Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_63_4_24148348_rv3iFz.cif"

There are 64 T-atoms per unit cell
There are 128 O-atoms per unit cell

Framework density = 25.18 T-atoms per nm^3
Material density = 2.512 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6600 Angstrom
T1  -- O2  = 1.5942 Angstrom
T1  -- O3  = 1.6014 Angstrom
T1  -- O4  = 1.7040 Angstrom
      mean = 1.6399 Angstrom
        t1 = 0.047484  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.028193  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.5950 Angstrom
T2  -- O5  = 1.6374 Angstrom
T2  -- O6  = 1.6217 Angstrom
T2  -- O7  = 1.5987 Angstrom
      mean = 1.6132 Angstrom
        t1 = 0.020631  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.012986  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6270 Angstrom
T3  -- O8  = 1.6346 Angstrom
T3  -- O9  = 1.4475 Angstrom
T3  -- O10 = 1.6585 Angstrom
      mean = 1.5919 Angstrom
        t1 = 0.091565  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.101485  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O9  = 1.6486 Angstrom
T4  -- O10 = 1.6906 Angstrom
T4  -- O11 = 1.6988 Angstrom
T4  -- O10 = 1.7186 Angstrom
T4  -- O7  = 1.6092 Angstrom
      mean = 1.6732 Angstrom

        T-O SUMMARY
          Range  = 1.4475 A <--> 1.7186 A
          Mean   = 1.6321 A
          StdDev = 0.0605 A

       t1 Range  = 0.0206 <-- 0.0399 --> 0.0916
       t2 Range  = 0.0130 <-- 0.0357 --> 0.1015

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 106.017 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.572 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 120.839 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 107.163 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 106.669 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 106.887 deg; O3  -- O4  = 3 A
       106.017 deg <-- 109.358 deg --> 120.839 deg

O3  -- T2  -- O5  = 108.840 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.853 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 107.299 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.224 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 115.259 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 106.268 deg; O6  -- O7  = 3 A
       106.268 deg <-- 109.457 deg --> 115.259 deg

O4  -- T3  -- O8  = 115.732 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  =  93.358 deg; O4  -- O9  = 2 A
O4  -- T3  -- O10 = 120.065 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 110.392 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 115.529 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 =  96.204 deg; O9  -- O10 = 2 A
       93.358 deg <-- 108.547 deg --> 120.065 deg

O9  -- T4  -- O10 =  87.830 deg; O9  -- O10 = 2 A
O9  -- T4  -- O11 = 128.981 deg; O9  -- O11 = 3 A
O9  -- T4  -- O10 = 106.000 deg; O9  -- O10 = 3 A
O9  -- T4  -- O7  =  86.799 deg; O9  -- O7  = 2 A
O10 -- T4  -- O11 =  96.359 deg; O10 -- O11 = 3 A
O10 -- T4  -- O10 =  99.478 deg; O10 -- O10 = 3 A
O10 -- T4  -- O7  = 174.596 deg; O10 -- O7  = 3 A
O11 -- T4  -- O10 = 123.098 deg; O11 -- O10 = 3 A
O11 -- T4  -- O7  =  87.499 deg; O11 -- O7  = 2 A
O10 -- T4  -- O7  =  81.450 deg; O10 -- O7  = 2 A
       81.450 deg <-- 107.209 deg --> 174.596 deg

        O-T-O SUMMARY
          Range  = 81.4502 deg <--> 174.5958 deg
          Mean   = 108.4682 deg
          StdDev = 17.3877 deg

        O--O SUMMARY
          Range  = 2.1727 A <--> 3.2962 A
          Mean   = 2.6244 A
          StdDev = 0.2576 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.3200 A

T1  -- O2  -- T1  = 158.714 deg ; T1  -- T1   3.1335 A

T1  -- O3  -- T2  = 125.328 deg ; T1  -- T2   2.8395 A

T1  -- O4  -- T3  = 132.037 deg ; T1  -- T3   3.0437 A

T2  -- O5  -- T2  = 113.901 deg ; T2  -- T2   2.7450 A

T2  -- O6  -- T2  = 114.917 deg ; T2  -- T2   2.7342 A

T2  -- O7  -- T4  = 166.978 deg ; T2  -- T4   3.1872 A

T3  -- O8  -- T3  = 133.175 deg ; T3  -- T3   3.0001 A

T3  -- O9  -- T4  =  87.217 deg ; T3  -- T4   2.1404 A

T3  -- O10 -- T4  = 142.811 deg ; T3  -- T4   3.2009 A
T3  -- O10 -- T4  =  79.441 deg ; T3  -- T4   2.1404 A
T4  -- O10 -- T4  =  73.591 deg ; T4  -- T4   2.0421 A

T4  -- O11 -- T4  = 141.216 deg ; T4  -- T4   3.2049 A


        T-O-T SUMMARY
          Range  = 73.5909° <--> 180.0000 deg
          Mean   = 126.8712 deg
          StdDev = 31.6329 deg

        T--T SUMMARY
          Range  = 2.0421 A <--> 3.3200 A
          Mean   = 2.8255 A
          StdDev = 0.4308 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O4  -- O9  = 2.2402 A
O7  -- O10 = 2.1727 A
O7  -- O9  = 2.2385 A
O7  -- O11 = 2.2884 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T2  = 2.8395 Angstrom
  T1  -- T3  = 3.0437 Angstrom
  T1  -- T4  = 3.4311 Angstrom
  T1  -- T1  = 3.1335 Angstrom
  T1  -- T1  = 3.3200 Angstrom
T2  -- T2  = 2.7450 Angstrom
T2  -- T2  = 2.7342 Angstrom
T3  -- T4  = 2.1404 Angstrom
T4  has 6 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T4  -- T1  = 3.4311 Angstrom
  T4  -- T3  = 2.1404 Angstrom
  T4  -- T4  = 3.2049 Angstrom
  T4  -- T3  = 3.2009 Angstrom
  T4  -- T4  = 2.0421 Angstrom
  T4  -- T2  = 3.1872 Angstrom