Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_59_5_25449476_R4B39B.cif"

There are 40 T-atoms per unit cell
There are 80 O-atoms per unit cell

Framework density = 24.85 T-atoms per nm^3
Material density = 2.479 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.4542 Angstrom
T1  -- O2  = 1.6152 Angstrom
T1  -- O3  = 1.6022 Angstrom
T1  -- O4  = 1.5627 Angstrom
      mean = 1.5586 Angstrom
        t1 = 0.099384  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.106769  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6248 Angstrom
T2  -- O5  = 1.6429 Angstrom
T2  -- O6  = 1.7514 Angstrom
T2  -- O7  = 1.7063 Angstrom
      mean = 1.6814 Angstrom
        t1 = 0.067056  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.031547  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.5618 Angstrom
T3  -- O8  = 1.6567 Angstrom
T3  -- O9  = 1.5815 Angstrom
T3  -- O10 = 1.6612 Angstrom
      mean = 1.6153 Angstrom
        t1 = 0.070966  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.052129  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O6  = 1.7645 Angstrom
T4  -- O10 = 1.6901 Angstrom
T4  -- O11 = 1.6384 Angstrom
T4  -- O12 = 1.6202 Angstrom
      mean = 1.6783 Angstrom
        t1 = 0.062805  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.029097  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O7  = 1.7319 Angstrom
T5  -- O12 = 1.6154 Angstrom
T5  -- O13 = 1.6217 Angstrom
T5  -- O14 = 1.6910 Angstrom
      mean = 1.6650 Angstrom
        t1 = 0.055323  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.027143  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4542 A <--> 1.7645 A
          Mean   = 1.6397 A
          StdDev = 0.0710 A

       t1 Range  = 0.0553 <-- 0.0711 --> 0.0994
       t2 Range  = 0.0271 <-- 0.0493 --> 0.1068

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 114.645 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  89.546 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 114.245 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 115.584 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 123.535 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  91.127 deg; O3  -- O4  = 2 A
       89.546 deg <-- 108.114 deg --> 123.535 deg

O3  -- T2  -- O5  = 111.502 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 107.286 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 102.158 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 107.062 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 106.546 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 122.185 deg; O6  -- O7  = 3 A
       102.158 deg <-- 109.456 deg --> 122.185 deg

O4  -- T3  -- O8  = 118.644 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 106.176 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 =  88.569 deg; O4  -- O10 = 2 A
O8  -- T3  -- O9  = 114.176 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 111.611 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 115.255 deg; O9  -- O10 = 3 A
       88.569 deg <-- 109.072 deg --> 118.644 deg

O6  -- T4  -- O10 = 119.413 deg; O6  -- O10 = 3 A
O6  -- T4  -- O11 = 108.250 deg; O6  -- O11 = 3 A
O6  -- T4  -- O12 = 108.222 deg; O6  -- O12 = 3 A
O10 -- T4  -- O11 = 109.476 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 104.269 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 106.463 deg; O11 -- O12 = 3 A
       104.269 deg <-- 109.349 deg --> 119.413 deg

O7  -- T5  -- O12 = 105.044 deg; O7  -- O12 = 3 A
O7  -- T5  -- O13 = 107.928 deg; O7  -- O13 = 3 A
O7  -- T5  -- O14 = 120.333 deg; O7  -- O14 = 3 A
O12 -- T5  -- O13 = 107.993 deg; O12 -- O13 = 3 A
O12 -- T5  -- O14 = 107.439 deg; O12 -- O14 = 3 A
O13 -- T5  -- O14 = 107.575 deg; O13 -- O14 = 3 A
       105.044 deg <-- 109.385 deg --> 120.333 deg

        O-T-O SUMMARY
          Range  = 88.5687 deg <--> 123.5349 deg
          Mean   = 108.9144 deg
          StdDev = 8.6059 deg

        O--O SUMMARY
          Range  = 2.1552 A <--> 3.0270 A
          Mean   = 2.6661 A
          StdDev = 0.1924 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   2.9085 A

