Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_63_4_13942773_bYSjT0.cif"

There are 64 T-atoms per unit cell
There are 128 O-atoms per unit cell

Framework density = 22.85 T-atoms per nm^3
Material density = 2.280 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6275 Angstrom
T1  -- O2  = 1.5996 Angstrom
T1  -- O3  = 1.6211 Angstrom
T1  -- O4  = 1.6216 Angstrom
      mean = 1.6174 Angstrom
        t1 = 0.011709  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.007476  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6187 Angstrom
T2  -- O5  = 1.6742 Angstrom
T2  -- O7  = 1.6141 Angstrom
T2  -- O6  = 1.6791 Angstrom
      mean = 1.6465 Angstrom
        t1 = 0.040992  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.029336  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O8  = 1.6138 Angstrom
T3  -- O9  = 1.5268 Angstrom
T3  -- O6  = 1.6582 Angstrom
T3  -- O10 = 1.7023 Angstrom
T3  -- O6  = 2.0056 Angstrom
T3  -- O10 = 1.9481 Angstrom
      mean = 1.7425 Angstrom

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O11 = 1.6176 Angstrom
T4  -- O12 = 1.6563 Angstrom
T4  -- O7  = 1.6073 Angstrom
T4  -- O10 = 1.6455 Angstrom
      mean = 1.6317 Angstrom
        t1 = 0.029711  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.025046  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5268 A <--> 2.0056 A
          Mean   = 1.6687 A
          StdDev = 0.1156 A

       t1 Range  = 0.0117 <-- 0.0206 --> 0.0410
       t2 Range  = 0.0075 <-- 0.0155 --> 0.0293

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.376 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.569 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 112.141 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.971 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 108.521 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.205 deg; O3  -- O4  = 3 A
       108.376 deg <-- 109.464 deg --> 112.141 deg

O4  -- T2  -- O5  = 106.807 deg; O4  -- O5  = 3 A
O4  -- T2  -- O7  = 107.170 deg; O4  -- O7  = 3 A
O4  -- T2  -- O6  = 108.810 deg; O4  -- O6  = 3 A
O5  -- T2  -- O7  = 108.975 deg; O5  -- O7  = 3 A
O5  -- T2  -- O6  = 118.472 deg; O5  -- O6  = 3 A
O7  -- T2  -- O6  = 106.128 deg; O7  -- O6  = 3 A
       106.128 deg <-- 109.394 deg --> 118.472 deg

O8  -- T3  -- O9  = 110.853 deg; O8  -- O9  = 3 A
O8  -- T3  -- O6  =  66.693 deg; O8  -- O6  = 2 A
O8  -- T3  -- O10 = 125.373 deg; O8  -- O10 = 3 A
O8  -- T3  -- O6  =  58.418 deg; O8  -- O6  = 2 A
O8  -- T3  -- O10 = 111.293 deg; O8  -- O10 = 3 A
O9  -- T3  -- O6  = 105.495 deg; O9  -- O6  = 3 A
O9  -- T3  -- O10 = 109.504 deg; O9  -- O10 = 3 A
O9  -- T3  -- O6  = 112.101 deg; O9  -- O6  = 3 A
O9  -- T3  -- O10 = 112.260 deg; O9  -- O10 = 3 A
O6  -- T3  -- O10 =  68.179 deg; O6  -- O10 = 2 A
O6  -- T3  -- O6  = 121.122 deg; O6  -- O6  = 3 A
O6  -- T3  -- O10 = 139.248 deg; O6  -- O10 = 3 A
O10 -- T3  -- O6  = 131.439 deg; O10 -- O6  = 3 A
O10 -- T3  -- O10 =  84.894 deg; O10 -- O10 = 2 A
O6  -- T3  -- O10 =  56.890 deg; O6  -- O10 = 2 A
       56.890 deg <-- 100.917 deg --> 139.248 deg

O11 -- T4  -- O12 = 111.451 deg; O11 -- O12 = 3 A
O11 -- T4  -- O7  = 106.508 deg; O11 -- O7  = 3 A
O11 -- T4  -- O10 = 105.046 deg; O11 -- O10 = 3 A
O12 -- T4  -- O7  = 111.198 deg; O12 -- O7  = 3 A
O12 -- T4  -- O10 = 114.757 deg; O12 -- O10 = 3 A
O7  -- T4  -- O10 = 107.362 deg; O7  -- O10 = 3 A
       105.046 deg <-- 109.387 deg --> 114.757 deg

        O-T-O SUMMARY
          Range  = 56.8900 deg <--> 139.2478 deg
          Mean   = 105.2006 deg
          StdDev = 18.9468 deg

        O--O SUMMARY
          Range  = 1.7990 A <--> 3.3822 A
          Mean   = 2.6438 A
          StdDev = 0.3824 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 139.187 deg ; T1  -- T1   3.0507 A

T1  -- O2  -- T1  = 173.835 deg ; T1  -- T1   3.1945 A

T1  -- O3  -- T1  = 145.608 deg ; T1  -- T1   3.0972 A

T1  -- O4  -- T2  = 156.626 deg ; T1  -- T2   3.1731 A

T2  -- O5  -- T2  = 166.539 deg ; T2  -- T2   3.3253 A

T2  -- O6  -- T3  = 144.883 deg ; T2  -- T3   3.1818 A
T3  -- O6  -- T3  =  39.061 deg ; T3  -- T3   1.2678 A
T2  -- O6  -- T3  = 108.310 deg ; T2  -- T3   2.9929 A

T2  -- O7  -- T4  = 157.325 deg ; T2  -- T4   3.1586 A

T3  -- O8  -- T3  =  46.258 deg ; T3  -- T3   1.2678 A

T3  -- O9  -- T3  = 154.360 deg ; T3  -- T3   2.9775 A

T3  -- O10 -- T3  =  39.936 deg ; T3  -- T3   1.2678 A
T3  -- O10 -- T4  = 136.825 deg ; T3  -- T4   3.1130 A
T3  -- O10 -- T4  = 108.026 deg ; T3  -- T4   2.9132 A

T4  -- O11 -- T4  = 115.909 deg ; T4  -- T4   2.7423 A

T4  -- O12 -- T4  = 168.366 deg ; T4  -- T4   3.2956 A


        T-O-T SUMMARY
          Range  = 39.0612° <--> 173.8350 deg
          Mean   = 125.0659 deg
          StdDev = 44.4787 deg

        T--T SUMMARY
          Range  = 1.2678 A <--> 3.3253 A
          Mean   = 2.7512 A
          StdDev = 0.7273 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O6  -- O10 = 1.8839 A
O6  -- O8  = 1.7990 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T2  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T2  = 3.3253 Angstrom
  T2  -- T3  = 2.9929 Angstrom
  T2  -- T1  = 3.1731 Angstrom
  T2  -- T3  = 3.1818 Angstrom
  T2  -- T4  = 3.1586 Angstrom
T3  has 6 oxygen-bridged T-atoms within 3.50 A
  T3  -- T2  = 2.9929 Angstrom
  T3  -- T3  = 2.9775 Angstrom
  T3  -- T4  = 2.9132 Angstrom
  T3  -- T2  = 3.1818 Angstrom
  T3  -- T4  = 3.1130 Angstrom
  T3  -- T3  = 1.2678 Angstrom
T4  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T3  = 2.9132 Angstrom
  T4  -- T4  = 3.2956 Angstrom
  T4  -- T4  = 2.7423 Angstrom
  T4  -- T2  = 3.1586 Angstrom
  T4  -- T3  = 3.1130 Angstrom