Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_54_2_131404_5MzMbq.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 22.40 T-atoms per nm^3
Material density = 2.235 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6126 Angstrom
T1  -- O2  = 1.6170 Angstrom
T1  -- O3  = 1.6187 Angstrom
T1  -- O4  = 1.6166 Angstrom
      mean = 1.6162 Angstrom
        t1 = 0.012526  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.010319  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6169 Angstrom
T2  -- O3  = 1.6169 Angstrom
T2  -- O4  = 1.6187 Angstrom
T2  -- O4  = 1.6187 Angstrom
      mean = 1.6178 Angstrom
        t1 = 0.183294  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.133980  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6126 A <--> 1.6187 A
          Mean   = 1.6168 A
          StdDev = 0.0021 A

       t1 Range  = 0.0125 <-- 0.0979 --> 0.1833
       t2 Range  = 0.0103 <-- 0.0721 --> 0.1340

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.252 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 107.722 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 111.003 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 111.239 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 106.364 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 111.276 deg; O3  -- O4  = 3 A
       106.364 deg <-- 109.476 deg --> 111.276 deg

O3  -- T2  -- O3  = 131.097 deg; O3  -- O3  = 3 A
O3  -- T2  -- O4  =  79.836 deg; O3  -- O4  = 2 A
O3  -- T2  -- O4  =  80.474 deg; O3  -- O4  = 2 A
O3  -- T2  -- O4  =  80.474 deg; O3  -- O4  = 2 A
O3  -- T2  -- O4  =  79.836 deg; O3  -- O4  = 2 A
O4  -- T2  -- O4  = 131.202 deg; O4  -- O4  = 3 A
       79.836 deg <-- 97.153 deg --> 131.202 deg

        O-T-O SUMMARY
          Range  = 79.8359 deg <--> 131.2025 deg
          Mean   = 103.0564 deg
          StdDev = 18.5790 deg

        O--O SUMMARY
          Range  = 2.0763 A <--> 2.9483 A
          Mean   = 2.4993 A
          StdDev = 0.3256 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 109.226 deg; T1  -- T1  = 5.2660 A
T1  - O1  - T1  - O3  - T2  = 123.212 deg; T1  -- T2  = 5.4853 A
T1  - O1  - T1  - O4  - T2  = 115.374 deg; T1  -- T2  = 5.3986 A
T1  - O2  - T1  - O3  - T2  =  85.939 deg; T1  -- T2  = 4.2464 A
T1  - O2  - T1  - O4  - T2  = 113.896 deg; T1  -- T2  = 5.3467 A
T2  - O3  - T1  - O4  - T2  = 105.858 deg; T2  -- T2  = 4.9107 A

T1  - O3  - T2  - O3  - T1  = 103.816 deg; T1  -- T1  = 4.8439 A
T1  - O3  - T2  - O4  - T1  =  74.142 deg; T1  -- T1  = 3.7114 A
T1  - O3  - T2  - O4  - T1  = 174.830 deg; T1  -- T1  = 5.9941 A
T1  - O3  - T2  - O4  - T1  = 135.106 deg; T1  -- T1  = 5.8291 A
T1  - O3  - T2  - O4  - T1  =  74.142 deg; T1  -- T1  = 3.7114 A
T1  - O4  - T2  - O4  - T1  = 103.816 deg; T1  -- T1  = 4.8439 A

        T-T-T SUMMARY
          Range  = 74.1422 deg <--> 174.8304 deg
          Mean   = 109.9779 deg
          StdDev = 27.0064 deg

        T--T SUMMARY
          Range  = 3.7114 A <--> 5.9941 A
          Mean   = 4.9526 A
          StdDev = 0.7350 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 179.948 deg ; T1  -- T1   3.2252 A

T1  -- O2  -- T1  = 180.000 deg ; T1  -- T1   3.2341 A

T1  -- O3  -- T2  = 136.011 deg ; T1  -- T2   3.0001 A

T1  -- O4  -- T2  = 154.178 deg ; T1  -- T2   3.1535 A


        T-O-T SUMMARY
          Range  = 136.0108° <--> 180.0000 deg
          Mean   = 162.5343 deg
          StdDev = 18.8825 deg

        T--T SUMMARY
          Range  = 3.0001 A <--> 3.2341 A
          Mean   = 3.1532 A
          StdDev = 0.0953 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O3  -- O4  = 2.0763 A
O3  -- O4  = 2.0900 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 42 65 93 125 163 207 255 308 366 429 498 572 650
TD10 = 990
Circuit symbol = 4.8_{8}.6.6.6.6
Weight = 27
Vertex symbol  = 4.8_{8}.6.6.6.6
Weight = 27

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 24 42 64 90 126 166 206 252 306 368 432 496 568 650
TD10 = 985
Circuit symbol = 4.4.6.6.6.6
Weight = 19
Vertex symbol  = 4.4.6.6.6.6
Weight = 19

<TD10> = 988.333
Average ring size = 6.4000