Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_65_4_673721_MNx7uo.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 19.20 T-atoms per nm^3
Material density = 1.916 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6111 Angstrom
T1  -- O2  = 1.6271 Angstrom
T1  -- O3  = 1.6248 Angstrom
T1  -- O3  = 1.6248 Angstrom
      mean = 1.6219 Angstrom
        t1 = 0.015707  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.014741  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6284 Angstrom
T2  -- O4  = 1.6266 Angstrom
T2  -- O5  = 1.6200 Angstrom
T2  -- O5  = 1.6200 Angstrom
      mean = 1.6237 Angstrom
        t1 = 0.011816  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006922  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O3  = 1.6247 Angstrom
T3  -- O3  = 1.6247 Angstrom
T3  -- O6  = 1.6132 Angstrom
T3  -- O7  = 1.6021 Angstrom
      mean = 1.6162 Angstrom
        t1 = 0.011982  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.012443  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O5  = 1.6187 Angstrom
T4  -- O5  = 1.6187 Angstrom
T4  -- O7  = 1.6033 Angstrom
T4  -- O8  = 1.6226 Angstrom
      mean = 1.6159 Angstrom
        t1 = 0.006985  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004022  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6021 A <--> 1.6284 A
          Mean   = 1.6194 A
          StdDev = 0.0079 A

       t1 Range  = 0.0070 <-- 0.0116 --> 0.0157
       t2 Range  = 0.0040 <-- 0.0095 --> 0.0147

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.785 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 106.829 deg; O1  -- O3  = 3 A
O1  -- T1  -- O3  = 106.829 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 111.170 deg; O2  -- O3  = 3 A
O2  -- T1  -- O3  = 111.170 deg; O2  -- O3  = 3 A
O3  -- T1  -- O3  = 110.865 deg; O3  -- O3  = 3 A
       106.829 deg <-- 109.442 deg --> 111.170 deg

O2  -- T2  -- O4  = 109.162 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 110.567 deg; O2  -- O5  = 3 A
O2  -- T2  -- O5  = 110.567 deg; O2  -- O5  = 3 A
O4  -- T2  -- O5  = 107.692 deg; O4  -- O5  = 3 A
O4  -- T2  -- O5  = 107.692 deg; O4  -- O5  = 3 A
O5  -- T2  -- O5  = 111.055 deg; O5  -- O5  = 3 A
       107.692 deg <-- 109.456 deg --> 111.055 deg

O3  -- T3  -- O3  = 110.335 deg; O3  -- O3  = 3 A
O3  -- T3  -- O6  = 106.601 deg; O3  -- O6  = 3 A
O3  -- T3  -- O7  = 110.771 deg; O3  -- O7  = 3 A
O3  -- T3  -- O6  = 106.601 deg; O3  -- O6  = 3 A
O3  -- T3  -- O7  = 110.771 deg; O3  -- O7  = 3 A
O6  -- T3  -- O7  = 111.607 deg; O6  -- O7  = 3 A
       106.601 deg <-- 109.448 deg --> 111.607 deg

O5  -- T4  -- O5  = 111.239 deg; O5  -- O5  = 3 A
O5  -- T4  -- O7  = 109.592 deg; O5  -- O7  = 3 A
O5  -- T4  -- O8  = 108.842 deg; O5  -- O8  = 3 A
O5  -- T4  -- O7  = 109.592 deg; O5  -- O7  = 3 A
O5  -- T4  -- O8  = 108.842 deg; O5  -- O8  = 3 A
O7  -- T4  -- O8  = 108.687 deg; O7  -- O8  = 3 A
       108.687 deg <-- 109.466 deg --> 111.239 deg

        O-T-O SUMMARY
          Range  = 106.6008 deg <--> 111.6070 deg
          Mean   = 109.4201 deg
          StdDev = 1.6552 deg

        O--O SUMMARY
          Range  = 2.5961 A <--> 2.6827 A
          Mean   = 2.6438 A
          StdDev = 0.0289 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  98.506 deg; T1  -- T2  = 4.8599 A
T1  - O1  - T1  - O3  - T3  =  81.859 deg; T1  -- T3  = 4.0247 A
T1  - O1  - T1  - O3  - T3  =  81.859 deg; T1  -- T3  = 4.0247 A
T2  - O2  - T1  - O3  - T3  = 112.812 deg; T2  -- T3  = 5.0863 A
T2  - O2  - T1  - O3  - T3  = 112.812 deg; T2  -- T3  = 5.0863 A
T3  - O3  - T1  - O3  - T3  = 133.223 deg; T3  -- T3  = 5.3430 A

