Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_55_2_78_y8KOWE.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 22.08 T-atoms per nm^3
Material density = 2.203 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6183 Angstrom
T1  -- O2  = 1.6220 Angstrom
T1  -- O3  = 1.6182 Angstrom
T1  -- O4  = 1.6190 Angstrom
      mean = 1.6194 Angstrom
        t1 = 0.006088  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001118  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6198 Angstrom
T2  -- O4  = 1.6198 Angstrom
T2  -- O5  = 1.6192 Angstrom
T2  -- O6  = 1.6229 Angstrom
      mean = 1.6204 Angstrom
        t1 = 0.006724  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002006  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6182 A <--> 1.6229 A
          Mean   = 1.6199 A
          StdDev = 0.0016 A

       t1 Range  = 0.0061 <-- 0.0064 --> 0.0067
       t2 Range  = 0.0011 <-- 0.0016 --> 0.0020

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.590 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.564 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.284 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.407 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.830 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.152 deg; O3  -- O4  = 3 A
       109.152 deg <-- 109.471 deg --> 109.830 deg

O3  -- T2  -- O4  = 109.508 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.144 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.659 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 109.196 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.600 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 109.718 deg; O5  -- O6  = 3 A
       109.144 deg <-- 109.471 deg --> 109.718 deg

        O-T-O SUMMARY
          Range  = 109.1443 deg <--> 109.8296 deg
          Mean   = 109.4543 deg
          StdDev = 0.2245 deg

        O--O SUMMARY
          Range  = 2.6379 A <--> 2.6521 A
          Mean   = 2.6449 A
          StdDev = 0.0049 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 106.111 deg; T2  -- T1  = 4.9273 A
T2  - O1  - T1  - O3  - T2  = 112.824 deg; T2  -- T2  = 5.0967 A
T2  - O1  - T1  - O4  - T1  = 109.500 deg; T2  -- T1  = 4.9669 A
T1  - O2  - T1  - O3  - T2  = 126.015 deg; T1  -- T2  = 5.4798 A
T1  - O2  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.3233 A
T2  - O3  - T1  - O4  - T1  = 109.602 deg; T2  -- T1  = 4.9574 A

T1  - O3  - T2  - O4  - T1  = 106.411 deg; T1  -- T1  = 4.8994 A
T1  - O3  - T2  - O5  - T2  = 109.500 deg; T1  -- T2  = 4.9663 A
T1  - O3  - T2  - O6  - T2  = 126.922 deg; T1  -- T2  = 5.4893 A
T1  - O4  - T2  - O5  - T2  = 109.602 deg; T1  -- T2  = 4.9569 A
T1  - O4  - T2  - O6  - T2  = 112.562 deg; T1  -- T2  = 5.0908 A
T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.3019 A

        T-T-T SUMMARY
          Range  = 90.0000 deg <--> 126.9222 deg
          Mean   = 110.0902 deg
          StdDev = 10.4103 deg

        T--T SUMMARY
          Range  = 4.3019 A <--> 5.4893 A
          Mean   = 4.9856 A
          StdDev = 0.3329 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 146.376 deg ; T1  -- T1   3.0983 A

T1  -- O2  -- T1  = 136.694 deg ; T1  -- T1   3.0152 A

T1  -- O3  -- T2  = 142.568 deg ; T1  -- T2   3.0668 A

T1  -- O4  -- T2  = 140.834 deg ; T1  -- T2   3.0514 A

T2  -- O5  -- T2  = 142.782 deg ; T2  -- T2   3.0690 A

T2  -- O6  -- T2  = 136.490 deg ; T2  -- T2   3.0145 A


        T-O-T SUMMARY
          Range  = 136.4896° <--> 146.3758 deg
          Mean   = 140.9572 deg
          StdDev = 3.5355 deg

        T--T SUMMARY
          Range  = 3.0145 A <--> 3.0983 A
          Mean   = 3.0525 A
          StdDev = 0.0303 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 41 63 91 123 160 202 249 301 358 420 487 559 635
TD10 = 969
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 41 63 91 123 160 202 249 301 358 420 487 559 635
TD10 = 969
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

<TD10> = 969.000
Average ring size = 5.6000