Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_63_4_38000552_ryd27R.cif"

There are 48 T-atoms per unit cell
There are 96 O-atoms per unit cell

Framework density = 21.76 T-atoms per nm^3
Material density = 2.171 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6147 Angstrom
T1  -- O2  = 1.6196 Angstrom
T1  -- O3  = 1.6193 Angstrom
T1  -- O4  = 1.6179 Angstrom
      mean = 1.6179 Angstrom
        t1 = 0.005235  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001437  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6218 Angstrom
T2  -- O6  = 1.6134 Angstrom
T2  -- O4  = 1.6191 Angstrom
T2  -- O7  = 1.6151 Angstrom
      mean = 1.6173 Angstrom
        t1 = 0.004821  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001076  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6201 Angstrom
T3  -- O6  = 1.6201 Angstrom
T3  -- O8  = 1.6219 Angstrom
T3  -- O9  = 1.6285 Angstrom
      mean = 1.6226 Angstrom
        t1 = 0.008844  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003320  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6189 Angstrom
T4  -- O7  = 1.6189 Angstrom
T4  -- O9  = 1.6248 Angstrom
T4  -- O10 = 1.6307 Angstrom
      mean = 1.6233 Angstrom
        t1 = 0.011836  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008626  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6134 A <--> 1.6307 A
          Mean   = 1.6194 A
          StdDev = 0.0042 A

       t1 Range  = 0.0048 <-- 0.0077 --> 0.0118
       t2 Range  = 0.0011 <-- 0.0036 --> 0.0086

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.239 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.763 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.115 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.661 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.481 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.566 deg; O3  -- O4  = 3 A
       109.115 deg <-- 109.471 deg --> 109.763 deg

O5  -- T2  -- O6  = 109.448 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 109.064 deg; O5  -- O4  = 3 A
O5  -- T2  -- O7  = 109.202 deg; O5  -- O7  = 3 A
O6  -- T2  -- O4  = 110.089 deg; O6  -- O4  = 3 A
O6  -- T2  -- O7  = 109.456 deg; O6  -- O7  = 3 A
O4  -- T2  -- O7  = 109.563 deg; O4  -- O7  = 3 A
       109.064 deg <-- 109.471 deg --> 110.089 deg

O6  -- T3  -- O6  = 108.846 deg; O6  -- O6  = 3 A
O6  -- T3  -- O8  = 109.100 deg; O6  -- O8  = 3 A
O6  -- T3  -- O9  = 109.927 deg; O6  -- O9  = 3 A
O6  -- T3  -- O8  = 109.100 deg; O6  -- O8  = 3 A
O6  -- T3  -- O9  = 109.927 deg; O6  -- O9  = 3 A
O8  -- T3  -- O9  = 109.915 deg; O8  -- O9  = 3 A
       108.846 deg <-- 109.469 deg --> 109.927 deg

O7  -- T4  -- O7  = 109.539 deg; O7  -- O7  = 3 A
O7  -- T4  -- O9  = 107.888 deg; O7  -- O9  = 3 A
O7  -- T4  -- O10 = 110.896 deg; O7  -- O10 = 3 A
O7  -- T4  -- O9  = 107.888 deg; O7  -- O9  = 3 A
O7  -- T4  -- O10 = 110.896 deg; O7  -- O10 = 3 A
O9  -- T4  -- O10 = 109.637 deg; O9  -- O10 = 3 A
       107.888 deg <-- 109.457 deg --> 110.896 deg

        O-T-O SUMMARY
          Range  = 107.8875 deg <--> 110.8962 deg
          Mean   = 109.4465 deg
          StdDev = 0.7201 deg

        O--O SUMMARY
          Range  = 2.6223 A <--> 2.6764 A
          Mean   = 2.6453 A
          StdDev = 0.0140 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 108.603 deg; T1  -- T2  = 4.9737 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.3006 A
T1  - O1  - T1  - O4  - T1  = 127.552 deg; T1  -- T1  = 5.6229 A
T2  - O2  - T1  - O3  - T1  = 111.812 deg; T2  -- T1  = 5.0306 A
T2  - O2  - T1  - O4  - T1  = 119.788 deg; T2  -- T1  = 5.4165 A
T1  - O3  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.3987 A

