Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_65_3_3839_zCdGlT.cif"

There are 40 T-atoms per unit cell
There are 80 O-atoms per unit cell

Framework density = 20.46 T-atoms per nm^3
Material density = 2.042 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6198 Angstrom
T1  -- O2  = 1.6196 Angstrom
T1  -- O3  = 1.6240 Angstrom
T1  -- O4  = 1.6217 Angstrom
      mean = 1.6213 Angstrom
        t1 = 0.007105  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001314  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6227 Angstrom
T2  -- O4  = 1.6219 Angstrom
T2  -- O5  = 1.6217 Angstrom
T2  -- O6  = 1.6235 Angstrom
      mean = 1.6225 Angstrom
        t1 = 0.007937  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001169  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6208 Angstrom
T3  -- O6  = 1.6208 Angstrom
T3  -- O7  = 1.6238 Angstrom
T3  -- O8  = 1.6109 Angstrom
      mean = 1.6191 Angstrom
        t1 = 0.006944  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003926  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6109 A <--> 1.6240 A
          Mean   = 1.6213 A
          StdDev = 0.0028 A

       t1 Range  = 0.0069 <-- 0.0073 --> 0.0079
       t2 Range  = 0.0012 <-- 0.0021 --> 0.0039

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.542 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.676 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.353 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.506 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.231 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.518 deg; O3  -- O4  = 3 A
       109.231 deg <-- 109.471 deg --> 109.676 deg

O3  -- T2  -- O4  = 109.169 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.595 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 108.988 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 109.766 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.478 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 109.827 deg; O5  -- O6  = 3 A
       108.988 deg <-- 109.470 deg --> 109.827 deg

O6  -- T3  -- O6  = 109.686 deg; O6  -- O6  = 3 A
O6  -- T3  -- O7  = 109.913 deg; O6  -- O7  = 3 A
O6  -- T3  -- O8  = 109.100 deg; O6  -- O8  = 3 A
O6  -- T3  -- O7  = 109.913 deg; O6  -- O7  = 3 A
O6  -- T3  -- O8  = 109.100 deg; O6  -- O8  = 3 A
O7  -- T3  -- O8  = 109.107 deg; O7  -- O8  = 3 A
       109.100 deg <-- 109.470 deg --> 109.913 deg

        O-T-O SUMMARY
          Range  = 108.9878 deg <--> 109.9134 deg
          Mean   = 109.4846 deg
          StdDev = 0.2913 deg

        O--O SUMMARY
          Range  = 2.6327 A <--> 2.6564 A
          Mean   = 2.6475 A
          StdDev = 0.0072 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  =  76.935 deg; T2  -- T2  = 3.7363 A
T2  - O1  - T1  - O3  - T1  = 112.275 deg; T2  -- T1  = 5.0015 A
T2  - O1  - T1  - O4  - T1  = 113.530 deg; T2  -- T1  = 5.0578 A
T2  - O2  - T1  - O3  - T1  = 149.886 deg; T2  -- T1  = 5.8535 A
T2  - O2  - T1  - O4  - T1  = 113.212 deg; T2  -- T1  = 5.0806 A
T1  - O3  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.3149 A

T1  - O3  - T2  - O4  - T1  =  84.915 deg; T1  -- T1  = 4.0545 A
T1  - O3  - T2  - O5  - T3  = 102.002 deg; T1  -- T3  = 4.6760 A
T1  - O3  - T2  - O6  - T2  = 146.598 deg; T1  -- T2  = 5.8103 A
T1  - O4  - T2  - O5  - T3  = 133.180 deg; T1  -- T3  = 5.5568 A
T1  - O4  - T2  - O6  - T2  = 108.087 deg; T1  -- T2  = 4.9416 A
T3  - O5  - T2  - O6  - T2  =  91.282 deg; T3  -- T2  = 4.3724 A

T2  - O6  - T3  - O6  - T2  = 135.591 deg; T2  -- T2  = 5.6160 A
T2  - O6  - T3  - O7  - T3  = 112.163 deg; T2  -- T3  = 5.0171 A
T2  - O6  - T3  - O8  - T3  =  88.718 deg; T2  -- T3  = 4.3724 A
T2  - O6  - T3  - O7  - T3  = 112.163 deg; T2  -- T3  = 5.0171 A
T2  - O6  - T3  - O8  - T3  =  88.718 deg; T2  -- T3  = 4.3724 A
T3  - O7  - T3  - O8  - T3  =  90.000 deg; T3  -- T3  = 4.4083 A

        T-T-T SUMMARY
          Range  = 76.9348 deg <--> 149.8862 deg
          Mean   = 110.0470 deg
          StdDev = 20.7132 deg

        T--T SUMMARY
          Range  = 3.7363 A <--> 5.8535 A
          Mean   = 4.9006 A
          StdDev = 0.5720 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 141.977 deg ; T1  -- T1   3.0629 A

T1  -- O2  -- T1  = 139.534 deg ; T1  -- T1   3.0393 A

T1  -- O3  -- T2  = 133.565 deg ; T1  -- T2   2.9838 A

T1  -- O4  -- T2  = 137.429 deg ; T1  -- T2   3.0223 A

T2  -- O5  -- T2  = 143.726 deg ; T2  -- T2   3.0823 A

T2  -- O6  -- T3  = 138.404 deg ; T2  -- T3   3.0329 A

T3  -- O7  -- T3  = 136.176 deg ; T3  -- T3   3.0129 A

T3  -- O8  -- T3  = 174.390 deg ; T3  -- T3   3.2180 A


        T-O-T SUMMARY
          Range  = 133.5647° <--> 174.3897 deg
          Mean   = 141.4168 deg
          StdDev = 9.7031 deg

        T--T SUMMARY
          Range  = 2.9838 A <--> 3.2180 A
          Mean   = 3.0484 A
          StdDev = 0.0557 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 22 37 53 80 113 141 178 225 267 313 370 433 501 564
TD10 = 864
Circuit symbol = 4.4.6.6_{2}.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.4.6.6_{2}.6_{2}.8
Weight = 18

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 20 36 57 79 106 142 181 220 266 319 374 429 490 566
TD10 = 856
Circuit symbol = 4.4.6.8_{3}.8_{3}.8_{6}
Weight = 30
Vertex symbol  = 4.4.6.8_{3}.8_{2}.8_{4}
Weight = 30

T3 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 33 55 83 110 137 175 222 269 317 370 433 499 554
TD10 = 847
Circuit symbol = 4.6.4.6_{2}.4.6_{2}
Weight = 14
Vertex symbol  = 4.6.4.6.4.8_{4}
Weight = 19

<TD10> = 857.400
Average ring size = 6.0619