T1  - O2  - T2  - O4  - T4  =  96.586 deg; T1  -- T4  = 4.7750 A
T1  - O2  - T2  - O5  - T2  = 146.508 deg; T1  -- T2  = 5.8559 A
T1  - O2  - T2  - O5  - T4  =  96.586 deg; T1  -- T4  = 4.7750 A
T4  - O4  - T2  - O5  - T2  = 101.665 deg; T4  -- T2  = 4.7524 A
T4  - O4  - T2  - O5  - T4  = 113.018 deg; T4  -- T4  = 5.3430 A
T2  - O5  - T2  - O5  - T4  = 101.665 deg; T2  -- T4  = 4.7524 A

T1  - O3  - T3  - O3  - T3  =  81.785 deg; T1  -- T3  = 4.0247 A
T1  - O3  - T3  - O6  - T4  = 112.998 deg; T1  -- T4  = 5.0554 A
T1  - O3  - T3  - O7  - T1  = 133.223 deg; T1  -- T1  = 5.3430 A
T3  - O3  - T3  - O6  - T4  = 100.906 deg; T3  -- T4  = 4.9169 A
T3  - O3  - T3  - O7  - T1  =  81.785 deg; T3  -- T1  = 4.0247 A
T4  - O6  - T3  - O7  - T1  = 112.998 deg; T4  -- T1  = 5.0554 A

T2  - O5  - T4  - O5  - T3  =  95.820 deg; T2  -- T3  = 4.7147 A
T2  - O5  - T4  - O7  - T4  = 120.892 deg; T2  -- T4  = 5.4644 A
T2  - O5  - T4  - O8  - T2  = 113.018 deg; T2  -- T2  = 5.3430 A
T3  - O5  - T4  - O7  - T4  = 100.906 deg; T3  -- T4  = 4.8024 A
T3  - O5  - T4  - O8  - T2  =  95.820 deg; T3  -- T2  = 4.7147 A
T4  - O7  - T4  - O8  - T2  = 120.892 deg; T4  -- T2  = 5.4644 A

        T-T-T SUMMARY
          Range  = 81.7851 deg <--> 146.5083 deg
          Mean   = 106.0751 deg
          StdDev = 17.2352 deg

        T--T SUMMARY
          Range  = 4.0247 A <--> 5.8559 A
          Mean   = 4.8875 A
          StdDev = 0.5003 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2221 A

T1  -- O2  -- T2  = 157.451 deg ; T1  -- T2   3.1927 A

T1  -- O3  -- T3  = 127.208 deg ; T1  -- T3   2.9107 A

T2  -- O4  -- T2  = 127.848 deg ; T2  -- T2   2.9220 A

T2  -- O5  -- T4  = 163.036 deg ; T2  -- T4   3.2033 A

T3  -- O6  -- T3  = 180.000 deg ; T3  -- T3   3.2264 A

T3  -- O7  -- T4  = 158.607 deg ; T3  -- T4   3.1497 A

T4  -- O8  -- T4  = 143.054 deg ; T4  -- T4   3.0780 A


        T-O-T SUMMARY
          Range  = 127.2077° <--> 180.0000 deg
          Mean   = 154.6506 deg
          StdDev = 19.4691 deg

        T--T SUMMARY
          Range  = 2.9107 A <--> 3.2264 A
          Mean   = 3.1131 A
          StdDev = 0.1231 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 16 32 56 69 87 127 170 212 252 270 325 408 476 524
TD10 = 784
Circuit symbol = 4.5.4.5.5_{2}.6_{2}
Weight = 12
Vertex symbol  = 4.5.4.5.5_{2}.*
Weight = 9

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 23 35 50 74 104 141 172 198 239 301 352 414 469 511
TD10 = 814
Circuit symbol = 5_{2}.6.5_{2}.6.6_{2}.8_{2}
Weight = 21
Vertex symbol  = 5_{2}.6.5_{2}.6.6.16_{6}
Weight = 46

T3 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 16 32 56 69 87 127 170 212 252 270 325 408 476 524
TD10 = 784
Circuit symbol = 4.5.4.5.5_{2}.6_{2}
Weight = 12
Vertex symbol  = 4.5.4.5.5_{2}.*
Weight = 9

T4 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 23 35 50 74 104 141 172 198 239 301 352 414 469 511
TD10 = 814
Circuit symbol = 5_{2}.6.5_{2}.6.6_{2}.8_{2}
Weight = 21
Vertex symbol  = 5_{2}.6.5_{2}.6.6.16_{6}
Weight = 46

<TD10> = 799.000
Average ring size = 6.3866