T1  -- O2  -- T1  = 119.902 deg ; T1  -- T1   2.7962 A

T1  -- O3  -- T2  = 129.792 deg ; T1  -- T2   2.9222 A

T1  -- O4  -- T3  =  99.437 deg ; T1  -- T3   2.3836 A

T2  -- O5  -- T2  = 137.786 deg ; T2  -- T2   3.0653 A

T2  -- O6  -- T4  = 159.588 deg ; T2  -- T4   3.4603 A

T2  -- O7  -- T5  = 159.344 deg ; T2  -- T5   3.3825 A

T3  -- O8  -- T3  = 133.308 deg ; T3  -- T3   3.0422 A

T3  -- O9  -- T3  = 102.253 deg ; T3  -- T3   2.4624 A

T3  -- O10 -- T4  = 134.905 deg ; T3  -- T4   3.0952 A

T4  -- O11 -- T4  = 153.057 deg ; T4  -- T4   3.1867 A

T4  -- O12 -- T5  = 149.899 deg ; T4  -- T5   3.1247 A

T5  -- O13 -- T5  = 172.092 deg ; T5  -- T5   3.2357 A

T5  -- O14 -- T5  = 128.504 deg ; T5  -- T5   3.0463 A


        T-O-T SUMMARY
          Range  = 99.4373° <--> 180.0000 deg
          Mean   = 139.9905 deg
          StdDev = 23.1601 deg

        T--T SUMMARY
          Range  = 2.3836 A <--> 3.4603 A
          Mean   = 3.0080 A
          StdDev = 0.2947 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O3  = 2.1552 A
O1  -- O3  = 2.1552 A
O3  -- O4  = 2.2600 A
O4  -- O10 = 2.2515 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T2  = 3.4633 Angstrom
  T1  -- T3  = 2.3836 Angstrom
  T1  -- T4  = 3.1408 Angstrom
  T1  -- T1  = 2.7962 Angstrom
  T1  -- T1  = 2.9085 Angstrom
  T1  -- T2  = 2.9222 Angstrom
T2  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 3.4633 Angstrom
  T2  -- T4  = 3.4603 Angstrom
  T2  -- T5  = 3.3825 Angstrom
  T2  -- T2  = 3.0653 Angstrom
  T2  -- T1  = 2.9222 Angstrom
T3  -- T3  = 2.4624 Angstrom
T3  -- T1  = 2.3836 Angstrom
T4  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T1  = 3.1408 Angstrom
  T4  -- T2  = 3.4603 Angstrom
  T4  -- T3  = 3.0952 Angstrom
  T4  -- T4  = 3.1867 Angstrom
  T4  -- T5  = 3.1247 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 22 39 64 93 127 168 211 259 314 374 441 508 583 669
TD10 = 999
Circuit symbol = 4.5.5.6_{2}.6.8_{5}
Weight = 24
Vertex symbol  = 4.5.5.6_{2}.6.8_{2}
Weight = 24

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 25 42 66 94 128 168 214 266 316 375 445 516 592 674
TD10 = 1020
Circuit symbol = 5.6.6.6_{2}.6.6_{2}
Weight = 21
Vertex symbol  = 5.6.6.6_{2}.6.6_{2}
Weight = 21

T3 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 22 40 63 92 127 167 210 258 317 381 442 514 594 668
TD10 = 994
Circuit symbol = 4.5.4.6.6.6_{2}
Weight = 15
Vertex symbol  = 4.5.4.6.6_{2}.8
Weight = 20

T4 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 24 40 65 95 128 165 211 264 317 379 445 516 592 670
TD10 = 1009
Circuit symbol = 5.6.6_{2}.6_{2}.6_{2}.7
Weight = 22
Vertex symbol  = 5.6.6_{2}.6_{2}.6_{2}.8_{3}
Weight = 29

T5 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 25 45 67 92 127 168 210 260 321 384 444 515 594 669
TD10 = 1010
Circuit symbol = 4.6_{2}.6.6_{2}.6_{2}.8_{5}
Weight = 29
Vertex symbol  = 4.6_{2}.6.6_{2}.6_{2}.8_{3}
Weight = 29

<TD10> = 1006.400
Average ring size = 5.9016