Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_59_5_20743796_Zg2egI.cif"

There are 40 T-atoms per unit cell
There are 80 O-atoms per unit cell

Framework density = 25.03 T-atoms per nm^3
Material density = 2.498 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6055 Angstrom
T1  -- O2  = 1.6848 Angstrom
T1  -- O3  = 1.5614 Angstrom
T1  -- O4  = 1.5526 Angstrom
      mean = 1.6011 Angstrom
        t1 = 0.067357  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.042742  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.4917 Angstrom
T2  -- O5  = 1.5903 Angstrom
T2  -- O6  = 1.6185 Angstrom
T2  -- O7  = 1.6838 Angstrom
      mean = 1.5961 Angstrom
        t1 = 0.032704  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.023815  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.5037 Angstrom
T3  -- O8  = 1.6312 Angstrom
T3  -- O9  = 1.6131 Angstrom
T3  -- O10 = 1.6526 Angstrom
      mean = 1.6002 Angstrom
        t1 = 0.071636  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.098365  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6713 Angstrom
T4  -- O9  = 1.6821 Angstrom
T4  -- O11 = 1.6013 Angstrom
T4  -- O12 = 1.6031 Angstrom
      mean = 1.6394 Angstrom
        t1 = 0.049090  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.033172  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.6531 Angstrom
T5  -- O12 = 1.6331 Angstrom
T5  -- O13 = 1.6089 Angstrom
T5  -- O14 = 1.6504 Angstrom
      mean = 1.6364 Angstrom
        t1 = 0.029952  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.018664  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4917 A <--> 1.6848 A
          Mean   = 1.6146 A
          StdDev = 0.0538 A

       t1 Range  = 0.0300 <-- 0.0501 --> 0.0716
       t2 Range  = 0.0187 <-- 0.0434 --> 0.0984

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 113.281 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.855 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 105.525 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 114.281 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 118.287 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  93.753 deg; O3  -- O4  = 2 A
       93.753 deg <-- 109.164 deg --> 118.287 deg

O3  -- T2  -- O5  = 106.106 deg; O3  -- O5  = 2 A
O3  -- T2  -- O6  = 110.400 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 109.308 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 110.302 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 110.194 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 110.440 deg; O6  -- O7  = 3 A
       106.106 deg <-- 109.458 deg --> 110.440 deg

O4  -- T3  -- O8  = 109.032 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  =  91.987 deg; O4  -- O9  = 2 A
O4  -- T3  -- O10 = 108.217 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 113.013 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 112.654 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 119.440 deg; O9  -- O10 = 3 A
       91.987 deg <-- 109.057 deg --> 119.440 deg

O7  -- T4  -- O9  = 121.057 deg; O7  -- O9  = 3 A
O7  -- T4  -- O11 = 105.359 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 111.771 deg; O7  -- O12 = 3 A
O9  -- T4  -- O11 = 107.959 deg; O9  -- O11 = 3 A
O9  -- T4  -- O12 = 101.606 deg; O9  -- O12 = 3 A
O11 -- T4  -- O12 = 108.664 deg; O11 -- O12 = 3 A
       101.606 deg <-- 109.403 deg --> 121.057 deg

O10 -- T5  -- O12 = 112.707 deg; O10 -- O12 = 3 A
O10 -- T5  -- O13 = 107.396 deg; O10 -- O13 = 3 A
O10 -- T5  -- O14 = 114.850 deg; O10 -- O14 = 3 A
O12 -- T5  -- O13 = 106.017 deg; O12 -- O13 = 3 A
O12 -- T5  -- O14 = 107.406 deg; O12 -- O14 = 3 A
O13 -- T5  -- O14 = 108.023 deg; O13 -- O14 = 3 A
       106.017 deg <-- 109.400 deg --> 114.850 deg

        O-T-O SUMMARY
          Range  = 91.9867 deg <--> 121.0567 deg
          Mean   = 109.2311 deg
          StdDev = 6.2120 deg

