Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_69_4_4437772_He_mdP.cif"

There are 128 T-atoms per unit cell
There are 256 O-atoms per unit cell

Framework density = 17.72 T-atoms per nm^3
Material density = 1.768 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6217 Angstrom
T1  -- O2  = 1.6165 Angstrom
T1  -- O3  = 1.6169 Angstrom
T1  -- O4  = 1.6200 Angstrom
      mean = 1.6188 Angstrom
        t1 = 0.006137  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001818  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6159 Angstrom
T2  -- O5  = 1.6219 Angstrom
T2  -- O6  = 1.6186 Angstrom
T2  -- O7  = 1.6168 Angstrom
      mean = 1.6183 Angstrom
        t1 = 0.005506  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002399  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6204 Angstrom
T3  -- O8  = 1.6208 Angstrom
T3  -- O9  = 1.6188 Angstrom
T3  -- O10 = 1.6217 Angstrom
      mean = 1.6204 Angstrom
        t1 = 0.006612  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001898  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6166 Angstrom
T4  -- O10 = 1.6211 Angstrom
T4  -- O11 = 1.6184 Angstrom
T4  -- O12 = 1.6206 Angstrom
      mean = 1.6192 Angstrom
        t1 = 0.005974  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002735  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6159 A <--> 1.6219 A
          Mean   = 1.6192 A
          StdDev = 0.0020 A

       t1 Range  = 0.0055 <-- 0.0061 --> 0.0066
       t2 Range  = 0.0018 <-- 0.0022 --> 0.0027

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.366 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.357 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.973 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.842 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.786 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.496 deg; O3  -- O4  = 3 A
       108.842 deg <-- 109.470 deg --> 109.973 deg

O3  -- T2  -- O5  = 109.555 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.054 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 109.323 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.419 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.751 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.724 deg; O6  -- O7  = 3 A
       109.054 deg <-- 109.471 deg --> 109.751 deg

O4  -- T3  -- O8  = 109.646 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 109.119 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 109.311 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 109.687 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.486 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.577 deg; O9  -- O10 = 3 A
       109.119 deg <-- 109.471 deg --> 109.687 deg

O7  -- T4  -- O10 = 109.629 deg; O7  -- O10 = 3 A
O7  -- T4  -- O11 = 109.000 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 109.656 deg; O7  -- O12 = 3 A
O10 -- T4  -- O11 = 109.479 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 109.408 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 109.655 deg; O11 -- O12 = 3 A
       109.000 deg <-- 109.471 deg --> 109.656 deg

        O-T-O SUMMARY
          Range  = 108.8418 deg <--> 109.9727 deg
          Mean   = 109.4653 deg
          StdDev = 0.2723 deg

        O--O SUMMARY
          Range  = 2.6298 A <--> 2.6549 A
          Mean   = 2.6439 A
          StdDev = 0.0058 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 116.753 deg; T1  -- T2  = 5.2074 A
T1  - O1  - T1  - O3  - T3  =  98.939 deg; T1  -- T3  = 4.6183 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.3814 A
T2  - O2  - T1  - O3  - T3  = 119.788 deg; T2  -- T3  = 5.3177 A
T2  - O2  - T1  - O4  - T1  = 133.850 deg; T2  -- T1  = 5.7639 A
T3  - O3  - T1  - O4  - T1  =  89.154 deg; T3  -- T1  = 4.3706 A

T1  - O3  - T2  - O5  - T2  = 117.607 deg; T1  -- T2  = 5.2227 A
T1  - O3  - T2  - O6  - T4  = 116.611 deg; T1  -- T4  = 5.2622 A
T1  - O3  - T2  - O7  - T2  = 136.143 deg; T1  -- T2  = 5.7794 A
T2  - O5  - T2  - O6  - T4  =  98.408 deg; T2  -- T4  = 4.6212 A
T2  - O5  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.3493 A
T4  - O6  - T2  - O7  - T2  =  89.510 deg; T4  -- T2  = 4.3856 A

