Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_62_3_1532529_7J_tE5.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 28.36 T-atoms per nm^3
Material density = 2.829 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6374 Angstrom
T1  -- O1  = 1.6324 Angstrom
T1  -- O3  = 1.6491 Angstrom
T1  -- O2  = 1.6306 Angstrom
      mean = 1.6374 Angstrom
        t1 = 0.024745  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.025753  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6738 Angstrom
T2  -- O5  = 1.6289 Angstrom
T2  -- O3  = 1.6307 Angstrom
T2  -- O6  = 1.7155 Angstrom
      mean = 1.6622 Angstrom
        t1 = 0.061462  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037829  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O5  = 1.5665 Angstrom
T3  -- O7  = 1.5055 Angstrom
T3  -- O5  = 1.6708 Angstrom
T3  -- O6  = 1.6983 Angstrom
T3  -- O8  = 1.5890 Angstrom
      mean = 1.6060 Angstrom

        T-O SUMMARY
          Range  = 1.5055 A <--> 1.7155 A
          Mean   = 1.6330 A
          StdDev = 0.0537 A

       t1 Range  = 0.0247 <-- 0.0287 --> 0.0615
       t2 Range  = 0.0258 <-- 0.0212 --> 0.0378

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 109.704 deg; O1  -- O1  = 3 A
O1  -- T1  -- O3  = 103.158 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 109.489 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 113.022 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 110.691 deg; O1  -- O2  = 3 A
O3  -- T1  -- O2  = 110.495 deg; O3  -- O2  = 3 A
       103.158 deg <-- 109.427 deg --> 113.022 deg

O4  -- T2  -- O5  = 114.536 deg; O4  -- O5  = 3 A
O4  -- T2  -- O3  = 105.373 deg; O4  -- O3  = 3 A
O4  -- T2  -- O6  = 113.292 deg; O4  -- O6  = 3 A
O5  -- T2  -- O3  =  96.435 deg; O5  -- O3  = 2 A
O5  -- T2  -- O6  = 110.937 deg; O5  -- O6  = 3 A
O3  -- T2  -- O6  = 115.119 deg; O3  -- O6  = 3 A
       96.435 deg <-- 109.282 deg --> 115.119 deg

O5  -- T3  -- O7  = 113.353 deg; O5  -- O7  = 3 A
O5  -- T3  -- O5  = 101.912 deg; O5  -- O5  = 3 A
O5  -- T3  -- O6  = 160.653 deg; O5  -- O6  = 3 A
O5  -- T3  -- O8  = 106.956 deg; O5  -- O8  = 3 A
O7  -- T3  -- O5  = 116.569 deg; O7  -- O5  = 3 A
O7  -- T3  -- O6  =  57.271 deg; O7  -- O6  = 2 A
O7  -- T3  -- O8  = 114.261 deg; O7  -- O8  = 3 A
O5  -- T3  -- O6  =  71.985 deg; O5  -- O6  = 2 A
O5  -- T3  -- O8  = 102.398 deg; O5  -- O8  = 3 A
O6  -- T3  -- O8  =  92.355 deg; O6  -- O8  = 2 A
       57.271 deg <-- 103.771 deg --> 160.653 deg

        O-T-O SUMMARY
          Range  = 57.2714 deg <--> 160.6528 deg
          Mean   = 106.6434 deg
          StdDev = 18.5777 deg

        O--O SUMMARY
          Range  = 1.5447 A <--> 3.2185 A
          Mean   = 2.5842 A
          StdDev = 0.3200 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 129.748 deg ; T1  -- T1   2.9604 A

T1  -- O2  -- T1  = 147.579 deg ; T1  -- T1   3.1315 A

T1  -- O3  -- T2  = 137.746 deg ; T1  -- T2   3.0594 A

T2  -- O4  -- T2  = 159.002 deg ; T2  -- T2   3.2916 A

T2  -- O5  -- T3  =  83.074 deg ; T2  -- T3   2.1194 A
T2  -- O5  -- T3  = 158.245 deg ; T2  -- T3   3.2404 A
T3  -- O5  -- T3  =  78.088 deg ; T3  -- T3   2.0409 A

T2  -- O6  -- T3  = 139.939 deg ; T2  -- T3   3.2074 A

T3  -- O7  -- T3  = 180.000 deg ; T3  -- T3   3.0109 A

T3  -- O8  -- T3  = 167.622 deg ; T3  -- T3   3.1595 A


        T-O-T SUMMARY
          Range  = 78.0885° <--> 180.0000 deg
          Mean   = 138.1044 deg
          StdDev = 32.2369 deg

        T--T SUMMARY
          Range  = 2.0409 A <--> 3.2916 A
          Mean   = 2.9221 A
          StdDev = 0.4350 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O5  -- O6  = 1.9801 A
O6  -- O7  = 1.5447 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T2  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 3.0594 Angstrom
  T2  -- T2  = 3.2916 Angstrom
  T2  -- T3  = 2.1194 Angstrom
  T2  -- T3  = 3.2404 Angstrom
  T2  -- T3  = 3.2074 Angstrom
T3  has 6 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T3  -- T2  = 2.1194 Angstrom
  T3  -- T3  = 3.1595 Angstrom
  T3  -- T2  = 3.2404 Angstrom
  T3  -- T2  = 3.2074 Angstrom
  T3  -- T3  = 2.0409 Angstrom
  T3  -- T3  = 3.0109 Angstrom