Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_65_2_119_M5Tmv4.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 17.68 T-atoms per nm^3
Material density = 1.764 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6156 Angstrom
T1  -- O2  = 1.6175 Angstrom
T1  -- O3  = 1.6190 Angstrom
T1  -- O3  = 1.6190 Angstrom
      mean = 1.6178 Angstrom
        t1 = 0.006258  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002538  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6188 Angstrom
T2  -- O4  = 1.6189 Angstrom
T2  -- O5  = 1.6156 Angstrom
T2  -- O3  = 1.6188 Angstrom
      mean = 1.6180 Angstrom
        t1 = 0.005771  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002747  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6156 A <--> 1.6190 A
          Mean   = 1.6179 A
          StdDev = 0.0014 A

       t1 Range  = 0.0058 <-- 0.0060 --> 0.0063
       t2 Range  = 0.0025 <-- 0.0026 --> 0.0027

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.514 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.446 deg; O1  -- O3  = 3 A
O1  -- T1  -- O3  = 109.446 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 108.853 deg; O2  -- O3  = 3 A
O2  -- T1  -- O3  = 108.853 deg; O2  -- O3  = 3 A
O3  -- T1  -- O3  = 110.709 deg; O3  -- O3  = 3 A
       108.853 deg <-- 109.470 deg --> 110.709 deg

O3  -- T2  -- O4  = 109.725 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.035 deg; O3  -- O5  = 3 A
O3  -- T2  -- O3  = 110.091 deg; O3  -- O3  = 3 A
O4  -- T2  -- O5  = 109.208 deg; O4  -- O5  = 3 A
O4  -- T2  -- O3  = 109.725 deg; O4  -- O3  = 3 A
O5  -- T2  -- O3  = 109.035 deg; O5  -- O3  = 3 A
       109.035 deg <-- 109.470 deg --> 110.091 deg

        O-T-O SUMMARY
          Range  = 108.8525 deg <--> 110.7088 deg
          Mean   = 109.4856 deg
          StdDev = 0.5543 deg

        O--O SUMMARY
          Range  = 2.6324 A <--> 2.6639 A
          Mean   = 2.6424 A
          StdDev = 0.0098 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 111.205 deg; T1  -- T2  = 5.2000 A
T1  - O1  - T1  - O3  - T2  = 111.205 deg; T1  -- T2  = 5.2000 A
T1  - O1  - T1  - O3  - T1  =  97.394 deg; T1  -- T1  = 4.8036 A
T2  - O2  - T1  - O3  - T2  =  75.518 deg; T2  -- T2  = 3.7596 A
T2  - O2  - T1  - O3  - T1  = 130.587 deg; T2  -- T1  = 5.6622 A
T2  - O3  - T1  - O3  - T1  = 130.587 deg; T2  -- T1  = 5.6622 A

T1  - O3  - T2  - O4  - T1  =  81.174 deg; T1  -- T1  = 3.9945 A
T1  - O3  - T2  - O5  - T2  = 116.690 deg; T1  -- T2  = 5.2387 A
T1  - O3  - T2  - O3  - T2  = 127.759 deg; T1  -- T2  = 5.6569 A
T1  - O4  - T2  - O5  - T2  = 116.690 deg; T1  -- T2  = 5.2387 A
T1  - O4  - T2  - O3  - T2  = 127.759 deg; T1  -- T2  = 5.6569 A
T2  - O5  - T2  - O3  - T2  =  90.000 deg; T2  -- T2  = 4.4662 A

        T-T-T SUMMARY
          Range  = 75.5179 deg <--> 130.5872 deg
          Mean   = 109.1093 deg
          StdDev = 19.8357 deg

        T--T SUMMARY
          Range  = 3.7596 A <--> 5.6622 A
          Mean   = 5.0201 A
          StdDev = 0.6732 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2312 A

T1  -- O2  -- T1  = 155.760 deg ; T1  -- T1   3.1628 A

T1  -- O3  -- T2  = 142.930 deg ; T1  -- T2   3.0698 A

T2  -- O4  -- T2  = 144.599 deg ; T2  -- T2   3.0845 A

T2  -- O5  -- T2  = 176.984 deg ; T2  -- T2   3.2300 A


        T-O-T SUMMARY
          Range  = 142.9297° <--> 180.0000 deg
          Mean   = 160.0545 deg
          StdDev = 15.9164 deg

        T--T SUMMARY
          Range  = 3.0698 A <--> 3.2312 A
          Mean   = 3.1557 A
          StdDev = 0.0697 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 21 39 60 89 118 153 195 240 293 341 403 474 539 613
TD10 = 931
Circuit symbol = 4.5_{2}.5.8_{5}.5.8_{5}
Weight = 26
Vertex symbol  = 4.5_{2}.5.8_{3}.5.8_{3}
Weight = 26

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 23 41 60 87 121 154 192 240 292 348 407 465 536 617
TD10 = 933
Circuit symbol = 4.4.6_{2}.8_{4}.6_{2}.8_{4}
Weight = 28
Vertex symbol  = 4.4.6_{2}.8_{2}.6_{2}.8_{2}
Weight = 28

<TD10> = 932.000
Average ring size = 6.0577