T1  - O4  - T3  - O8  - T3  =  90.846 deg; T1  -- T3  = 4.3706 A
T1  - O4  - T3  - O9  - T4  = 117.809 deg; T1  -- T4  = 5.2259 A
T1  - O4  - T3  - O10 - T3  = 138.383 deg; T1  -- T3  = 5.7983 A
T3  - O8  - T3  - O9  - T4  = 135.166 deg; T3  -- T4  = 5.6676 A
T3  - O8  - T3  - O10 - T3  =  90.000 deg; T3  -- T3  = 4.4061 A
T4  - O9  - T3  - O10 - T3  =  89.316 deg; T4  -- T3  = 4.3569 A

T2  - O7  - T4  - O10 - T3  = 116.436 deg; T2  -- T3  = 5.2198 A
T2  - O7  - T4  - O11 - T4  =  90.490 deg; T2  -- T4  = 4.3856 A
T2  - O7  - T4  - O12 - T4  = 139.523 deg; T2  -- T4  = 5.7869 A
T3  - O10 - T4  - O11 - T4  = 134.826 deg; T3  -- T4  = 5.6628 A
T3  - O10 - T4  - O12 - T4  =  90.684 deg; T3  -- T4  = 4.3569 A
T4  - O11 - T4  - O12 - T4  =  90.000 deg; T4  -- T4  = 4.3561 A

        T-T-T SUMMARY
          Range  = 89.1535 deg <--> 139.5233 deg
          Mean   = 109.0945 deg
          StdDev = 19.2720 deg

        T--T SUMMARY
          Range  = 4.3493 A <--> 5.7983 A
          Mean   = 4.9521 A
          StdDev = 0.5787 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 137.450 deg ; T1  -- T1   3.0223 A

T1  -- O2  -- T1  = 157.719 deg ; T1  -- T1   3.1721 A

T1  -- O3  -- T2  = 146.185 deg ; T1  -- T2   3.0930 A

T1  -- O4  -- T3  = 140.934 deg ; T1  -- T3   3.0539 A

T2  -- O5  -- T2  = 136.459 deg ; T2  -- T2   3.0124 A

T2  -- O6  -- T2  = 151.449 deg ; T2  -- T2   3.1372 A

T2  -- O7  -- T4  = 145.925 deg ; T2  -- T4   3.0915 A

T3  -- O8  -- T3  = 143.872 deg ; T3  -- T3   3.0819 A

T3  -- O9  -- T3  = 153.115 deg ; T3  -- T3   3.1489 A

T3  -- O10 -- T4  = 140.178 deg ; T3  -- T4   3.0490 A

T4  -- O11 -- T4  = 143.749 deg ; T4  -- T4   3.0761 A

T4  -- O12 -- T4  = 144.201 deg ; T4  -- T4   3.0842 A


        T-O-T SUMMARY
          Range  = 136.4585° <--> 157.7189 deg
          Mean   = 145.1030 deg
          StdDev = 6.0945 deg

        T--T SUMMARY
          Range  = 3.0124 A <--> 3.1721 A
          Mean   = 3.0852 A
          StdDev = 0.0467 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 32
Coordination Sequence =
    1 4 10 21 36 53 74 100 129 163 203 245 291 344 399 456 519
TD10 = 794
Circuit symbol = 4.6.4.8_{3}.6_{2}.8_{3}
Weight = 27
Vertex symbol  = 4.6.4.8_{3}.6.8
Weight = 26

T2 (Si): multiplicity = 32
Coordination Sequence =
    1 4 10 21 36 53 74 100 129 163 203 245 291 344 399 456 519
TD10 = 794
Circuit symbol = 4.6.4.8_{3}.6_{2}.8_{3}
Weight = 27
Vertex symbol  = 4.6.4.8_{3}.6.8
Weight = 26

T3 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 18 32 50 74 103 133 166 204 245 290 340 392 448 513
TD10 = 794
Circuit symbol = 4.4.4.6.6.6
Weight = 11
Vertex symbol  = 4.4.4.6.8.8
Weight = 21

T4 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 18 32 50 74 103 133 166 204 245 290 340 392 448 513
TD10 = 794
Circuit symbol = 4.4.4.6.6.6
Weight = 11
Vertex symbol  = 4.4.4.6.8.8
Weight = 21

<TD10> = 794.000
Average ring size = 5.6000