Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_69_2_329_GdksQT.cif"

There are 48 T-atoms per unit cell
There are 96 O-atoms per unit cell

Framework density = 19.57 T-atoms per nm^3
Material density = 1.952 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6159 Angstrom
T1  -- O2  = 1.6218 Angstrom
T1  -- O3  = 1.6144 Angstrom
T1  -- O4  = 1.6164 Angstrom
      mean = 1.6171 Angstrom
        t1 = 0.005438  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002681  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6190 Angstrom
T2  -- O5  = 1.6269 Angstrom
T2  -- O6  = 1.6154 Angstrom
T2  -- O4  = 1.6190 Angstrom
      mean = 1.6201 Angstrom
        t1 = 0.008453  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005643  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6144 A <--> 1.6269 A
          Mean   = 1.6181 A
          StdDev = 0.0036 A

       t1 Range  = 0.0054 <-- 0.0069 --> 0.0085
       t2 Range  = 0.0027 <-- 0.0042 --> 0.0056

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.673 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.206 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.043 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.204 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.209 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.488 deg; O3  -- O4  = 3 A
       109.043 deg <-- 109.471 deg --> 110.209 deg

O4  -- T2  -- O5  = 110.318 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 108.639 deg; O4  -- O6  = 3 A
O4  -- T2  -- O4  = 109.637 deg; O4  -- O4  = 3 A
O5  -- T2  -- O6  = 109.249 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 110.318 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 108.639 deg; O6  -- O4  = 3 A
       108.639 deg <-- 109.467 deg --> 110.318 deg

        O-T-O SUMMARY
          Range  = 108.6395 deg <--> 110.3177 deg
          Mean   = 109.5021 deg
          StdDev = 0.6142 deg

        O--O SUMMARY
          Range  = 2.6273 A <--> 2.6640 A
          Mean   = 2.6437 A
          StdDev = 0.0135 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  82.073 deg; T1  -- T1  = 4.0663 A
T1  - O1  - T1  - O3  - T2  = 121.632 deg; T1  -- T2  = 5.4973 A
T1  - O1  - T1  - O4  - T1  = 110.940 deg; T1  -- T1  = 5.3024 A
T1  - O2  - T1  - O3  - T2  = 111.165 deg; T1  -- T2  = 4.9987 A
T1  - O2  - T1  - O4  - T1  = 112.699 deg; T1  -- T1  = 5.1622 A
T2  - O3  - T1  - O4  - T1  = 114.168 deg; T2  -- T1  = 5.2957 A

T1  - O4  - T2  - O5  - T1  =  91.816 deg; T1  -- T1  = 4.4298 A
T1  - O4  - T2  - O6  - T2  = 114.168 deg; T1  -- T2  = 5.1032 A
T1  - O4  - T2  - O4  - T2  = 124.237 deg; T1  -- T2  = 5.5759 A
T1  - O5  - T2  - O6  - T2  = 114.168 deg; T1  -- T2  = 5.1032 A
T1  - O5  - T2  - O4  - T2  = 124.237 deg; T1  -- T2  = 5.5759 A
T2  - O6  - T2  - O4  - T2  =  90.000 deg; T2  -- T2  = 4.4004 A

        T-T-T SUMMARY
          Range  = 82.0730 deg <--> 124.2371 deg
          Mean   = 109.5632 deg
          StdDev = 12.9891 deg

        T--T SUMMARY
          Range  = 4.0663 A <--> 5.5759 A
          Mean   = 5.0669 A
          StdDev = 0.4629 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 167.431 deg ; T1  -- T1   3.2124 A

T1  -- O2  -- T1  = 133.056 deg ; T1  -- T1   2.9752 A

T1  -- O3  -- T1  = 173.658 deg ; T1  -- T1   3.2239 A

T1  -- O4  -- T2  = 144.779 deg ; T1  -- T2   3.0838 A

T2  -- O5  -- T2  = 133.991 deg ; T2  -- T2   2.9950 A

T2  -- O6  -- T2  = 172.489 deg ; T2  -- T2   3.2239 A


        T-O-T SUMMARY
          Range  = 133.0561° <--> 173.6577 deg
          Mean   = 154.4328 deg
          StdDev = 17.1457 deg

        T--T SUMMARY
          Range  = 2.9752 A <--> 3.2239 A
          Mean   = 3.1210 A
          StdDev = 0.1050 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 32
Coordination Sequence =
    1 4 11 22 39 63 89 118 152 195 242 290 344 404 472 540 612
TD10 = 936
Circuit symbol = 4.6.6.6_{3}.6_{2}.6_{3}
Weight = 21
Vertex symbol  = 4.6.6.6_{3}.6_{2}.6_{3}
Weight = 21

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 24 41 60 85 119 157 196 239 290 347 406 468 536 613
TD10 = 937
Circuit symbol = 4.6_{2}.6_{2}.8_{5}.6_{2}.8_{5}
Weight = 31
Vertex symbol  = 4.6_{2}.6_{2}.8_{3}.6_{2}.8_{3}
Weight = 31

<TD10> = 936.333
Average ring size = 6.0000