Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_53_3_228721_2qa0AM.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 19.76 T-atoms per nm^3
Material density = 1.971 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6171 Angstrom
T1  -- O2  = 1.6149 Angstrom
T1  -- O3  = 1.6254 Angstrom
T1  -- O4  = 1.6115 Angstrom
      mean = 1.6172 Angstrom
        t1 = 0.006322  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004756  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6148 Angstrom
T2  -- O6  = 1.6115 Angstrom
T2  -- O4  = 1.6118 Angstrom
T2  -- O7  = 1.6117 Angstrom
      mean = 1.6124 Angstrom
        t1 = 0.004417  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003579  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O7  = 1.6118 Angstrom
T3  -- O8  = 1.6188 Angstrom
T3  -- O9  = 1.6155 Angstrom
T3  -- O10 = 1.6258 Angstrom
      mean = 1.6180 Angstrom
        t1 = 0.006610  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004485  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6115 A <--> 1.6258 A
          Mean   = 1.6159 A
          StdDev = 0.0050 A

       t1 Range  = 0.0044 <-- 0.0058 --> 0.0066
       t2 Range  = 0.0036 <-- 0.0043 --> 0.0048

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.820 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.048 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.228 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.392 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.146 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 110.181 deg; O3  -- O4  = 3 A
       108.820 deg <-- 109.469 deg --> 110.181 deg

O5  -- T2  -- O6  = 108.563 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 110.004 deg; O5  -- O4  = 3 A
O5  -- T2  -- O7  = 110.037 deg; O5  -- O7  = 3 A
O6  -- T2  -- O4  = 108.968 deg; O6  -- O4  = 3 A
O6  -- T2  -- O7  = 108.960 deg; O6  -- O7  = 3 A
O4  -- T2  -- O7  = 110.271 deg; O4  -- O7  = 3 A
       108.563 deg <-- 109.467 deg --> 110.271 deg

O7  -- T3  -- O8  = 109.271 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 108.998 deg; O7  -- O9  = 3 A
O7  -- T3  -- O10 = 110.177 deg; O7  -- O10 = 3 A
O8  -- T3  -- O9  = 108.980 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 110.047 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.344 deg; O9  -- O10 = 3 A
       108.980 deg <-- 109.469 deg --> 110.177 deg

        O-T-O SUMMARY
          Range  = 108.5631 deg <--> 110.2710 deg
          Mean   = 109.5060 deg
          StdDev = 0.5443 deg

        O--O SUMMARY
          Range  = 2.6195 A <--> 2.6586 A
          Mean   = 2.6382 A
          StdDev = 0.0118 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 117.203 deg; T1  -- T1  = 5.2714 A
T1  - O1  - T1  - O3  - T1  = 117.956 deg; T1  -- T1  = 5.4850 A
T1  - O1  - T1  - O4  - T2  = 105.023 deg; T1  -- T2  = 5.0500 A
T1  - O2  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.4044 A
T1  - O2  - T1  - O4  - T2  = 114.918 deg; T1  -- T2  = 5.2180 A
T1  - O3  - T1  - O4  - T2  = 111.757 deg; T1  -- T2  = 5.3100 A

T2  - O5  - T2  - O6  - T2  = 112.494 deg; T2  -- T2  = 5.3587 A
T2  - O5  - T2  - O4  - T1  = 107.949 deg; T2  -- T1  = 5.1911 A
T2  - O5  - T2  - O7  - T3  = 107.874 deg; T2  -- T3  = 5.1878 A
T2  - O6  - T2  - O4  - T1  = 114.918 deg; T2  -- T1  = 5.3991 A
T2  - O6  - T2  - O7  - T3  = 114.885 deg; T2  -- T3  = 5.3971 A
T1  - O4  - T2  - O7  - T3  =  97.519 deg; T1  -- T3  = 4.7951 A

T3  - O7  - T3  - O8  - T3  = 117.044 deg; T3  -- T3  = 5.2773 A
T3  - O7  - T3  - O9  - T2  = 105.055 deg; T3  -- T2  = 5.0564 A
T3  - O7  - T3  - O10 - T3  = 117.786 deg; T3  -- T3  = 5.4883 A
T3  - O8  - T3  - O9  - T2  = 114.885 deg; T3  -- T2  = 5.2196 A
T3  - O8  - T3  - O10 - T3  =  90.000 deg; T3  -- T3  = 4.4085 A
T2  - O9  - T3  - O10 - T3  = 112.099 deg; T2  -- T3  = 5.3212 A

        T-T-T SUMMARY
          Range  = 90.0000 deg <--> 117.9561 deg
          Mean   = 109.7964 deg
          StdDev = 7.7954 deg

        T--T SUMMARY
          Range  = 4.4044 A <--> 5.4883 A
          Mean   = 5.1796 A
          StdDev = 0.2734 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 158.109 deg ; T1  -- T1   3.1753 A

T1  -- O2  -- T1  = 173.838 deg ; T1  -- T1   3.2251 A

T1  -- O3  -- T1  = 134.643 deg ; T1  -- T1   2.9995 A

T1  -- O4  -- T2  = 163.288 deg ; T1  -- T2   3.1890 A

T2  -- O5  -- T2  = 179.497 deg ; T2  -- T2   3.2296 A

T2  -- O6  -- T2  = 172.137 deg ; T2  -- T2   3.2155 A

T2  -- O7  -- T3  = 162.979 deg ; T2  -- T3   3.1879 A

T3  -- O8  -- T3  = 158.948 deg ; T3  -- T3   3.1832 A

T3  -- O9  -- T3  = 174.112 deg ; T3  -- T3   3.2268 A

T3  -- O10 -- T3  = 134.978 deg ; T3  -- T3   3.0038 A


        T-O-T SUMMARY
          Range  = 134.6432° <--> 179.4970 deg
          Mean   = 161.2531 deg
          StdDev = 14.9118 deg

        T--T SUMMARY
          Range  = 2.9995 A <--> 3.2296 A
          Mean   = 3.1636 A
          StdDev = 0.0836 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 42 65 93 126 164 207 255 308 366 429 499 573 651
TD10 = 992
Circuit symbol = 4.6_{2}.6.6.6.6_{2}
Weight = 23
Vertex symbol  = 4.6_{2}.6.6.6.6_{2}
Weight = 23

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 25 42 65 92 126 164 206 256 309 368 431 498 572 650
TD10 = 993
Circuit symbol = 6.6_{2}.6.6_{2}.6_{2}.6_{2}
Weight = 25
Vertex symbol  = 6.6_{2}.6.6_{2}.6_{2}.6_{2}
Weight = 25

T3 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 42 65 93 126 164 207 255 308 366 429 499 573 651
TD10 = 992
Circuit symbol = 4.6_{2}.6.6.6.6_{2}
Weight = 23
Vertex symbol  = 4.6_{2}.6.6.6.6_{2}
Weight = 23

<TD10> = 992.333
Average ring size = 5.7778