Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_53_2_1422_Xpam6u.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 24.64 T-atoms per nm^3
Material density = 2.458 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6329 Angstrom
T1  -- O2  = 1.6146 Angstrom
T1  -- O3  = 1.6423 Angstrom
T1  -- O4  = 1.6464 Angstrom
      mean = 1.6341 Angstrom
        t1 = 0.020037  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.017503  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6239 Angstrom
T2  -- O4  = 1.6239 Angstrom
T2  -- O5  = 1.6316 Angstrom
T2  -- O6  = 1.5903 Angstrom
      mean = 1.6174 Angstrom
        t1 = 0.036147  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.038814  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5903 A <--> 1.6464 A
          Mean   = 1.6285 A
          StdDev = 0.0159 A

       t1 Range  = 0.0200 <-- 0.0281 --> 0.0361
       t2 Range  = 0.0175 <-- 0.0282 --> 0.0388

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 107.976 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 113.114 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.501 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.765 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 111.390 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 107.140 deg; O3  -- O4  = 3 A
       107.140 deg <-- 109.481 deg --> 113.114 deg

O4  -- T2  -- O4  = 103.294 deg; O4  -- O4  = 3 A
O4  -- T2  -- O5  = 116.436 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 105.734 deg; O4  -- O6  = 3 A
O4  -- T2  -- O5  = 116.436 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 105.734 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 108.239 deg; O5  -- O6  = 3 A
       103.294 deg <-- 109.312 deg --> 116.436 deg

        O-T-O SUMMARY
          Range  = 103.2938 deg <--> 116.4361 deg
          Mean   = 109.4003 deg
          StdDev = 4.3425 deg

        O--O SUMMARY
          Range  = 2.5469 A <--> 2.7674 A
          Mean   = 2.6528 A
          StdDev = 0.0787 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  99.386 deg; T1  -- T2  = 4.2791 A
T1  - O1  - T1  - O3  - T1  = 153.575 deg; T1  -- T1  = 5.5054 A
T1  - O1  - T1  - O4  - T1  = 115.913 deg; T1  -- T1  = 5.0489 A
T2  - O2  - T1  - O3  - T1  =  59.485 deg; T2  -- T1  = 2.8232 A
T2  - O2  - T1  - O4  - T1  = 122.536 deg; T2  -- T1  = 5.2523 A
T1  - O3  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.2695 A

T1  - O4  - T2  - O4  - T1  =  61.030 deg; T1  -- T1  = 2.8670 A
T1  - O4  - T2  - O5  - T2  = 146.644 deg; T1  -- T2  = 5.8318 A
T1  - O4  - T2  - O6  - T2  =  86.499 deg; T1  -- T2  = 4.1219 A
T1  - O4  - T2  - O5  - T2  = 146.644 deg; T1  -- T2  = 5.8318 A
T1  - O4  - T2  - O6  - T2  =  86.499 deg; T1  -- T2  = 4.1219 A
T2  - O5  - T2  - O6  - T2  = 108.239 deg; T2  -- T2  = 5.2214 A

        T-T-T SUMMARY
          Range  = 59.4849 deg <--> 153.5749 deg
          Mean   = 106.5689 deg
          StdDev = 30.4901 deg

        T--T SUMMARY
          Range  = 2.8232 A <--> 5.8318 A
          Mean   = 4.6107 A
          StdDev = 0.9865 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 117.236 deg ; T1  -- T1   2.7880 A

T1  -- O2  -- T1  = 156.866 deg ; T1  -- T1   3.1637 A

T1  -- O3  -- T1  = 121.582 deg ; T1  -- T1   2.8670 A

T1  -- O4  -- T2  = 119.372 deg ; T1  -- T2   2.8232 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2633 A

T2  -- O6  -- T2  = 180.000 deg ; T2  -- T2   3.1807 A


        T-O-T SUMMARY
          Range  = 117.2361° <--> 180.0000 deg
          Mean   = 139.0112 deg
          StdDev = 25.4699 deg

        T--T SUMMARY
          Range  = 2.7880 A <--> 3.2633 A
          Mean   = 2.9728 A
          StdDev = 0.1856 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.7880 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 19 37 65 99 136 179 230 284 345 413 487 567 653 741
TD10 = 1063
Circuit symbol = 3.6.4.6.5.7
Weight = 12
Vertex symbol  = 3.6.4.6.10_{5}.*
Weight = 30

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 40 65 92 130 176 220 276 338 402 474 554 636 726
TD10 = 1035
Circuit symbol = 3.10_{8}.6.10_{6}.6.10_{6}
Weight = 50
Vertex symbol  = 3.10_{8}.6.10_{6}.6.10_{6}
Weight = 50

<TD10> = 1053.667
Average ring size = 7.4545