Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_64_2_12188_wGHlzr.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 22.93 T-atoms per nm^3
Material density = 2.287 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6197 Angstrom
T1  -- O2  = 1.6232 Angstrom
T1  -- O3  = 1.6173 Angstrom
T1  -- O4  = 1.6220 Angstrom
      mean = 1.6205 Angstrom
        t1 = 0.007009  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002210  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6201 Angstrom
T2  -- O3  = 1.6201 Angstrom
T2  -- O4  = 1.6220 Angstrom
T2  -- O4  = 1.6220 Angstrom
      mean = 1.6211 Angstrom
        t1 = 0.007193  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001768  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6173 A <--> 1.6232 A
          Mean   = 1.6207 A
          StdDev = 0.0020 A

       t1 Range  = 0.0070 <-- 0.0071 --> 0.0072
       t2 Range  = 0.0018 <-- 0.0020 --> 0.0022

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.946 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.282 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.862 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.003 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.428 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.302 deg; O3  -- O4  = 3 A
       109.003 deg <-- 109.470 deg --> 109.946 deg

O3  -- T2  -- O3  = 109.239 deg; O3  -- O3  = 3 A
O3  -- T2  -- O4  = 109.174 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 109.625 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 109.625 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 109.174 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  = 109.988 deg; O4  -- O4  = 3 A
       109.174 deg <-- 109.471 deg --> 109.988 deg

        O-T-O SUMMARY
          Range  = 109.0026 deg <--> 109.9882 deg
          Mean   = 109.4500 deg
          StdDev = 0.3089 deg

        O--O SUMMARY
          Range  = 2.6381 A <--> 2.6572 A
          Mean   = 2.6464 A
          StdDev = 0.0060 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 100.965 deg; T1  -- T2  = 4.7815 A
T1  - O1  - T1  - O3  - T2  =  97.349 deg; T1  -- T2  = 4.6278 A
T1  - O1  - T1  - O4  - T1  = 134.939 deg; T1  -- T1  = 5.6372 A
T2  - O2  - T1  - O3  - T2  =  91.841 deg; T2  -- T2  = 4.3580 A
T2  - O2  - T1  - O4  - T1  = 108.602 deg; T2  -- T1  = 4.8790 A
T2  - O3  - T1  - O4  - T1  = 114.474 deg; T2  -- T1  = 5.0214 A

T1  - O3  - T2  - O3  - T1  = 142.796 deg; T1  -- T1  = 5.7839 A
T1  - O3  - T2  - O4  - T1  =  88.159 deg; T1  -- T1  = 4.2202 A
T1  - O3  - T2  - O4  - T1  = 107.244 deg; T1  -- T1  = 4.8842 A
T1  - O3  - T2  - O4  - T1  = 107.244 deg; T1  -- T1  = 4.8842 A
T1  - O3  - T2  - O4  - T1  =  88.159 deg; T1  -- T1  = 4.2202 A
T1  - O4  - T2  - O4  - T1  = 131.052 deg; T1  -- T1  = 5.4883 A

        T-T-T SUMMARY
          Range  = 88.1587 deg <--> 142.7956 deg
          Mean   = 109.7687 deg
          StdDev = 17.8932 deg

        T--T SUMMARY
          Range  = 4.2202 A <--> 5.7839 A
          Mean   = 4.9039 A
          StdDev = 0.5109 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 152.467 deg ; T1  -- T1   3.1464 A

T1  -- O2  -- T1  = 131.180 deg ; T1  -- T1   2.9562 A

T1  -- O3  -- T2  = 140.965 deg ; T1  -- T2   3.0514 A

T1  -- O4  -- T2  = 136.687 deg ; T1  -- T2   3.0150 A


        T-O-T SUMMARY
          Range  = 131.1803° <--> 152.4671 deg
          Mean   = 140.3246 deg
          StdDev = 7.8833 deg

        T--T SUMMARY
          Range  = 2.9562 A <--> 3.1464 A
          Mean   = 3.0422 A
          StdDev = 0.0696 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 24 42 65 93 125 163 207 255 308 366 429 498 572 650
TD10 = 990
Circuit symbol = 4.8_{8}.6.6.6.6
Weight = 27
Vertex symbol  = 4.8_{8}.6.6.6.6
Weight = 27

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 24 42 64 90 126 166 206 252 306 368 432 496 568 650
TD10 = 985
Circuit symbol = 4.4.6.6.6.6
Weight = 19
Vertex symbol  = 4.4.6.6.6.6
Weight = 19

<TD10> = 988.333
Average ring size = 6.4000