2  =  84.215 deg; T2  -- T2  = 3.7897 A

T1  - O2  - T2  - O3  - T2  = 122.504 deg; T1  -- T2  = 5.1271 A
T1  - O2  - T2  - O5  - T1  = 104.102 deg; T1  -- T1  = 4.7315 A
T1  - O2  - T2  - O4  - T1  =  84.386 deg; T1  -- T1  = 3.7960 A
T2  - O3  - T2  - O5  - T1  =  82.635 deg; T2  -- T1  = 4.0266 A
T2  - O3  - T2  - O4  - T1  = 120.466 deg; T2  -- T1  = 4.9924 A
T1  - O5  - T2  - O4  - T1  = 146.465 deg; T1  -- T1  = 5.6496 A

        T-T-T SUMMARY
          Range  = 77.5879 deg <--> 146.4655 deg
          Mean   = 110.2286 deg
          StdDev = 23.2194 deg

        T--T SUMMARY
          Range  = 3.7559 A <--> 5.7319 A
          Mean   = 4.6981 A
          StdDev = 0.6745 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 126.768 deg ; T1  -- T1   2.8632 A

T1  -- O2  -- T2  = 122.610 deg ; T1  -- T2   2.8742 A

T1  -- O3  -- T2  = 115.990 deg ; T1  -- T2   2.7767 A

T1  -- O4  -- T2  = 144.553 deg ; T1  -- T2   3.1229 A

T2  -- O5  -- T2  = 136.118 deg ; T2  -- T2   2.9735 A


        T-O-T SUMMARY
          Range  = 115.9897° <--> 144.5526 deg
          Mean   = 129.2075 deg
          StdDev = 10.1055 deg

        T--T SUMMARY
          Range  = 2.7767 A <--> 3.1229 A
          Mean   = 2.9221 A
          StdDev = 0.1186 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O3  -- O3  = 2.2810 A
T1  -- T2  = 2.7767 Angstrom
T2  -- T1  = 2.7767 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 32
Coordination Sequence =
    1 4 11 24 43 68 102 139 183 230 283 343 410 479 555 638 727
TD10 = 1088
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 32
Coordination Sequence =
    1 4 11 24 43 68 102 139 183 230 283 343 410 479 555 638 727
TD10 = 1088
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

<TD10> = 1088.000
Average ring size = 5.6000