Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_57_2_8573_fl1djL.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 19.82 T-atoms per nm^3
Material density = 1.978 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6188 Angstrom
T1  -- O3  = 1.6217 Angstrom
T1  -- O4  = 1.6220 Angstrom
T1  -- O2  = 1.6216 Angstrom
      mean = 1.6210 Angstrom
        t1 = 0.006952  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001441  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6216 Angstrom
T2  -- O4  = 1.6221 Angstrom
T2  -- O5  = 1.6190 Angstrom
T2  -- O3  = 1.6217 Angstrom
      mean = 1.6211 Angstrom
        t1 = 0.006982  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000669  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6188 A <--> 1.6221 A
          Mean   = 1.6211 A
          StdDev = 0.0013 A

       t1 Range  = 0.0070 <-- 0.0070 --> 0.0070
       t2 Range  = 0.0007 <-- 0.0011 --> 0.0014

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 109.195 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.847 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 109.497 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 109.443 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 109.405 deg; O3  -- O2  = 3 A
O4  -- T1  -- O2  = 109.439 deg; O4  -- O2  = 3 A
       109.195 deg <-- 109.471 deg --> 109.847 deg

O2  -- T2  -- O4  = 109.386 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.563 deg; O2  -- O5  = 3 A
O2  -- T2  -- O3  = 109.443 deg; O2  -- O3  = 3 A
O4  -- T2  -- O5  = 109.177 deg; O4  -- O5  = 3 A
O4  -- T2  -- O3  = 109.518 deg; O4  -- O3  = 3 A
O5  -- T2  -- O3  = 109.740 deg; O5  -- O3  = 3 A
       109.177 deg <-- 109.471 deg --> 109.740 deg

        O-T-O SUMMARY
          Range  = 109.1765 deg <--> 109.8470 deg
          Mean   = 109.4711 deg
          StdDev = 0.1840 deg

        O--O SUMMARY
          Range  = 2.6413 A <--> 2.6522 A
          Mean   = 2.6472 A
          StdDev = 0.0030 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O3  - T2  = 110.683 deg; T2  -- T2  = 4.9548 A
T2  - O1  - T1  - O4  - T2  =  97.197 deg; T2  -- T2  = 4.5203 A
T2  - O1  - T1  - O2  - T1  = 113.872 deg; T2  -- T1  = 5.1307 A
T2  - O3  - T1  - O4  - T2  =  83.083 deg; T2  -- T2  = 4.0005 A
T2  - O3  - T1  - O2  - T1  = 113.820 deg; T2  -- T1  = 5.1343 A
T2  - O4  - T1  - O2  - T1  = 133.811 deg; T2  -- T1  = 5.6393 A

T1  - O2  - T2  - O4  - T2  = 117.002 deg; T1  -- T2  = 5.2115 A
T1  - O2  - T2  - O5  - T1  = 110.683 deg; T1  -- T1  = 4.9548 A
T1  - O2  - T2  - O3  - T1  =  82.803 deg; T1  -- T1  = 3.9853 A
T2  - O4  - T2  - O5  - T1  = 116.942 deg; T2  -- T1  = 5.2150 A
T2  - O4  - T2  - O3  - T1  = 126.867 deg; T2  -- T1  = 5.4745 A
T1  - O5  - T2  - O3  - T1  =  96.917 deg; T1  -- T1  = 4.5151 A

        T-T-T SUMMARY
          Range  = 82.8026 deg <--> 133.8109 deg
          Mean   = 108.6400 deg
          StdDev = 15.2351 deg

        T--T SUMMARY
          Range  = 3.9853 A <--> 5.6393 A
          Mean   = 4.8947 A
          StdDev = 0.5130 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 148.110 deg ; T1  -- T1   3.1130 A

T1  -- O2  -- T2  = 136.993 deg ; T1  -- T2   3.0175 A

T1  -- O3  -- T2  = 136.737 deg ; T1  -- T2   3.0149 A

T1  -- O4  -- T2  = 136.077 deg ; T1  -- T2   3.0087 A

T2  -- O5  -- T2  = 146.794 deg ; T2  -- T2   3.1031 A


        T-O-T SUMMARY
          Range  = 136.0770° <--> 148.1103 deg
          Mean   = 140.9422 deg
          StdDev = 5.4079 deg

        T--T SUMMARY
          Range  = 3.0087 A <--> 3.1130 A
          Mean   = 3.0514 A
          StdDev = 0.0470 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 38 56 80 112 142 179 224 268 318 376 434 497 568
TD10 = 867
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 21

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 36 56 82 110 142 181 222 266 320 376 432 499 568
TD10 = 865
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 866.000
Average ring size = 5.6000