Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_5_2_28343_59QjPT.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 27.33 T-atoms per nm^3
Material density = 2.727 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6198 Angstrom
T1  -- O2  = 1.6173 Angstrom
T1  -- O1  = 1.6216 Angstrom
T1  -- O3  = 1.6203 Angstrom
      mean = 1.6197 Angstrom
        t1 = 0.006419  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001542  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6186 Angstrom
T2  -- O3  = 1.6203 Angstrom
T2  -- O2  = 1.6186 Angstrom
T2  -- O3  = 1.6203 Angstrom
      mean = 1.6194 Angstrom
        t1 = 0.006130  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002576  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6173 A <--> 1.6216 A
          Mean   = 1.6196 A
          StdDev = 0.0014 A

       t1 Range  = 0.0061 <-- 0.0063 --> 0.0064
       t2 Range  = 0.0015 <-- 0.0021 --> 0.0026

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.897 deg; O1  -- O2  = 3 A
O1  -- T1  -- O1  = 109.562 deg; O1  -- O1  = 3 A
O1  -- T1  -- O3  = 109.397 deg; O1  -- O3  = 3 A
O2  -- T1  -- O1  = 109.743 deg; O2  -- O1  = 3 A
O2  -- T1  -- O3  = 109.502 deg; O2  -- O3  = 3 A
O1  -- T1  -- O3  = 109.723 deg; O1  -- O3  = 3 A
       108.897 deg <-- 109.471 deg --> 109.743 deg

O2  -- T2  -- O3  = 109.352 deg; O2  -- O3  = 3 A
O2  -- T2  -- O2  = 110.152 deg; O2  -- O2  = 3 A
O2  -- T2  -- O3  = 109.237 deg; O2  -- O3  = 3 A
O3  -- T2  -- O2  = 109.237 deg; O3  -- O2  = 3 A
O3  -- T2  -- O3  = 109.496 deg; O3  -- O3  = 3 A
O2  -- T2  -- O3  = 109.352 deg; O2  -- O3  = 3 A
       109.237 deg <-- 109.471 deg --> 110.152 deg

        O-T-O SUMMARY
          Range  = 108.8972 deg <--> 110.1521 deg
          Mean   = 109.4709 deg
          StdDev = 0.3037 deg

        O--O SUMMARY
          Range  = 2.6337 A <--> 2.6542 A
          Mean   = 2.6448 A
          StdDev = 0.0053 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 108.034 deg; T1  -- T1  = 4.9218 A
T1  - O1  - T1  - O1  - T2  = 143.969 deg; T1  -- T2  = 5.7705 A
T1  - O1  - T1  - O3  - T2  =  89.499 deg; T1  -- T2  = 4.2770 A
T1  - O2  - T1  - O1  - T2  =  90.368 deg; T1  -- T2  = 4.3044 A
T1  - O2  - T1  - O3  - T2  = 120.236 deg; T1  -- T2  = 5.2675 A
T2  - O1  - T1  - O3  - T2  = 107.999 deg; T2  -- T2  = 4.9033 A

T1  - O2  - T2  - O3  - T1  = 107.999 deg; T1  -- T1  = 4.9033 A
T1  - O2  - T2  - O2  - T1  = 143.090 deg; T1  -- T1  = 5.7560 A
T1  - O2  - T2  - O3  - T1  =  90.278 deg; T1  -- T1  = 4.2960 A
T1  - O3  - T2  - O2  - T1  =  90.278 deg; T1  -- T1  = 4.2960 A
T1  - O3  - T2  - O3  - T1  = 120.564 deg; T1  -- T1  = 5.2574 A
T1  - O2  - T2  - O3  - T1  = 107.999 deg; T1  -- T1  = 4.9033 A

        T-T-T SUMMARY
          Range  = 89.4992 deg <--> 143.9687 deg
          Mean   = 110.0262 deg
          StdDev = 18.5994 deg

        T--T SUMMARY
          Range  = 4.2770 A <--> 5.7705 A
          Mean   = 4.9047 A
          StdDev = 0.5240 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 139.511 deg ; T1  -- T1   3.0412 A

T1  -- O2  -- T2  = 139.311 deg ; T1  -- T2   3.0340 A

T1  -- O3  -- T2  = 138.144 deg ; T1  -- T2   3.0268 A


        T-O-T SUMMARY
          Range  = 138.1440° <--> 139.5113 deg
          Mean   = 138.9886 deg
          StdDev = 0.6296 deg

        T--T SUMMARY
          Range  = 3.0268 A <--> 3.0412 A
          Mean   = 3.0340 A
          StdDev = 0.0061 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 30 52 80 116 156 204 258 318 384 458 536 622 714 812
TD10 = 1231
Circuit symbol = 6.6.6_{2}.6_{2}.8_{9}.8_{9}
Weight = 37
Vertex symbol  = 6.6.6_{2}.6_{2}.8_{7}.8_{7}
Weight = 37

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 12 30 52 80 116 156 204 258 318 384 458 536 622 714 812
TD10 = 1231
Circuit symbol = 6.6.6_{2}.6_{2}.8_{9}.8_{9}
Weight = 37
Vertex symbol  = 6.6.6_{2}.6_{2}.8_{7}.8_{7}
Weight = 37

<TD10> = 1231.000
Average ring size = 7.2727