Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_69_2_361_A3c0WP.cif"

There are 48 T-atoms per unit cell
There are 96 O-atoms per unit cell

Framework density = 19.46 T-atoms per nm^3
Material density = 1.941 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6161 Angstrom
T1  -- O2  = 1.6213 Angstrom
T1  -- O3  = 1.6144 Angstrom
T1  -- O4  = 1.6138 Angstrom
      mean = 1.6164 Angstrom
        t1 = 0.004805  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002208  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6187 Angstrom
T2  -- O5  = 1.6154 Angstrom
T2  -- O6  = 1.6260 Angstrom
T2  -- O4  = 1.6187 Angstrom
      mean = 1.6197 Angstrom
        t1 = 0.007583  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004681  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6138 A <--> 1.6260 A
          Mean   = 1.6175 A
          StdDev = 0.0037 A

       t1 Range  = 0.0048 <-- 0.0062 --> 0.0076
       t2 Range  = 0.0022 <-- 0.0034 --> 0.0047

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.748 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.232 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.078 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.239 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.021 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.508 deg; O3  -- O4  = 3 A
       109.078 deg <-- 109.471 deg --> 110.021 deg

O4  -- T2  -- O5  = 108.845 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 110.142 deg; O4  -- O6  = 3 A
O4  -- T2  -- O4  = 109.555 deg; O4  -- O4  = 3 A
O5  -- T2  -- O6  = 109.283 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 108.845 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 110.142 deg; O6  -- O4  = 3 A
       108.845 deg <-- 109.469 deg --> 110.142 deg

        O-T-O SUMMARY
          Range  = 108.8447 deg <--> 110.1420 deg
          Mean   = 109.4938 deg
          StdDev = 0.4810 deg

        O--O SUMMARY
          Range  = 2.6304 A <--> 2.6602 A
          Mean   = 2.6425 A
          StdDev = 0.0112 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  82.123 deg; T1  -- T1  = 4.0772 A
T1  - O1  - T1  - O3  - T2  = 122.043 deg; T1  -- T2  = 5.5107 A
T1  - O1  - T1  - O4  - T1  = 110.977 deg; T1  -- T1  = 5.2976 A
T1  - O2  - T1  - O3  - T2  = 111.011 deg; T1  -- T2  = 5.0207 A
T1  - O2  - T1  - O4  - T1  = 112.507 deg; T1  -- T1  = 5.1746 A
T2  - O3  - T1  - O4  - T1  = 114.011 deg; T2  -- T1  = 5.2995 A

T1  - O4  - T2  - O5  - T2  = 114.011 deg; T1  -- T2  = 5.1122 A
T1  - O4  - T2  - O6  - T1  =  92.809 deg; T1  -- T1  = 4.4815 A
T1  - O4  - T2  - O4  - T2  = 123.829 deg; T1  -- T2  = 5.5754 A
T2  - O5  - T2  - O6  - T1  = 114.011 deg; T2  -- T1  = 5.1122 A
T2  - O5  - T2  - O4  - T2  =  90.000 deg; T2  -- T2  = 4.4053 A
T1  - O6  - T2  - O4  - T2  = 123.829 deg; T1  -- T2  = 5.5754 A

        T-T-T SUMMARY
          Range  = 82.1233 deg <--> 123.8287 deg
          Mean   = 109.5449 deg
          StdDev = 12.7544 deg

        T--T SUMMARY
          Range  = 4.0772 A <--> 5.5754 A
          Mean   = 5.0773 A
          StdDev = 0.4545 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 165.153 deg ; T1  -- T1   3.2051 A

T1  -- O2  -- T1  = 135.155 deg ; T1  -- T1   2.9974 A

T1  -- O3  -- T1  = 173.811 deg ; T1  -- T1   3.2240 A

T1  -- O4  -- T2  = 146.336 deg ; T1  -- T2   3.0940 A

T2  -- O5  -- T2  = 173.236 deg ; T2  -- T2   3.2252 A

T2  -- O6  -- T2  = 134.670 deg ; T2  -- T2   3.0009 A


        T-O-T SUMMARY
          Range  = 134.6698° <--> 173.8105 deg
          Mean   = 154.8814 deg
          StdDev = 16.1670 deg

        T--T SUMMARY
          Range  = 2.9974 A <--> 3.2252 A
          Mean   = 3.1267 A
          StdDev = 0.0964 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 32
Coordination Sequence =
    1 4 11 22 39 63 89 118 152 195 242 290 344 404 472 540 612
TD10 = 936
Circuit symbol = 4.6.6.6_{3}.6_{2}.6_{3}
Weight = 21
Vertex symbol  = 4.6.6.6_{3}.6_{2}.6_{3}
Weight = 21

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 24 41 60 85 119 157 196 239 290 347 406 468 536 613
TD10 = 937
Circuit symbol = 4.6_{2}.6_{2}.8_{5}.6_{2}.8_{5}
Weight = 31
Vertex symbol  = 4.6_{2}.6_{2}.8_{3}.6_{2}.8_{3}
Weight = 31

<TD10> = 936.333
Average ring size = 6.0000