T3  - O5  - T2  - O6  - T2  = 113.482 deg; T3  -- T2  = 5.0068 A
T3  - O5  - T2  - O4  - T1  = 116.538 deg; T3  -- T1  = 5.1523 A
T3  - O5  - T2  - O7  - T4  = 110.006 deg; T3  -- T4  = 5.0344 A
T2  - O6  - T2  - O4  - T1  = 111.812 deg; T2  -- T1  = 5.0079 A
T2  - O6  - T2  - O7  - T4  = 110.782 deg; T2  -- T4  = 5.0495 A
T1  - O4  - T2  - O7  - T4  =  92.249 deg; T1  -- T4  = 4.4728 A

T2  - O6  - T3  - O6  - T2  = 113.541 deg; T2  -- T2  = 5.0173 A
T2  - O6  - T3  - O8  - T3  = 113.482 deg; T2  -- T3  = 4.9322 A
T2  - O6  - T3  - O9  - T4  = 101.024 deg; T2  -- T4  = 4.6140 A
T2  - O6  - T3  - O8  - T3  = 113.482 deg; T2  -- T3  = 4.9322 A
T2  - O6  - T3  - O9  - T4  = 101.024 deg; T2  -- T4  = 4.6140 A
T3  - O8  - T3  - O9  - T4  = 112.931 deg; T3  -- T4  = 4.9002 A

T2  - O7  - T4  - O7  - T2  = 105.780 deg; T2  -- T2  = 5.0173 A
T2  - O7  - T4  - O9  - T3  = 108.131 deg; T2  -- T3  = 4.9605 A
T2  - O7  - T4  - O10 - T4  = 110.782 deg; T2  -- T4  = 5.1051 A
T2  - O7  - T4  - O9  - T3  = 108.131 deg; T2  -- T3  = 4.9605 A
T2  - O7  - T4  - O10 - T4  = 110.782 deg; T2  -- T4  = 5.1051 A
T3  - O9  - T4  - O10 - T4  = 112.931 deg; T3  -- T4  = 5.0317 A

        T-T-T SUMMARY
          Range  = 90.0000 deg <--> 127.5520 deg
          Mean   = 109.1398 deg
          StdDev = 8.6311 deg

        T--T SUMMARY
          Range  = 4.3006 A <--> 5.6229 A
          Mean   = 4.9553 A
          StdDev = 0.2872 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 165.072 deg ; T1  -- T1   3.2020 A

T1  -- O2  -- T1  = 142.342 deg ; T1  -- T1   3.0658 A

T1  -- O3  -- T1  = 137.257 deg ; T1  -- T1   3.0160 A

T1  -- O4  -- T2  = 141.787 deg ; T1  -- T2   3.0587 A

T2  -- O5  -- T2  = 134.249 deg ; T2  -- T2   2.9885 A

T2  -- O6  -- T3  = 136.100 deg ; T2  -- T3   2.9990 A

T2  -- O7  -- T4  = 153.170 deg ; T2  -- T4   3.1457 A

T3  -- O8  -- T3  = 126.681 deg ; T3  -- T3   2.8989 A

T3  -- O9  -- T4  = 132.655 deg ; T3  -- T4   2.9795 A

T4  -- O10 -- T4  = 139.184 deg ; T4  -- T4   3.0567 A


        T-O-T SUMMARY
          Range  = 126.6810° <--> 165.0720 deg
          Mean   = 142.2631 deg
          StdDev = 10.5495 deg

        T--T SUMMARY
          Range  = 2.8989 A <--> 3.2020 A
          Mean   = 3.0521 A
          StdDev = 0.0800 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 22 41 66 96 130 171 217 265 322 386 449 520 604 689
TD10 = 1023
Circuit symbol = 4.5.4.7.6.6_{2}
Weight = 16
Vertex symbol  = 4.5.4.7.6_{2}.7
Weight = 20

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 12 25 43 66 98 135 172 216 270 327 385 452 528 603 682
TD10 = 1042
Circuit symbol = 5.6_{2}.6.6_{2}.6_{2}.7
Weight = 21
Vertex symbol  = 5.6_{2}.6.6_{2}.6_{2}.8
Weight = 26

T3 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 26 44 67 96 131 174 220 269 323 387 457 524 602 690
TD10 = 1044
Circuit symbol = 6.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 26
Vertex symbol  = 6.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 26

T4 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 24 44 69 96 131 174 220 267 323 387 453 528 608 688
TD10 = 1042
Circuit symbol = 5.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 26
Vertex symbol  = 5.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 26

<TD10> = 1036.000
Average ring size = 5.7931