Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_62_3_1839985_UX9uKG.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 22.22 T-atoms per nm^3
Material density = 2.217 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.5996 Angstrom
T1  -- O1  = 1.6434 Angstrom
T1  -- O1  = 1.6524 Angstrom
T1  -- O3  = 1.6561 Angstrom
      mean = 1.6379 Angstrom
        t1 = 0.033940  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.018797  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.5881 Angstrom
T2  -- O5  = 1.6037 Angstrom
T2  -- O4  = 1.6211 Angstrom
T2  -- O6  = 1.6114 Angstrom
      mean = 1.6061 Angstrom
        t1 = 0.010587  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006904  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O5  = 1.6063 Angstrom
T3  -- O6  = 1.6098 Angstrom
T3  -- O7  = 1.5719 Angstrom
T3  -- O3  = 1.6348 Angstrom
      mean = 1.6057 Angstrom
        t1 = 0.044052  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.031737  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5719 A <--> 1.6561 A
          Mean   = 1.6166 A
          StdDev = 0.0249 A

       t1 Range  = 0.0106 <-- 0.0295 --> 0.0441
       t2 Range  = 0.0069 <-- 0.0191 --> 0.0317

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O1  = 107.686 deg; O2  -- O1  = 3 A
O2  -- T1  -- O1  = 109.547 deg; O2  -- O1  = 3 A
O2  -- T1  -- O3  = 103.537 deg; O2  -- O3  = 3 A
O1  -- T1  -- O1  = 108.103 deg; O1  -- O1  = 3 A
O1  -- T1  -- O3  = 115.886 deg; O1  -- O3  = 3 A
O1  -- T1  -- O3  = 111.823 deg; O1  -- O3  = 3 A
       103.537 deg <-- 109.430 deg --> 115.886 deg

O2  -- T2  -- O5  = 108.494 deg; O2  -- O5  = 3 A
O2  -- T2  -- O4  = 110.188 deg; O2  -- O4  = 3 A
O2  -- T2  -- O6  = 107.655 deg; O2  -- O6  = 3 A
O5  -- T2  -- O4  = 110.343 deg; O5  -- O4  = 3 A
O5  -- T2  -- O6  = 109.665 deg; O5  -- O6  = 3 A
O4  -- T2  -- O6  = 110.432 deg; O4  -- O6  = 3 A
       107.655 deg <-- 109.463 deg --> 110.432 deg

O5  -- T3  -- O6  = 113.192 deg; O5  -- O6  = 3 A
O5  -- T3  -- O7  = 114.761 deg; O5  -- O7  = 3 A
O5  -- T3  -- O3  = 111.153 deg; O5  -- O3  = 3 A
O6  -- T3  -- O7  = 112.529 deg; O6  -- O7  = 3 A
O6  -- T3  -- O3  = 108.906 deg; O6  -- O3  = 3 A
O7  -- T3  -- O3  =  94.732 deg; O7  -- O3  = 2 A
       94.732 deg <-- 109.212 deg --> 114.761 deg

        O-T-O SUMMARY
          Range  = 94.7322 deg <--> 115.8863 deg
          Mean   = 109.3686 deg
          StdDev = 4.5178 deg

        O--O SUMMARY
          Range  = 2.3595 A <--> 2.7964 A
          Mean   = 2.6363 A
          StdDev = 0.0859 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O2  - T1  - O1  - T1  =  90.926 deg; T2  -- T1  = 4.3460 A
T2  - O2  - T1  - O1  - T1  = 108.035 deg; T2  -- T1  = 4.9330 A
T2  - O2  - T1  - O3  - T3  = 135.030 deg; T2  -- T3  = 5.6364 A
T1  - O1  - T1  - O1  - T1  = 103.549 deg; T1  -- T1  = 4.9098 A
T1  - O1  - T1  - O3  - T3  = 116.385 deg; T1  -- T3  = 5.3152 A
T1  - O1  - T1  - O3  - T3  =  99.720 deg; T1  -- T3  = 4.7814 A

T1  - O2  - T2  - O5  - T2  = 124.529 deg; T1  -- T2  = 5.2903 A
T1  - O2  - T2  - O4  - T3  = 106.783 deg; T1  -- T3  = 4.7839 A
T1  - O2  - T2  - O6  - T3  =  88.973 deg; T1  -- T3  = 4.1834 A
T2  - O5  - T2  - O4  - T3  = 112.022 deg; T2  -- T3  = 4.9715 A
T2  - O5  - T2  - O6  - T3  = 111.941 deg; T2  -- T3  = 4.9777 A
T3  - O4  - T2  - O6  - T3  = 110.134 deg; T3  -- T3  = 4.9098 A

T2  - O5  - T3  - O6  - T1  = 110.117 deg; T2  -- T1  = 5.0164 A
T2  - O5  - T3  - O7  - T3  =  93.754 deg; T2  -- T3  = 4.4777 A
T2  - O5  - T3  - O3  - T2  = 110.134 deg; T2  -- T2  = 4.9098 A
T1  - O6  - T3  - O7  - T3  =  76.719 deg; T1  -- T3  = 3.8932 A
T1  - O6  - T3  - O3  - T2  = 129.037 deg; T1  -- T2  = 5.5332 A
T3  - O7  - T3  - O3  - T2  = 129.534 deg; T3  -- T2  = 5.5575 A

        T-T-T SUMMARY
          Range  = 76.7185 deg <--> 135.0304 deg
          Mean   = 108.7402 deg
          StdDev = 14.8479 deg

        T--T SUMMARY
          Range  = 3.8932 A <--> 5.6364 A
          Mean   = 4.9126 A
          StdDev = 0.4589 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 142.944 deg ; T1  -- T1   3.1250 A

T1  -- O2  -- T2  = 137.428 deg ; T1  -- T2   2.9702 A

T1  -- O3  -- T3  = 143.971 deg ; T1  -- T3   3.1296 A

T2  -- O4  -- T2  = 136.050 deg ; T2  -- T2   3.0067 A

T2  -- O5  -- T3  = 137.248 deg ; T2  -- T3   2.9892 A

T2  -- O6  -- T3  = 137.242 deg ; T2  -- T3   2.9996 A

T3  -- O7  -- T3  = 180.000 deg ; T3  -- T3   3.1437 A


        T-O-T SUMMARY
          Range  = 136.0499° <--> 180.0000 deg
          Mean   = 144.9835 deg
          StdDev = 14.7117 deg

        T--T SUMMARY
          Range  = 2.9702 A <--> 3.1437 A
          Mean   = 3.0520 A
          StdDev = 0.0715 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 23 41 70 97 125 174 224 264 318 397 462 513 594 703
TD10 = 1035
Circuit symbol = 5.5.5.5.6_{2}.8_{6}
Weight = 26
Vertex symbol  = 5.5.5.5.6.8_{2}
Weight = 20

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 26 43 64 101 138 165 215 284 328 372 453 546 611 665
TD10 = 1053
Circuit symbol = 5.6.5.6.6_{2}.8_{4}
Weight = 28
Vertex symbol  = 5.6.5.6.6_{2}.8_{2}
Weight = 26

T3 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 23 43 72 95 128 177 225 259 322 401 460 513 597 708
TD10 = 1039
Circuit symbol = 5.6.5.6.5_{2}.6_{2}
Weight = 19
Vertex symbol  = 5.6.5.6.5_{2}.6
Weight = 19

<TD10> = 1042.333
Average ring size = 5.7391