Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_63_3_84908_iCg_to.cif"

There are 48 T-atoms per unit cell
There are 96 O-atoms per unit cell

Framework density = 22.26 T-atoms per nm^3
Material density = 2.221 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6182 Angstrom
T1  -- O2  = 1.6198 Angstrom
T1  -- O3  = 1.6160 Angstrom
T1  -- O4  = 1.6214 Angstrom
      mean = 1.6189 Angstrom
        t1 = 0.006818  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002831  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6238 Angstrom
T2  -- O5  = 1.6221 Angstrom
T2  -- O6  = 1.6242 Angstrom
T2  -- O6  = 1.6285 Angstrom
      mean = 1.6247 Angstrom
        t1 = 0.009991  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004091  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6192 Angstrom
T3  -- O7  = 1.6246 Angstrom
T3  -- O8  = 1.6167 Angstrom
T3  -- O3  = 1.6190 Angstrom
      mean = 1.6199 Angstrom
        t1 = 0.006985  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002353  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6160 A <--> 1.6285 A
          Mean   = 1.6211 A
          StdDev = 0.0035 A

       t1 Range  = 0.0068 <-- 0.0079 --> 0.0100
       t2 Range  = 0.0024 <-- 0.0031 --> 0.0041

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.073 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.328 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.516 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.620 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.268 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.012 deg; O3  -- O4  = 3 A
       108.620 deg <-- 109.469 deg --> 110.268 deg

O2  -- T2  -- O5  = 109.333 deg; O2  -- O5  = 3 A
O2  -- T2  -- O6  = 108.728 deg; O2  -- O6  = 3 A
O2  -- T2  -- O6  = 110.537 deg; O2  -- O6  = 3 A
O5  -- T2  -- O6  = 109.193 deg; O5  -- O6  = 3 A
O5  -- T2  -- O6  = 109.244 deg; O5  -- O6  = 3 A
O6  -- T2  -- O6  = 109.784 deg; O6  -- O6  = 3 A
       108.728 deg <-- 109.470 deg --> 110.537 deg

O4  -- T3  -- O7  = 109.271 deg; O4  -- O7  = 3 A
O4  -- T3  -- O8  = 109.932 deg; O4  -- O8  = 3 A
O4  -- T3  -- O3  = 108.989 deg; O4  -- O3  = 3 A
O7  -- T3  -- O8  = 109.497 deg; O7  -- O8  = 3 A
O7  -- T3  -- O3  = 110.190 deg; O7  -- O3  = 3 A
O8  -- T3  -- O3  = 108.950 deg; O8  -- O3  = 3 A
       108.950 deg <-- 109.471 deg --> 110.190 deg

        O-T-O SUMMARY
          Range  = 108.6201 deg <--> 110.5373 deg
          Mean   = 109.4694 deg
          StdDev = 0.5441 deg

        O--O SUMMARY
          Range  = 2.6281 A <--> 2.6729 A
          Mean   = 2.6473 A
          StdDev = 0.0112 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T3  =  93.550 deg; T2  -- T3  = 4.4227 A
T2  - O1  - T1  - O3  - T1  = 116.450 deg; T2  -- T1  = 5.2634 A
T2  - O1  - T1  - O4  - T3  = 105.929 deg; T2  -- T3  = 4.8594 A
T3  - O2  - T1  - O3  - T1  = 131.469 deg; T3  -- T1  = 5.6302 A
T3  - O2  - T1  - O4  - T3  = 108.475 deg; T3  -- T3  = 4.9273 A
T1  - O3  - T1  - O4  - T3  =  99.189 deg; T1  -- T3  = 4.7167 A

T1  - O2  - T2  - O5  - T2  = 115.188 deg; T1  -- T2  = 5.1143 A
T1  - O2  - T2  - O6  - T2  = 127.865 deg; T1  -- T2  = 5.4136 A
T1  - O2  - T2  - O6  - T2  = 113.363 deg; T1  -- T2  = 5.0361 A
T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.2422 A
T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.2422 A
T2  - O6  - T2  - O6  - T2  = 111.298 deg; T2  -- T2  = 4.9273 A

T1  - O4  - T3  - O7  - T3  = 115.537 deg; T1  -- T3  = 5.0963 A
T1  - O4  - T3  - O8  - T3  = 113.081 deg; T1  -- T3  = 5.2127 A
T1  - O4  - T3  - O3  - T1  = 108.475 deg; T1  -- T1  = 4.9273 A
T3  - O7  - T3  - O8  - T3  =  90.000 deg; T3  -- T3  = 4.3739 A
T3  - O7  - T3  - O3  - T1  = 115.699 deg; T3  -- T1  = 5.0856 A
T3  - O8  - T3  - O3  - T1  = 113.226 deg; T3  -- T1  = 5.2023 A

        T-T-T SUMMARY
          Range  = 90.0000 deg <--> 131.4686 deg
          Mean   = 109.3597 deg
          StdDev = 11.5995 deg

        T--T SUMMARY
          Range  = 4.2422 A <--> 5.6302 A
          Mean   = 4.9432 A
          StdDev = 0.3780 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 153.236 deg ; T1  -- T1   3.1485 A

T1  -- O2  -- T2  = 139.427 deg ; T1  -- T2   3.0425 A

T1  -- O3  -- T3  = 138.700 deg ; T1  -- T3   3.0272 A

T1  -- O4  -- T3  = 139.990 deg ; T1  -- T3   3.0451 A

T2  -- O5  -- T2  = 136.684 deg ; T2  -- T2   3.0152 A

T2  -- O6  -- T2  = 133.103 deg ; T2  -- T2   2.9841 A

T3  -- O7  -- T3  = 132.972 deg ; T3  -- T3   2.9794 A

T3  -- O8  -- T3  = 164.064 deg ; T3  -- T3   3.2022 A


        T-O-T SUMMARY
          Range  = 132.9721° <--> 164.0640 deg
          Mean   = 142.2720 deg
          StdDev = 10.1821 deg

        T--T SUMMARY
          Range  = 2.9794 A <--> 3.2022 A
          Mean   = 3.0555 A
          StdDev = 0.0743 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 12 25 40 63 95 129 161 198 255 316 365 419 491 577 652
TD10 = 983
Circuit symbol = 6.6_{2}.6.6_{2}.6_{2}.8_{4}
Weight = 29
Vertex symbol  = 6.6_{2}.6.6_{2}.6_{2}.8_{2}
Weight = 29

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 38 61 87 118 160 206 249 296 358 430 495 559 638
TD10 = 955
Circuit symbol = 4.6.4.6.6_{2}.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6_{2}
Weight = 19

T3 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 24 43 66 90 121 165 212 253 298 363 437 498 560 643
TD10 = 990
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

<TD10> = 976.000
Average ring size = 5.7778