Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_53_2_1316_YGvkUW.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 17.52 T-atoms per nm^3
Material density = 1.748 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6155 Angstrom
T1  -- O2  = 1.6234 Angstrom
T1  -- O3  = 1.6234 Angstrom
T1  -- O4  = 1.6621 Angstrom
      mean = 1.6311 Angstrom
        t1 = 0.015827  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006847  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6246 Angstrom
T2  -- O4  = 1.6246 Angstrom
T2  -- O5  = 1.6003 Angstrom
T2  -- O6  = 1.6004 Angstrom
      mean = 1.6125 Angstrom
        t1 = 0.024249  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.017430  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6003 A <--> 1.6621 A
          Mean   = 1.6249 A
          StdDev = 0.0188 A

       t1 Range  = 0.0158 <-- 0.0200 --> 0.0242
       t2 Range  = 0.0068 <-- 0.0121 --> 0.0174

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.593 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.597 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.600 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.233 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.900 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.897 deg; O3  -- O4  = 3 A
       108.233 deg <-- 109.470 deg --> 109.900 deg

O4  -- T2  -- O4  = 117.096 deg; O4  -- O4  = 3 A
O4  -- T2  -- O5  = 107.289 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 107.298 deg; O4  -- O6  = 3 A
O4  -- T2  -- O5  = 107.289 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 107.298 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 110.540 deg; O5  -- O6  = 3 A
       107.289 deg <-- 109.468 deg --> 117.096 deg

        O-T-O SUMMARY
          Range  = 107.2890 deg <--> 117.0963 deg
          Mean   = 109.4373 deg
          StdDev = 2.8568 deg

        O--O SUMMARY
          Range  = 2.5972 A <--> 2.7718 A
          Mean   = 2.6501 A
          StdDev = 0.0560 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 139.594 deg; T1  -- T2  = 5.6949 A
T1  - O1  - T1  - O3  - T1  = 112.570 deg; T1  -- T1  = 5.3829 A
T1  - O1  - T1  - O4  - T1  = 112.570 deg; T1  -- T1  = 5.3829 A
T2  - O2  - T1  - O3  - T1  =  89.595 deg; T2  -- T1  = 4.2906 A
T2  - O2  - T1  - O4  - T1  =  89.597 deg; T2  -- T1  = 4.2907 A
T1  - O3  - T1  - O4  - T1  = 108.551 deg; T1  -- T1  = 5.2611 A

T1  - O4  - T2  - O4  - T1  = 178.617 deg; T1  -- T1  = 5.6706 A
T1  - O4  - T2  - O5  - T2  =  90.395 deg; T1  -- T2  = 4.2906 A
T1  - O4  - T2  - O6  - T2  =  90.393 deg; T1  -- T2  = 4.2907 A
T1  - O4  - T2  - O5  - T2  =  90.395 deg; T1  -- T2  = 4.2906 A
T1  - O4  - T2  - O6  - T2  =  90.393 deg; T1  -- T2  = 4.2907 A
T2  - O5  - T2  - O6  - T2  = 110.540 deg; T2  -- T2  = 5.2611 A

        T-T-T SUMMARY
          Range  = 89.5955 deg <--> 178.6172 deg
          Mean   = 107.6334 deg
          StdDev = 27.4751 deg

        T--T SUMMARY
          Range  = 4.2906 A <--> 5.6949 A
          Mean   = 4.7967 A
          StdDev = 0.5909 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 179.989 deg ; T1  -- T1   3.2310 A

T1  -- O2  -- T1  = 172.729 deg ; T1  -- T1   3.2403 A

T1  -- O3  -- T1  = 172.763 deg ; T1  -- T1   3.2403 A

T1  -- O4  -- T2  = 119.246 deg ; T1  -- T2   2.8355 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2007 A

T2  -- O6  -- T2  = 180.000 deg ; T2  -- T2   3.2009 A


        T-O-T SUMMARY
          Range  = 119.2460° <--> 180.0000 deg
          Mean   = 164.9454 deg
          StdDev = 23.3725 deg

        T--T SUMMARY
          Range  = 2.8355 A <--> 3.2403 A
          Mean   = 3.1496 A
          StdDev = 0.1597 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 19 33 51 72 96 126 160 196 235 281 331 382 436 498
TD10 = 768
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.10_{2}
Weight = 26

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 8 16 30 48 66 92 128 158 182 230 294 330 354 430 528
TD10 = 733
Circuit symbol = 4.4.4.4.6_{2}.6_{2}
Weight = 9
Vertex symbol  = 4.4.4.4.10_{2}.*
Weight = 21

<TD10> = 756.333
Average ring size = 5.5556