Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_63_4_40620256_Np7MFt.cif"

There are 40 T-atoms per unit cell
There are 80 O-atoms per unit cell

Framework density = 18.02 T-atoms per nm^3
Material density = 1.798 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6150 Angstrom
T1  -- O2  = 1.4765 Angstrom
T1  -- O3  = 1.6368 Angstrom
T1  -- O4  = 1.6374 Angstrom
      mean = 1.5914 Angstrom
        t1 = 0.032380  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.018187  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.5778 Angstrom
T2  -- O2  = 1.5778 Angstrom
T2  -- O5  = 1.6133 Angstrom
T2  -- O6  = 1.6193 Angstrom
      mean = 1.5970 Angstrom
        t1 = 0.055511  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037026  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O3  = 1.6331 Angstrom
T3  -- O3  = 1.6331 Angstrom
T3  -- O5  = 1.6159 Angstrom
T3  -- O7  = 1.6140 Angstrom
      mean = 1.6240 Angstrom
        t1 = 0.022457  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.013164  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O4  = 1.6342 Angstrom
T4  -- O4  = 1.6342 Angstrom
T4  -- O6  = 1.6218 Angstrom
T4  -- O8  = 1.6185 Angstrom
      mean = 1.6272 Angstrom
        t1 = 0.023872  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.013860  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4765 A <--> 1.6374 A
          Mean   = 1.6062 A
          StdDev = 0.0465 A

       t1 Range  = 0.0225 <-- 0.0336 --> 0.0555
       t2 Range  = 0.0132 <-- 0.0206 --> 0.0370

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 124.638 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 104.096 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 104.393 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.789 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.766 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 100.352 deg; O3  -- O4  = 3 A
       100.352 deg <-- 109.006 deg --> 124.638 deg

O2  -- T2  -- O2  =  92.592 deg; O2  -- O2  = 2 A
O2  -- T2  -- O5  = 112.398 deg; O2  -- O5  = 3 A
O2  -- T2  -- O6  = 112.646 deg; O2  -- O6  = 3 A
O2  -- T2  -- O5  = 112.398 deg; O2  -- O5  = 3 A
O2  -- T2  -- O6  = 112.646 deg; O2  -- O6  = 3 A
O5  -- T2  -- O6  = 112.665 deg; O5  -- O6  = 3 A
       92.592 deg <-- 109.224 deg --> 112.665 deg

O3  -- T3  -- O3  = 115.890 deg; O3  -- O3  = 3 A
O3  -- T3  -- O5  = 109.137 deg; O3  -- O5  = 3 A
O3  -- T3  -- O7  = 107.444 deg; O3  -- O7  = 3 A
O3  -- T3  -- O5  = 109.137 deg; O3  -- O5  = 3 A
O3  -- T3  -- O7  = 107.444 deg; O3  -- O7  = 3 A
O5  -- T3  -- O7  = 107.462 deg; O5  -- O7  = 3 A
       107.444 deg <-- 109.419 deg --> 115.890 deg

O4  -- T4  -- O4  = 116.605 deg; O4  -- O4  = 3 A
O4  -- T4  -- O6  = 108.571 deg; O4  -- O6  = 3 A
O4  -- T4  -- O8  = 107.404 deg; O4  -- O8  = 3 A
O4  -- T4  -- O6  = 108.571 deg; O4  -- O6  = 3 A
O4  -- T4  -- O8  = 107.404 deg; O4  -- O8  = 3 A
O6  -- T4  -- O8  = 107.993 deg; O6  -- O8  = 3 A
       107.404 deg <-- 109.424 deg --> 116.605 deg

        O-T-O SUMMARY
          Range  = 92.5918 deg <--> 124.6376 deg
          Mean   = 109.2613 deg
          StdDev = 6.0074 deg

        O--O SUMMARY
          Range  = 2.2812 A <--> 2.7809 A
          Mean   = 2.6210 A
          StdDev = 0.0972 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 129.311 deg; T2  -- T1  = 5.6710 A
T2  - O1  - T1  - O3  - T3  = 110.441 deg; T2  -- T3  = 5.0689 A
T2  - O1  - T1  - O4  - T4  = 111.732 deg; T2  -- T4  = 5.1375 A
T1  - O2  - T1  - O3  - T3  = 110.772 deg; T1  -- T3  = 5.2315 A
T1  - O2  - T1  - O4  - T4  = 109.853 deg; T1  -- T4  = 5.2309 A
T3  - O3  - T1  - O4  - T4  =  68.677 deg; T3  -- T4  = 3.5471 A

