Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_63_3_95296_kxZXwm.cif"

There are 48 T-atoms per unit cell
There are 96 O-atoms per unit cell

Framework density = 20.79 T-atoms per nm^3
Material density = 2.074 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6180 Angstrom
T1  -- O2  = 1.6221 Angstrom
T1  -- O3  = 1.6181 Angstrom
T1  -- O4  = 1.6225 Angstrom
      mean = 1.6202 Angstrom
        t1 = 0.006865  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003704  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6170 Angstrom
T2  -- O5  = 1.6195 Angstrom
T2  -- O6  = 1.6223 Angstrom
T2  -- O7  = 1.6200 Angstrom
      mean = 1.6197 Angstrom
        t1 = 0.006173  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001316  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6234 Angstrom
T3  -- O6  = 1.6228 Angstrom
T3  -- O7  = 1.6214 Angstrom
T3  -- O8  = 1.6189 Angstrom
      mean = 1.6216 Angstrom
        t1 = 0.007362  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000889  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6170 A <--> 1.6234 A
          Mean   = 1.6205 A
          StdDev = 0.0021 A

       t1 Range  = 0.0062 <-- 0.0068 --> 0.0074
       t2 Range  = 0.0009 <-- 0.0020 --> 0.0037

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.561 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.843 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.913 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.784 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.521 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.203 deg; O3  -- O4  = 3 A
       108.843 deg <-- 109.471 deg --> 109.913 deg

O3  -- T2  -- O5  = 109.731 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.727 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 109.161 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.277 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.439 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.492 deg; O6  -- O7  = 3 A
       109.161 deg <-- 109.471 deg --> 109.731 deg

O4  -- T3  -- O6  = 109.605 deg; O4  -- O6  = 3 A
O4  -- T3  -- O7  = 109.423 deg; O4  -- O7  = 3 A
O4  -- T3  -- O8  = 109.141 deg; O4  -- O8  = 3 A
O6  -- T3  -- O7  = 109.375 deg; O6  -- O7  = 3 A
O6  -- T3  -- O8  = 109.797 deg; O6  -- O8  = 3 A
O7  -- T3  -- O8  = 109.487 deg; O7  -- O8  = 3 A
       109.141 deg <-- 109.471 deg --> 109.797 deg

        O-T-O SUMMARY
          Range  = 108.8434 deg <--> 109.9133 deg
          Mean   = 109.4686 deg
          StdDev = 0.2708 deg

        O--O SUMMARY
          Range  = 2.6319 A <--> 2.6530 A
          Mean   = 2.6462 A
          StdDev = 0.0054 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 123.870 deg; T1  -- T2  = 5.4769 A
T1  - O1  - T1  - O3  - T3  = 116.153 deg; T1  -- T3  = 5.2263 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.3567 A
T2  - O2  - T1  - O3  - T3  = 101.119 deg; T2  -- T3  = 4.6763 A
T2  - O2  - T1  - O4  - T1  = 113.043 deg; T2  -- T1  = 5.0526 A
T3  - O3  - T1  - O4  - T1  = 113.026 deg; T3  -- T1  = 5.0107 A

T1  - O3  - T2  - O5  - T2  = 113.043 deg; T1  -- T2  = 5.1108 A
T1  - O3  - T2  - O6  - T3  = 116.827 deg; T1  -- T3  = 5.1488 A
T1  - O3  - T2  - O7  - T3  = 124.498 deg; T1  -- T3  = 5.3832 A
T2  - O5  - T2  - O6  - T3  = 112.390 deg; T2  -- T3  = 5.0414 A
T2  - O5  - T2  - O7  - T3  =  90.383 deg; T2  -- T3  = 4.3318 A
T3  - O6  - T2  - O7  - T3  =  96.253 deg; T3  -- T3  = 4.4845 A

T2  - O4  - T3  - O6  - T3  = 112.390 deg; T2  -- T3  = 5.0753 A
T2  - O4  - T3  - O7  - T1  = 130.289 deg; T2  -- T1  = 5.4393 A
T2  - O4  - T3  - O8  - T2  =  83.747 deg; T2  -- T2  = 4.0200 A
T3  - O6  - T3  - O7  - T1  = 113.026 deg; T3  -- T1  = 5.1030 A
T3  - O6  - T3  - O8  - T2  =  89.617 deg; T3  -- T2  = 4.3318 A
T1  - O7  - T3  - O8  - T2  = 115.489 deg; T1  -- T2  = 5.1022 A

        T-T-T SUMMARY
          Range  = 83.7473 deg <--> 130.2892 deg
          Mean   = 108.1844 deg
          StdDev = 13.0739 deg

        T--T SUMMARY
          Range  = 4.0200 A <--> 5.4769 A
          Mean   = 4.8933 A
          StdDev = 0.4154 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 154.188 deg ; T1  -- T1   3.1542 A

T1  -- O2  -- T1  = 135.738 deg ; T1  -- T1   3.0053 A

T1  -- O3  -- T2  = 141.301 deg ; T1  -- T2   3.0523 A

T1  -- O4  -- T3  = 135.361 deg ; T1  -- T3   3.0027 A

T2  -- O5  -- T2  = 143.394 deg ; T2  -- T2   3.0750 A

T2  -- O6  -- T3  = 134.423 deg ; T2  -- T3   2.9919 A

T2  -- O7  -- T3  = 138.441 deg ; T2  -- T3   3.0306 A

T3  -- O8  -- T3  = 148.413 deg ; T3  -- T3   3.1155 A


        T-O-T SUMMARY
          Range  = 134.4228° <--> 154.1881 deg
          Mean   = 141.4073 deg
          StdDev = 6.5704 deg

        T--T SUMMARY
          Range  = 2.9919 A <--> 3.1542 A
          Mean   = 3.0534 A
          StdDev = 0.0546 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 24 39 56 82 116 153 190 229 278 334 390 451 520 593
TD10 = 905
Circuit symbol = 4.6_{2}.6.8_{4}.6.8_{4}
Weight = 29
Vertex symbol  = 4.6_{2}.6.8_{3}.6.8_{3}
Weight = 29

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 38 61 87 113 145 187 233 281 333 390 453 519 588
TD10 = 900
Circuit symbol = 4.6.4.6.6.6_{2}
Weight = 18
Vertex symbol  = 4.6.4.6.6.6
Weight = 18

T3 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 38 61 87 113 145 187 233 281 333 390 453 519 588
TD10 = 900
Circuit symbol = 4.6.4.6.6.6_{2}
Weight = 18
Vertex symbol  = 4.6.4.6.6.6
Weight = 18

<TD10> = 901.667
Average ring size = 5.7500