        O--O SUMMARY
          Range  = 2.2431 A <--> 2.9194 A
          Mean   = 2.6296 A
          StdDev = 0.1424 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2110 A

T1  -- O2  -- T1  = 151.520 deg ; T1  -- T1   3.2660 A

T1  -- O3  -- T2  = 119.021 deg ; T1  -- T2   2.6311 A

T1  -- O4  -- T3  = 131.052 deg ; T1  -- T3   2.7817 A

T2  -- O5  -- T2  = 141.188 deg ; T2  -- T2   2.9999 A

T2  -- O6  -- T2  = 126.573 deg ; T2  -- T2   2.8916 A

T2  -- O7  -- T4  = 142.048 deg ; T2  -- T4   3.1728 A

T3  -- O8  -- T3  = 129.268 deg ; T3  -- T3   2.9478 A

T3  -- O9  -- T4  = 141.698 deg ; T3  -- T4   3.1129 A

T3  -- O10 -- T5  = 161.301 deg ; T3  -- T5   3.2618 A

T4  -- O11 -- T4  = 135.721 deg ; T4  -- T4   2.9665 A

T4  -- O12 -- T5  = 125.458 deg ; T4  -- T5   2.8765 A

T5  -- O13 -- T5  = 143.667 deg ; T5  -- T5   3.0575 A

T5  -- O14 -- T5  = 120.072 deg ; T5  -- T5   2.8595 A


        T-O-T SUMMARY
          Range  = 119.0207° <--> 180.0000 deg
          Mean   = 139.1847 deg
          StdDev = 16.2006 deg

        T--T SUMMARY
          Range  = 2.6311 A <--> 3.2660 A
          Mean   = 3.0026 A
          StdDev = 0.1829 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O3  -- O4  = 2.2728 A
O4  -- O9  = 2.2431 A

T-T-T analysis was not conducted.
T1  -- T2  = 2.6311 Angstrom
T1  -- T3  = 2.7817 Angstrom
T2  -- T1  = 2.6311 Angstrom

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T3  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T3  -- T1  = 2.7817 Angstrom
  T3  -- T3  = 3.2557 Angstrom
  T3  -- T3  = 2.9478 Angstrom
  T3  -- T4  = 3.1129 Angstrom
  T3  -- T5  = 3.2618 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 22 39 64 93 127 168 211 259 314 374 441 508 583 669
TD10 = 999
Circuit symbol = 4.5.5.6_{2}.6.8_{5}
Weight = 24
Vertex symbol  = 4.5.5.6_{2}.6.8_{2}
Weight = 24

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 22 40 63 92 127 167 210 258 317 381 442 514 594 668
TD10 = 994
Circuit symbol = 4.5.4.6.6.6_{2}
Weight = 15
Vertex symbol  = 4.5.4.6.6_{2}.8
Weight = 20

T3 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 25 42 66 94 128 168 214 266 316 375 445 516 592 674
TD10 = 1020
Circuit symbol = 5.6.6.6_{2}.6.6_{2}
Weight = 21
Vertex symbol  = 5.6.6.6_{2}.6.6_{2}
Weight = 21

T4 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 24 40 65 95 128 165 211 264 317 379 445 516 592 670
TD10 = 1009
Circuit symbol = 5.6.6_{2}.6_{2}.6_{2}.7
Weight = 22
Vertex symbol  = 5.6.6_{2}.6_{2}.6_{2}.8_{3}
Weight = 29

T5 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 25 45 67 92 127 168 210 260 321 384 444 515 594 669
TD10 = 1010
Circuit symbol = 4.6_{2}.6.6_{2}.6_{2}.8_{5}
Weight = 29
Vertex symbol  = 4.6_{2}.6.6_{2}.6_{2}.8_{3}
Weight = 29

<TD10> = 1006.400
Average ring size = 5.9016