T1  - O2  - T2  - O2  - T1  = 101.349 deg; T1  -- T1  = 4.7105 A
T1  - O2  - T2  - O5  - T3  = 119.600 deg; T1  -- T3  = 5.2801 A
T1  - O2  - T2  - O6  - T4  = 122.151 deg; T1  -- T4  = 5.2842 A
T1  - O2  - T2  - O5  - T3  = 119.600 deg; T1  -- T3  = 5.2801 A
T1  - O2  - T2  - O6  - T4  = 122.151 deg; T1  -- T4  = 5.2842 A
T3  - O5  - T2  - O6  - T4  =  71.680 deg; T3  -- T4  = 3.5471 A

T1  - O3  - T3  - O3  - T1  =  97.757 deg; T1  -- T1  = 4.7105 A
T1  - O3  - T3  - O5  - T2  =  86.899 deg; T1  -- T2  = 4.2580 A
T1  - O3  - T3  - O7  - T3  = 123.630 deg; T1  -- T3  = 5.6001 A
T1  - O3  - T3  - O5  - T2  =  86.899 deg; T1  -- T2  = 4.2580 A
T1  - O3  - T3  - O7  - T3  = 123.630 deg; T1  -- T3  = 5.6001 A
T2  - O5  - T3  - O7  - T3  = 127.353 deg; T2  -- T3  = 5.6394 A

T1  - O4  - T4  - O4  - T1  =  96.312 deg; T1  -- T1  = 4.7105 A
T1  - O4  - T4  - O6  - T2  =  87.515 deg; T1  -- T2  = 4.2580 A
T1  - O4  - T4  - O8  - T4  = 125.043 deg; T1  -- T4  = 5.6598 A
T1  - O4  - T4  - O6  - T2  =  87.515 deg; T1  -- T2  = 4.2580 A
T1  - O4  - T4  - O8  - T4  = 125.043 deg; T1  -- T4  = 5.6598 A
T2  - O6  - T4  - O8  - T4  = 124.328 deg; T2  -- T4  = 5.4927 A

        T-T-T SUMMARY
          Range  = 68.6770 deg <--> 129.3105 deg
          Mean   = 107.8916 deg
          StdDev = 17.3652 deg

        T--T SUMMARY
          Range  = 3.5471 A <--> 5.6710 A
          Mean   = 4.9795 A
          StdDev = 0.6128 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 178.367 deg ; T1  -- T1   3.2297 A

T1  -- O2  -- T2  = 170.899 deg ; T1  -- T2   3.0447 A

T1  -- O3  -- T3  = 145.937 deg ; T1  -- T3   3.1265 A

T1  -- O4  -- T4  = 150.197 deg ; T1  -- T4   3.1616 A

T2  -- O5  -- T3  = 143.266 deg ; T2  -- T3   3.0646 A

T2  -- O6  -- T4  = 134.833 deg ; T2  -- T4   2.9925 A

T3  -- O7  -- T3  = 176.922 deg ; T3  -- T3   3.2267 A

T4  -- O8  -- T4  = 167.540 deg ; T4  -- T4   3.2178 A


        T-O-T SUMMARY
          Range  = 134.8329° <--> 178.3669 deg
          Mean   = 159.4468 deg
          StdDev = 15.2258 deg

        T--T SUMMARY
          Range  = 2.9925 A <--> 3.2297 A
          Mean   = 3.1356 A
          StdDev = 0.0802 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O2  -- O2  = 2.2812 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 38 57 80 112 144 178 224 273 320 373 436 504 570
TD10 = 869
Circuit symbol = 4_{2}.6_{2}.6.6_{2}.6.6_{2}
Weight = 16
Vertex symbol  = 4_{2}.6_{2}.6.6_{2}.6.6_{2}
Weight = 16

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 20 36 58 80 108 146 182 222 268 318 380 436 494 572
TD10 = 867
Circuit symbol = 4_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 17
Vertex symbol  = 4_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 17

T3 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 37 57 81 109 144 184 222 266 322 379 435 497 569
TD10 = 870
Circuit symbol = 4.8_{3}.4.8_{3}.4.8_{4}
Weight = 29
Vertex symbol  = 4.8_{3}.4.8_{3}.4.8_{4}
Weight = 29

T4 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 37 57 81 109 144 184 222 266 322 379 435 497 569
TD10 = 870
Circuit symbol = 4.8_{3}.4.8_{3}.4.8_{4}
Weight = 29
Vertex symbol  = 4.8_{3}.4.8_{3}.4.8_{4}
Weight = 29

<TD10> = 869.000
Average ring size = 5.8983