Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_59_5_22682903_w4BhtB.cif"

There are 40 T-atoms per unit cell
There are 80 O-atoms per unit cell

Framework density = 25.58 T-atoms per nm^3
Material density = 2.552 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5620 Angstrom
T1  -- O2  = 1.5980 Angstrom
T1  -- O3  = 1.5256 Angstrom
T1  -- O4  = 1.6544 Angstrom
      mean = 1.5850 Angstrom
        t1 = 0.057488  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.081683  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.5564 Angstrom
T2  -- O5  = 1.6654 Angstrom
T2  -- O6  = 1.6814 Angstrom
T2  -- O7  = 1.6265 Angstrom
      mean = 1.6324 Angstrom
        t1 = 0.076920  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.056715  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6572 Angstrom
T3  -- O8  = 1.6583 Angstrom
T3  -- O9  = 1.6774 Angstrom
T3  -- O10 = 1.7222 Angstrom
      mean = 1.6788 Angstrom
        t1 = 0.055496  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.022593  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O6  = 1.7287 Angstrom
T4  -- O6  = 2.0174 Angstrom
T4  -- O7  = 1.9603 Angstrom
T4  -- O10 = 1.7246 Angstrom
T4  -- O11 = 1.6344 Angstrom
T4  -- O12 = 1.6085 Angstrom
      mean = 1.7790 Angstrom

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O7  = 1.5921 Angstrom
T5  -- O12 = 1.5640 Angstrom
T5  -- O13 = 1.6109 Angstrom
T5  -- O14 = 1.5676 Angstrom
      mean = 1.5837 Angstrom
        t1 = 0.116871  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.078438  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5256 A <--> 2.0174 A
          Mean   = 1.6633 A
          StdDev = 0.1176 A

       t1 Range  = 0.0555 <-- 0.0614 --> 0.1169
       t2 Range  = 0.0226 <-- 0.0479 --> 0.0817

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.873 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  95.287 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 110.839 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.080 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 111.914 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 116.720 deg; O3  -- O4  = 3 A
       95.287 deg <-- 109.286 deg --> 116.720 deg

O3  -- T2  -- O5  =  99.451 deg; O3  -- O5  = 2 A
O3  -- T2  -- O6  = 118.272 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  =  93.079 deg; O3  -- O7  = 2 A
O5  -- T2  -- O6  = 116.462 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 118.909 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 108.529 deg; O6  -- O7  = 3 A
       93.079 deg <-- 109.117 deg --> 118.909 deg

O4  -- T3  -- O8  = 101.392 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 109.608 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 109.229 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 107.564 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 115.750 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 112.641 deg; O9  -- O10 = 3 A
       101.392 deg <-- 109.364 deg --> 115.750 deg

O6  -- T4  -- O6  =  83.704 deg; O6  -- O6  = 3 A
O6  -- T4  -- O7  = 116.708 deg; O6  -- O7  = 3 A
O6  -- T4  -- O10 =  62.635 deg; O6  -- O10 = 2 A
O6  -- T4  -- O11 =  96.237 deg; O6  -- O11 = 3 A
O6  -- T4  -- O12 = 121.355 deg; O6  -- O12 = 3 A
O6  -- T4  -- O7  =  84.911 deg; O6  -- O7  = 3 A
O6  -- T4  -- O10 = 144.890 deg; O6  -- O10 = 4 A
O6  -- T4  -- O11 =  90.673 deg; O6  -- O11 = 3 A
O6  -- T4  -- O12 = 149.089 deg; O6  -- O12 = 3 A
O7  -- T4  -- O10 = 100.808 deg; O7  -- O10 = 3 A
O7  -- T4  -- O11 = 145.933 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 =  68.186 deg; O7  -- O12 = 2 A
O10 -- T4  -- O11 = 102.018 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 =  59.347 deg; O10 -- O12 = 2 A
O11 -- T4  -- O12 = 102.989 deg; O11 -- O12 = 3 A
       59.347 deg <-- 101.966 deg --> 149.089 deg

