Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_56_2_31033_DDjIWN.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 19.54 T-atoms per nm^3
Material density = 1.950 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6122 Angstrom
T1  -- O2  = 1.6077 Angstrom
T1  -- O3  = 1.6102 Angstrom
T1  -- O4  = 1.6226 Angstrom
      mean = 1.6132 Angstrom
        t1 = 0.004288  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002534  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6093 Angstrom
T2  -- O5  = 1.6207 Angstrom
T2  -- O3  = 1.6111 Angstrom
T2  -- O4  = 1.6199 Angstrom
      mean = 1.6152 Angstrom
        t1 = 0.005106  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004350  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6077 A <--> 1.6226 A
          Mean   = 1.6142 A
          StdDev = 0.0055 A

       t1 Range  = 0.0043 <-- 0.0047 --> 0.0051
       t2 Range  = 0.0025 <-- 0.0034 --> 0.0044

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.724 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.465 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.410 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.669 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.207 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.349 deg; O3  -- O4  = 3 A
       108.724 deg <-- 109.471 deg --> 110.207 deg

O2  -- T2  -- O5  = 110.048 deg; O2  -- O5  = 3 A
O2  -- T2  -- O3  = 109.058 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 108.781 deg; O2  -- O4  = 3 A
O5  -- T2  -- O3  = 109.598 deg; O5  -- O3  = 3 A
O5  -- T2  -- O4  = 109.781 deg; O5  -- O4  = 3 A
O3  -- T2  -- O4  = 109.555 deg; O3  -- O4  = 3 A
       108.781 deg <-- 109.470 deg --> 110.048 deg

        O-T-O SUMMARY
          Range  = 108.7241 deg <--> 110.2073 deg
          Mean   = 109.4705 deg
          StdDev = 0.4360 deg

        O--O SUMMARY
          Range  = 2.6168 A <--> 2.6509 A
          Mean   = 2.6360 A
          StdDev = 0.0104 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 107.890 deg; T1  -- T2  = 5.2066 A
T1  - O1  - T1  - O3  - T2  = 118.566 deg; T1  -- T2  = 5.3742 A
T1  - O1  - T1  - O4  - T2  = 110.342 deg; T1  -- T2  = 5.2899 A
T2  - O2  - T1  - O3  - T2  =  90.732 deg; T2  -- T2  = 4.4436 A
T2  - O2  - T1  - O4  - T2  = 107.282 deg; T2  -- T2  = 5.1829 A
T2  - O3  - T1  - O4  - T2  = 118.906 deg; T2  -- T2  = 5.3799 A

T1  - O2  - T2  - O5  - T2  = 109.187 deg; T1  -- T2  = 5.2626 A
T1  - O2  - T2  - O3  - T1  =  89.268 deg; T1  -- T1  = 4.3873 A
T1  - O2  - T2  - O4  - T1  = 109.958 deg; T1  -- T1  = 5.2705 A
T2  - O5  - T2  - O3  - T1  = 117.879 deg; T2  -- T1  = 5.3693 A
T2  - O5  - T2  - O4  - T1  = 109.768 deg; T2  -- T1  = 5.2849 A
T1  - O3  - T2  - O4  - T1  = 118.430 deg; T1  -- T1  = 5.3666 A

        T-T-T SUMMARY
          Range  = 89.2679 deg <--> 118.9062 deg
          Mean   = 109.0173 deg
          StdDev = 9.5719 deg

        T--T SUMMARY
          Range  = 4.3873 A <--> 5.3799 A
          Mean   = 5.1515 A
          StdDev = 0.3369 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 179.655 deg ; T1  -- T1   3.2244 A

T1  -- O2  -- T2  = 176.864 deg ; T1  -- T2   3.2158 A

T1  -- O3  -- T2  = 176.722 deg ; T1  -- T2   3.2200 A

T1  -- O4  -- T2  = 137.874 deg ; T1  -- T2   3.0258 A

T2  -- O5  -- T2  = 177.949 deg ; T2  -- T2   3.2408 A


        T-O-T SUMMARY
          Range  = 137.8736° <--> 179.6551 deg
          Mean   = 169.8126 deg
          StdDev = 16.2078 deg

        T--T SUMMARY
          Range  = 3.0258 A <--> 3.2408 A
          Mean   = 3.1854 A
          StdDev = 0.0813 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 41 63 91 123 160 202 249 301 358 420 487 559 635
TD10 = 969
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 41 63 91 123 160 202 249 301 358 420 487 559 635
TD10 = 969
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

<TD10> = 969.000
Average ring size = 5.6000