Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_62_2_4807_sbeHEl.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 18.53 T-atoms per nm^3
Material density = 1.848 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6203 Angstrom
T1  -- O2  = 1.6209 Angstrom
T1  -- O3  = 1.6213 Angstrom
T1  -- O4  = 1.6205 Angstrom
      mean = 1.6207 Angstrom
        t1 = 0.006704  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000874  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6200 Angstrom
T2  -- O4  = 1.6217 Angstrom
T2  -- O5  = 1.6213 Angstrom
T2  -- O3  = 1.6206 Angstrom
      mean = 1.6209 Angstrom
        t1 = 0.006811  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000385  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6200 A <--> 1.6217 A
          Mean   = 1.6208 A
          StdDev = 0.0005 A

       t1 Range  = 0.0067 <-- 0.0068 --> 0.0068
       t2 Range  = 0.0004 <-- 0.0006 --> 0.0009

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.511 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.268 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.547 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.576 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.417 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.507 deg; O3  -- O4  = 3 A
       109.268 deg <-- 109.471 deg --> 109.576 deg

O2  -- T2  -- O4  = 109.570 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.479 deg; O2  -- O5  = 3 A
O2  -- T2  -- O3  = 109.433 deg; O2  -- O3  = 3 A
O4  -- T2  -- O5  = 109.543 deg; O4  -- O5  = 3 A
O4  -- T2  -- O3  = 109.481 deg; O4  -- O3  = 3 A
O5  -- T2  -- O3  = 109.321 deg; O5  -- O3  = 3 A
       109.321 deg <-- 109.471 deg --> 109.570 deg

        O-T-O SUMMARY
          Range  = 109.2677 deg <--> 109.5764 deg
          Mean   = 109.4712 deg
          StdDev = 0.0932 deg

        O--O SUMMARY
          Range  = 2.6434 A <--> 2.6491 A
          Mean   = 2.6468 A
          StdDev = 0.0017 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  90.011 deg; T1  -- T2  = 4.3136 A
T1  - O1  - T1  - O3  - T2  =  90.011 deg; T1  -- T2  = 4.3020 A
T1  - O1  - T1  - O4  - T2  = 130.259 deg; T1  -- T2  = 5.5220 A
T2  - O2  - T1  - O3  - T2  = 145.079 deg; T2  -- T2  = 5.7939 A
T2  - O2  - T1  - O4  - T2  = 115.888 deg; T2  -- T2  = 5.1504 A
T2  - O3  - T1  - O4  - T2  =  90.001 deg; T2  -- T2  = 4.2854 A

T1  - O2  - T2  - O4  - T2  =  89.989 deg; T1  -- T2  = 4.3136 A
T1  - O2  - T2  - O5  - T1  = 105.895 deg; T1  -- T1  = 4.8474 A
T1  - O2  - T2  - O3  - T1  = 137.233 deg; T1  -- T1  = 5.6586 A
T2  - O4  - T2  - O5  - T1  =  89.989 deg; T2  -- T1  = 4.3020 A
T2  - O4  - T2  - O3  - T1  = 130.259 deg; T2  -- T1  = 5.5231 A
T1  - O5  - T2  - O3  - T1  =  89.999 deg; T1  -- T1  = 4.2854 A

        T-T-T SUMMARY
          Range  = 89.9886 deg <--> 145.0793 deg
          Mean   = 108.7177 deg
          StdDev = 20.9758 deg

        T--T SUMMARY
          Range  = 4.2854 A <--> 5.7939 A
          Mean   = 4.8581 A
          StdDev = 0.6054 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 140.999 deg ; T1  -- T1   3.0547 A

T1  -- O2  -- T2  = 139.959 deg ; T1  -- T2   3.0451 A

T1  -- O3  -- T2  = 138.514 deg ; T1  -- T2   3.0318 A

T1  -- O4  -- T2  = 138.184 deg ; T1  -- T2   3.0287 A

T2  -- O5  -- T2  = 140.918 deg ; T2  -- T2   3.0559 A


        T-O-T SUMMARY
          Range  = 138.1840° <--> 140.9986 deg
          Mean   = 139.7147 deg
          StdDev = 1.1933 deg

        T--T SUMMARY
          Range  = 3.0287 A <--> 3.0559 A
          Mean   = 3.0432 A
          StdDev = 0.0114 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 32 48 67 92 120 150 185 224 266 312 361 414 472
TD10 = 726
Circuit symbol = 4.4.4.8_{3}.6.6
Weight = 18
Vertex symbol  = 4.4.4.8_{2}.8.8
Weight = 26

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 32 48 67 92 120 150 185 224 266 312 361 414 472
TD10 = 726
Circuit symbol = 4.4.4.8_{3}.6.6
Weight = 18
Vertex symbol  = 4.4.4.8_{2}.8.8
Weight = 26

<TD10> = 726.000
Average ring size = 5.6000