Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_62_3_1512746_E89iU0.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 22.16 T-atoms per nm^3
Material density = 2.211 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6220 Angstrom
T1  -- O2  = 1.6228 Angstrom
T1  -- O3  = 1.6182 Angstrom
T1  -- O1  = 1.6219 Angstrom
      mean = 1.6212 Angstrom
        t1 = 0.007320  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002083  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6181 Angstrom
T2  -- O4  = 1.6203 Angstrom
T2  -- O5  = 1.6201 Angstrom
T2  -- O6  = 1.6206 Angstrom
      mean = 1.6198 Angstrom
        t1 = 0.006161  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001093  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6200 Angstrom
T3  -- O7  = 1.6154 Angstrom
T3  -- O8  = 1.6194 Angstrom
T3  -- O5  = 1.6209 Angstrom
      mean = 1.6189 Angstrom
        t1 = 0.005643  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001433  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6154 A <--> 1.6228 A
          Mean   = 1.6200 A
          StdDev = 0.0019 A

       t1 Range  = 0.0056 <-- 0.0064 --> 0.0073
       t2 Range  = 0.0011 <-- 0.0015 --> 0.0021

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.358 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.192 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 109.998 deg; O1  -- O1  = 3 A
O2  -- T1  -- O3  = 109.463 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 109.647 deg; O2  -- O1  = 3 A
O3  -- T1  -- O1  = 109.168 deg; O3  -- O1  = 3 A
       109.168 deg <-- 109.471 deg --> 109.998 deg

O3  -- T2  -- O4  = 109.558 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.764 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.275 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 109.612 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.333 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 109.284 deg; O5  -- O6  = 3 A
       109.275 deg <-- 109.471 deg --> 109.764 deg

O6  -- T3  -- O7  = 109.465 deg; O6  -- O7  = 3 A
O6  -- T3  -- O8  = 109.723 deg; O6  -- O8  = 3 A
O6  -- T3  -- O5  = 109.185 deg; O6  -- O5  = 3 A
O7  -- T3  -- O8  = 109.495 deg; O7  -- O8  = 3 A
O7  -- T3  -- O5  = 109.664 deg; O7  -- O5  = 3 A
O8  -- T3  -- O5  = 109.296 deg; O8  -- O5  = 3 A
       109.185 deg <-- 109.471 deg --> 109.723 deg

        O-T-O SUMMARY
          Range  = 109.1682 deg <--> 109.9976 deg
          Mean   = 109.4703 deg
          StdDev = 0.2288 deg

        O--O SUMMARY
          Range  = 2.6406 A <--> 2.6572 A
          Mean   = 2.6455 A
          StdDev = 0.0044 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  90.230 deg; T1  -- T2  = 4.3193 A
T1  - O1  - T1  - O3  - T1  = 110.779 deg; T1  -- T1  = 5.0161 A
T1  - O1  - T1  - O1  - T1  = 110.779 deg; T1  -- T1  = 5.0161 A
T2  - O2  - T1  - O3  - T1  = 115.178 deg; T2  -- T1  = 5.1811 A
T2  - O2  - T1  - O1  - T1  = 123.097 deg; T2  -- T1  = 5.3959 A
T1  - O3  - T1  - O1  - T1  = 105.716 deg; T1  -- T1  = 4.8910 A

T1  - O3  - T2  - O4  - T2  =  89.770 deg; T1  -- T2  = 4.3193 A
T1  - O3  - T2  - O5  - T3  = 121.789 deg; T1  -- T3  = 5.3037 A
T1  - O3  - T2  - O6  - T3  = 113.650 deg; T1  -- T3  = 5.0954 A
T2  - O4  - T2  - O5  - T3  = 110.720 deg; T2  -- T3  = 4.9796 A
T2  - O4  - T2  - O6  - T3  = 110.595 deg; T2  -- T3  = 4.9901 A
T3  - O5  - T2  - O6  - T3  = 108.696 deg; T3  -- T3  = 4.8910 A

T3  - O6  - T3  - O7  - T3  = 109.147 deg; T3  -- T3  = 5.1235 A
T3  - O6  - T3  - O8  - T2  = 110.595 deg; T3  -- T2  = 4.9933 A
T3  - O6  - T3  - O5  - T2  = 110.720 deg; T3  -- T2  = 4.9828 A
T3  - O7  - T3  - O8  - T2  = 105.006 deg; T3  -- T2  = 4.9597 A
T3  - O7  - T3  - O5  - T2  = 112.538 deg; T3  -- T2  = 5.1842 A
T2  - O8  - T3  - O5  - T2  = 108.696 deg; T2  -- T2  = 4.8910 A

        T-T-T SUMMARY
          Range  = 89.7695 deg <--> 123.0969 deg
          Mean   = 109.4399 deg
          StdDev = 8.2744 deg

        T--T SUMMARY
          Range  = 4.3193 A <--> 5.3959 A
          Mean   = 4.9745 A
          StdDev = 0.2728 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 142.073 deg ; T1  -- T1   3.0678 A

T1  -- O2  -- T1  = 137.675 deg ; T1  -- T1   3.0268 A

T1  -- O3  -- T2  = 143.027 deg ; T1  -- T2   3.0693 A

T2  -- O4  -- T2  = 140.647 deg ; T2  -- T2   3.0515 A

T2  -- O5  -- T3  = 137.264 deg ; T2  -- T3   3.0183 A

T2  -- O6  -- T3  = 135.651 deg ; T2  -- T3   3.0009 A

T3  -- O7  -- T3  = 180.000 deg ; T3  -- T3   3.2309 A

T3  -- O8  -- T3  = 141.261 deg ; T3  -- T3   3.0554 A


        T-O-T SUMMARY
          Range  = 135.6513° <--> 180.0000 deg
          Mean   = 144.6999 deg
          StdDev = 13.6652 deg

        T--T SUMMARY
          Range  = 3.0009 A <--> 3.2309 A
          Mean   = 3.0651 A
          StdDev = 0.0672 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 41 64 92 126 164 205 254 307 362 426 494 568 647
TD10 = 986
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 43 64 91 126 164 205 254 307 362 426 499 568 643
TD10 = 987
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

T3 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 25 42 65 93 124 162 205 254 307 366 430 495 569 648
TD10 = 987
Circuit symbol = 6.6_{2}.6.6_{2}.6_{2}.6_{2}
Weight = 25
Vertex symbol  = 6.6_{2}.6.6_{2}.6_{2}.6_{2}
Weight = 25

<TD10> = 986.667
Average ring size = 5.7778