Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_64_2_4961_Ym0m9a.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 17.92 T-atoms per nm^3
Material density = 1.788 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6164 Angstrom
T1  -- O2  = 1.6202 Angstrom
T1  -- O3  = 1.6145 Angstrom
T1  -- O4  = 1.6180 Angstrom
      mean = 1.6173 Angstrom
        t1 = 0.004816  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001494  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6180 Angstrom
T2  -- O5  = 1.6174 Angstrom
T2  -- O6  = 1.6158 Angstrom
T2  -- O7  = 1.6172 Angstrom
      mean = 1.6171 Angstrom
        t1 = 0.004842  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002064  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6145 A <--> 1.6202 A
          Mean   = 1.6172 A
          StdDev = 0.0016 A

       t1 Range  = 0.0048 <-- 0.0048 --> 0.0048
       t2 Range  = 0.0015 <-- 0.0018 --> 0.0021

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.231 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.375 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 110.018 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.532 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.276 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.395 deg; O3  -- O4  = 3 A
       109.231 deg <-- 109.471 deg --> 110.018 deg

O4  -- T2  -- O5  = 110.008 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.070 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 109.506 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 109.241 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.477 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.524 deg; O6  -- O7  = 3 A
       109.070 deg <-- 109.471 deg --> 110.008 deg

        O-T-O SUMMARY
          Range  = 109.0702 deg <--> 110.0177 deg
          Mean   = 109.4959 deg
          StdDev = 0.3084 deg

        O--O SUMMARY
          Range  = 2.6339 A <--> 2.6504 A
          Mean   = 2.6414 A
          StdDev = 0.0053 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  83.137 deg; T1  -- T2  = 4.1487 A
T1  - O1  - T1  - O3  - T1  = 109.979 deg; T1  -- T1  = 5.2448 A
T1  - O1  - T1  - O4  - T1  = 128.226 deg; T1  -- T1  = 5.6103 A
T2  - O2  - T1  - O3  - T1  = 110.585 deg; T2  -- T1  = 5.1848 A
T2  - O2  - T1  - O4  - T1  = 134.762 deg; T2  -- T1  = 5.6664 A
T1  - O3  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.4495 A

T1  - O4  - T2  - O5  - T2  =  83.102 deg; T1  -- T2  = 4.1487 A
T1  - O4  - T2  - O6  - T2  = 123.072 deg; T1  -- T2  = 5.5467 A
T1  - O4  - T2  - O7  - T2  = 110.585 deg; T1  -- T2  = 5.1893 A
T2  - O5  - T2  - O6  - T2  = 118.158 deg; T2  -- T2  = 5.4975 A
T2  - O5  - T2  - O7  - T2  = 109.862 deg; T2  -- T2  = 5.2472 A
T2  - O6  - T2  - O7  - T2  = 109.509 deg; T2  -- T2  = 5.2807 A

        T-T-T SUMMARY
          Range  = 83.1020 deg <--> 134.7624 deg
          Mean   = 110.0403 deg
          StdDev = 17.1687 deg

        T--T SUMMARY
          Range  = 4.1487 A <--> 5.6664 A
          Mean   = 5.1014 A
          StdDev = 0.5486 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 158.173 deg ; T1  -- T1   3.1744 A

T1  -- O2  -- T1  = 141.724 deg ; T1  -- T1   3.0614 A

T1  -- O3  -- T1  = 179.209 deg ; T1  -- T1   3.2290 A

T1  -- O4  -- T2  = 143.951 deg ; T1  -- T2   3.0772 A

T2  -- O5  -- T2  = 158.201 deg ; T2  -- T2   3.1765 A

T2  -- O6  -- T2  = 180.000 deg ; T2  -- T2   3.2317 A

T2  -- O7  -- T2  = 179.968 deg ; T2  -- T2   3.2343 A


        T-O-T SUMMARY
          Range  = 141.7245° <--> 180.0000 deg
          Mean   = 163.0323 deg
          StdDev = 15.6607 deg

        T--T SUMMARY
          Range  = 3.0614 A <--> 3.2343 A
          Mean   = 3.1692 A
          StdDev = 0.0678 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 37 57 82 112 145 184 228 275 328 385 446 512 583
TD10 = 881
Circuit symbol = 4.4.6_{2}.8_{6}.6_{3}.8_{5}
Weight = 27
Vertex symbol  = 4.4.6_{2}.8_{3}.6_{3}.8_{3}
Weight = 27

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 22 38 59 83 113 147 186 230 278 330 386 448 513 585
TD10 = 894
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{3}
Weight = 20
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{3}
Weight = 20

<TD10> = 887.500
Average ring size = 6.0000