Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_55_3_49766_JcQ8yF.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 21.33 T-atoms per nm^3
Material density = 2.129 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6144 Angstrom
T1  -- O2  = 1.6275 Angstrom
T1  -- O3  = 1.6199 Angstrom
T1  -- O4  = 1.6241 Angstrom
      mean = 1.6215 Angstrom
        t1 = 0.010131  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.009498  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6257 Angstrom
T2  -- O6  = 1.6122 Angstrom
T2  -- O3  = 1.6184 Angstrom
T2  -- O5  = 1.6201 Angstrom
      mean = 1.6191 Angstrom
        t1 = 0.006991  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005421  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6162 Angstrom
T3  -- O7  = 1.6143 Angstrom
T3  -- O8  = 1.6189 Angstrom
T3  -- O8  = 1.6202 Angstrom
      mean = 1.6174 Angstrom
        t1 = 0.007642  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006244  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6122 A <--> 1.6275 A
          Mean   = 1.6193 A
          StdDev = 0.0045 A

       t1 Range  = 0.0070 <-- 0.0083 --> 0.0101
       t2 Range  = 0.0054 <-- 0.0071 --> 0.0095

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.022 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 107.772 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.274 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.928 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.250 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 110.542 deg; O3  -- O4  = 3 A
       107.772 deg <-- 109.465 deg --> 110.542 deg

O4  -- T2  -- O6  = 109.525 deg; O4  -- O6  = 3 A
O4  -- T2  -- O3  = 110.394 deg; O4  -- O3  = 3 A
O4  -- T2  -- O5  = 109.386 deg; O4  -- O5  = 3 A
O6  -- T2  -- O3  = 109.510 deg; O6  -- O3  = 3 A
O6  -- T2  -- O5  = 108.813 deg; O6  -- O5  = 3 A
O3  -- T2  -- O5  = 109.187 deg; O3  -- O5  = 3 A
       108.813 deg <-- 109.469 deg --> 110.394 deg

O6  -- T3  -- O7  = 108.971 deg; O6  -- O7  = 3 A
O6  -- T3  -- O8  = 110.709 deg; O6  -- O8  = 3 A
O6  -- T3  -- O8  = 110.888 deg; O6  -- O8  = 3 A
O7  -- T3  -- O8  = 108.582 deg; O7  -- O8  = 3 A
O7  -- T3  -- O8  = 108.686 deg; O7  -- O8  = 3 A
O8  -- T3  -- O8  = 108.950 deg; O8  -- O8  = 3 A
       108.582 deg <-- 109.464 deg --> 110.888 deg

        O-T-O SUMMARY
          Range  = 107.7720 deg <--> 110.8876 deg
          Mean   = 109.4787 deg
          StdDev = 0.8252 deg

        O--O SUMMARY
          Range  = 2.6128 A <--> 2.6676 A
          Mean   = 2.6443 A
          StdDev = 0.0163 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 119.754 deg; T2  -- T1  = 5.5149 A
T2  - O1  - T1  - O3  - T2  = 113.892 deg; T2  -- T2  = 5.2722 A
T2  - O1  - T1  - O4  - T1  = 109.982 deg; T2  -- T1  = 5.0402 A
T1  - O2  - T1  - O3  - T2  = 110.462 deg; T1  -- T2  = 5.2270 A
T1  - O2  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.4047 A
T2  - O3  - T1  - O4  - T1  = 110.069 deg; T2  -- T1  = 5.0320 A

T1  - O4  - T2  - O6  - T2  = 110.069 deg; T1  -- T2  = 5.0948 A
T1  - O4  - T2  - O3  - T3  = 107.406 deg; T1  -- T3  = 5.0272 A
T1  - O4  - T2  - O5  - T1  = 113.892 deg; T1  -- T1  = 5.2722 A
T2  - O6  - T2  - O3  - T3  = 109.316 deg; T2  -- T3  = 5.0388 A
T2  - O6  - T2  - O5  - T1  = 109.982 deg; T2  -- T1  = 5.1029 A
T3  - O3  - T2  - O5  - T1  = 105.991 deg; T3  -- T1  = 4.9917 A

T2  - O6  - T3  - O7  - T3  = 112.724 deg; T2  -- T3  = 5.0022 A
T2  - O6  - T3  - O8  - T3  = 114.241 deg; T2  -- T3  = 5.0458 A
T2  - O6  - T3  - O8  - T3  = 109.316 deg; T2  -- T3  = 5.0605 A
T3  - O7  - T3  - O8  - T3  = 130.047 deg; T3  -- T3  = 5.2722 A
T3  - O7  - T3  - O8  - T3  =  90.000 deg; T3  -- T3  = 4.2541 A
T3  - O8  - T3  - O8  - T3  =  90.000 deg; T3  -- T3  = 4.2541 A

        T-T-T SUMMARY
          Range  = 90.0000 deg <--> 130.0473 deg
          Mean   = 108.4152 deg
          StdDev = 9.8483 deg

        T--T SUMMARY
          Range  = 4.2541 A <--> 5.5149 A
          Mean   = 4.9800 A
          StdDev = 0.3304 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 173.884 deg ; T1  -- T1   3.2242 A

T1  -- O2  -- T1  = 134.436 deg ; T1  -- T1   3.0010 A

T1  -- O3  -- T2  = 153.433 deg ; T1  -- T2   3.1517 A

T1  -- O4  -- T2  = 149.930 deg ; T1  -- T2   3.1386 A

T2  -- O5  -- T2  = 143.619 deg ; T2  -- T2   3.0783 A

T2  -- O6  -- T3  = 147.435 deg ; T2  -- T3   3.0989 A

T3  -- O7  -- T3  = 148.172 deg ; T3  -- T3   3.1049 A

T3  -- O8  -- T3  = 127.742 deg ; T3  -- T3   2.9081 A


        T-O-T SUMMARY
          Range  = 127.7416° <--> 173.8842 deg
          Mean   = 147.3314 deg
          StdDev = 12.9152 deg

        T--T SUMMARY
          Range  = 2.9081 A <--> 3.2242 A
          Mean   = 3.0882 A
          StdDev = 0.0913 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 43 66 90 121 165 212 253 298 363 437 498 560 643
TD10 = 990
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 25 40 63 95 129 161 198 255 316 365 419 491 577 652
TD10 = 983
Circuit symbol = 6.6_{2}.6.6_{2}.6_{2}.8_{4}
Weight = 29
Vertex symbol  = 6.6_{2}.6.6_{2}.6_{2}.8_{2}
Weight = 29

T3 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 38 61 87 118 160 206 249 296 358 430 495 559 638
TD10 = 955
Circuit symbol = 4.6.4.6.6_{2}.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6_{2}
Weight = 19

<TD10> = 976.000
Average ring size = 5.7778