O7  -- T5  -- O12 =  79.657 deg; O7  -- O12 = 2 A
O7  -- T5  -- O13 =  94.977 deg; O7  -- O13 = 2 A
O7  -- T5  -- O14 =  99.679 deg; O7  -- O14 = 2 A
O12 -- T5  -- O13 = 132.040 deg; O12 -- O13 = 3 A
O12 -- T5  -- O14 = 111.845 deg; O12 -- O14 = 3 A
O13 -- T5  -- O14 = 116.020 deg; O13 -- O14 = 3 A
       79.657 deg <-- 105.703 deg --> 132.040 deg

        O-T-O SUMMARY
          Range  = 59.3474 deg <--> 149.0887 deg
          Mean   = 105.6820 deg
          StdDev = 19.9556 deg

        O--O SUMMARY
          Range  = 1.6532 A <--> 3.5688 A
          Mean   = 2.6444 A
          StdDev = 0.3940 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.1241 A

T1  -- O2  -- T1  = 175.534 deg ; T1  -- T1   3.1936 A

T1  -- O3  -- T2  = 166.183 deg ; T1  -- T2   3.0596 A

T1  -- O4  -- T3  = 129.874 deg ; T1  -- T3   2.9998 A

T2  -- O5  -- T2  = 148.023 deg ; T2  -- T2   3.2019 A

T2  -- O6  -- T4  = 148.651 deg ; T2  -- T4   3.2834 A
T2  -- O6  -- T4  =  59.055 deg ; T2  -- T4   1.8462 A
T4  -- O6  -- T4  =  96.296 deg ; T4  -- T4   2.7970 A

T2  -- O7  -- T4  =  61.121 deg ; T2  -- T4   1.8462 A
T2  -- O7  -- T5  = 140.463 deg ; T2  -- T5   3.0289 A
T4  -- O7  -- T5  =  84.923 deg ; T4  -- T5   2.4135 A

T3  -- O8  -- T3  = 160.065 deg ; T3  -- T3   3.2664 A

T3  -- O9  -- T3  = 153.788 deg ; T3  -- T3   3.2674 A

T3  -- O10 -- T4  = 164.187 deg ; T3  -- T4   3.4140 A

T4  -- O11 -- T4  = 134.548 deg ; T4  -- T4   3.0151 A

T4  -- O12 -- T5  =  99.053 deg ; T4  -- T5   2.4135 A

T5  -- O13 -- T5  = 118.222 deg ; T5  -- T5   2.7649 A

T5  -- O14 -- T5  = 118.308 deg ; T5  -- T5   2.6917 A


        T-O-T SUMMARY
          Range  = 59.0552° <--> 180.0000 deg
          Mean   = 129.9052 deg
          StdDev = 36.2603 deg

        T--T SUMMARY
          Range  = 1.8462 A <--> 3.4140 A
          Mean   = 2.8682 A
          StdDev = 0.4563 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O3  = 2.2818 A
O1  -- O3  = 2.2818 A
O6  -- O10 = 1.7950 A
O7  -- O12 = 2.0216 A
O10 -- O12 = 1.6532 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T2  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 3.0596 Angstrom
  T2  -- T2  = 3.2019 Angstrom
  T2  -- T4  = 1.8462 Angstrom
  T2  -- T4  = 3.2834 Angstrom
  T2  -- T5  = 3.0289 Angstrom
T3  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T3  -- T3  = 3.2664 Angstrom
  T3  -- T4  = 3.4140 Angstrom
  T3  -- T5  = 2.7659 Angstrom
  T3  -- T3  = 3.2674 Angstrom
  T3  -- T1  = 2.9998 Angstrom
T4  has 6 oxygen-bridged T-atoms within 3.50 A
  T4  -- T2  = 1.8462 Angstrom
  T4  -- T2  = 3.2834 Angstrom
  T4  -- T3  = 3.4140 Angstrom
  T4  -- T4  = 2.7970 Angstrom
  T4  -- T4  = 3.0151 Angstrom
  T4  -- T5  = 2.4135 Angstrom
T5  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T5  -- T2  = 3.0289 Angstrom
  T5  -- T3  = 2.7659 Angstrom
  T5  -- T4  = 2.4135 Angstrom
  T5  -- T5  = 2.7649 Angstrom
  T5  -- T5  = 2.6917 Angstrom