Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_64_2_8290_ttUx1a.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 23.20 T-atoms per nm^3
Material density = 2.315 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6196 Angstrom
T1  -- O2  = 1.6161 Angstrom
T1  -- O3  = 1.6204 Angstrom
T1  -- O4  = 1.6210 Angstrom
      mean = 1.6193 Angstrom
        t1 = 0.005944  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001316  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6166 Angstrom
T2  -- O3  = 1.6211 Angstrom
T2  -- O5  = 1.6202 Angstrom
T2  -- O4  = 1.6216 Angstrom
      mean = 1.6199 Angstrom
        t1 = 0.006339  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001441  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6161 A <--> 1.6216 A
          Mean   = 1.6196 A
          StdDev = 0.0020 A

       t1 Range  = 0.0059 <-- 0.0061 --> 0.0063
       t2 Range  = 0.0013 <-- 0.0014 --> 0.0014

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.547 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.165 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.623 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.197 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.785 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.508 deg; O3  -- O4  = 3 A
       109.165 deg <-- 109.471 deg --> 109.785 deg

O2  -- T2  -- O3  = 109.898 deg; O2  -- O3  = 3 A
O2  -- T2  -- O5  = 109.348 deg; O2  -- O5  = 3 A
O2  -- T2  -- O4  = 109.175 deg; O2  -- O4  = 3 A
O3  -- T2  -- O5  = 109.417 deg; O3  -- O5  = 3 A
O3  -- T2  -- O4  = 109.550 deg; O3  -- O4  = 3 A
O5  -- T2  -- O4  = 109.439 deg; O5  -- O4  = 3 A
       109.175 deg <-- 109.471 deg --> 109.898 deg

        O-T-O SUMMARY
          Range  = 109.1655 deg <--> 109.8976 deg
          Mean   = 109.4709 deg
          StdDev = 0.2227 deg

        O--O SUMMARY
          Range  = 2.6381 A <--> 2.6505 A
          Mean   = 2.6448 A
          StdDev = 0.0041 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 101.547 deg; T1  -- T2  = 4.8155 A
T1  - O1  - T1  - O3  - T2  = 114.568 deg; T1  -- T2  = 5.1560 A
T1  - O1  - T1  - O4  - T2  = 119.357 deg; T1  -- T2  = 5.2942 A
T2  - O2  - T1  - O3  - T2  = 139.258 deg; T2  -- T2  = 5.7567 A
T2  - O2  - T1  - O4  - T2  =  96.950 deg; T2  -- T2  = 4.6014 A
T2  - O3  - T1  - O4  - T2  =  81.819 deg; T2  -- T2  = 3.9668 A

T1  - O2  - T2  - O3  - T2  = 109.046 deg; T1  -- T2  = 5.0211 A
T1  - O2  - T2  - O5  - T1  = 101.095 deg; T1  -- T1  = 4.7419 A
T1  - O2  - T2  - O4  - T1  = 135.868 deg; T1  -- T1  = 5.6956 A
T2  - O3  - T2  - O5  - T1  = 109.625 deg; T2  -- T1  = 4.9667 A
T2  - O3  - T2  - O4  - T1  = 109.591 deg; T2  -- T1  = 4.9698 A
T1  - O5  - T2  - O4  - T1  =  85.243 deg; T1  -- T1  = 4.1017 A

        T-T-T SUMMARY
          Range  = 81.8192 deg <--> 139.2576 deg
          Mean   = 108.6638 deg
          StdDev = 16.7306 deg

        T--T SUMMARY
          Range  = 3.9668 A <--> 5.7567 A
          Mean   = 4.9240 A
          StdDev = 0.5205 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 146.518 deg ; T1  -- T1   3.1018 A

T1  -- O2  -- T2  = 148.923 deg ; T1  -- T2   3.1145 A

T1  -- O3  -- T2  = 137.991 deg ; T1  -- T2   3.0262 A

T1  -- O4  -- T2  = 138.390 deg ; T1  -- T2   3.0312 A

T2  -- O5  -- T2  = 140.625 deg ; T2  -- T2   3.0510 A


        T-O-T SUMMARY
          Range  = 137.9913° <--> 148.9227 deg
          Mean   = 142.4894 deg
          StdDev = 4.4581 deg

        T--T SUMMARY
          Range  = 3.0262 A <--> 3.1145 A
          Mean   = 3.0649 A
          StdDev = 0.0367 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 23 40 62 90 123 160 201 249 299 356 420 487 557 634
TD10 = 964
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 21
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 21

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 23 42 63 90 123 160 201 249 300 358 420 485 557 636
TD10 = 967
Circuit symbol = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 23
Vertex symbol  = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 23

<TD10> = 965.500
Average ring size = 5.6842