Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_51_3_48024_BIk8SB.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 19.80 T-atoms per nm^3
Material density = 1.976 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6222 Angstrom
T1  -- O2  = 1.6162 Angstrom
T1  -- O3  = 1.6189 Angstrom
T1  -- O4  = 1.6186 Angstrom
      mean = 1.6190 Angstrom
        t1 = 0.006063  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002240  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6180 Angstrom
T2  -- O5  = 1.6189 Angstrom
T2  -- O7  = 1.6216 Angstrom
T2  -- O6  = 1.6213 Angstrom
      mean = 1.6199 Angstrom
        t1 = 0.006262  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000952  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6180 Angstrom
T3  -- O6  = 1.6215 Angstrom
T3  -- O8  = 1.6213 Angstrom
T3  -- O7  = 1.6217 Angstrom
      mean = 1.6206 Angstrom
        t1 = 0.006635  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000784  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6162 A <--> 1.6222 A
          Mean   = 1.6199 A
          StdDev = 0.0019 A

       t1 Range  = 0.0061 <-- 0.0063 --> 0.0066
       t2 Range  = 0.0008 <-- 0.0013 --> 0.0022

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.650 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.736 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.785 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.119 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.194 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.339 deg; O3  -- O4  = 3 A
       109.119 deg <-- 109.471 deg --> 109.785 deg

O3  -- T2  -- O5  = 109.589 deg; O3  -- O5  = 3 A
O3  -- T2  -- O7  = 109.666 deg; O3  -- O7  = 3 A
O3  -- T2  -- O6  = 109.406 deg; O3  -- O6  = 3 A
O5  -- T2  -- O7  = 109.144 deg; O5  -- O7  = 3 A
O5  -- T2  -- O6  = 109.583 deg; O5  -- O6  = 3 A
O7  -- T2  -- O6  = 109.438 deg; O7  -- O6  = 3 A
       109.144 deg <-- 109.471 deg --> 109.666 deg

O4  -- T3  -- O6  = 109.540 deg; O4  -- O6  = 3 A
O4  -- T3  -- O8  = 109.393 deg; O4  -- O8  = 3 A
O4  -- T3  -- O7  = 109.690 deg; O4  -- O7  = 3 A
O6  -- T3  -- O8  = 109.408 deg; O6  -- O8  = 3 A
O6  -- T3  -- O7  = 109.428 deg; O6  -- O7  = 3 A
O8  -- T3  -- O7  = 109.368 deg; O8  -- O7  = 3 A
       109.368 deg <-- 109.471 deg --> 109.690 deg

        O-T-O SUMMARY
          Range  = 109.1187 deg <--> 109.7849 deg
          Mean   = 109.4659 deg
          StdDev = 0.1941 deg

        O--O SUMMARY
          Range  = 2.6357 A <--> 2.6513 A
          Mean   = 2.6452 A
          StdDev = 0.0043 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 127.582 deg; T1  -- T2  = 5.6363 A
T1  - O1  - T1  - O3  - T3  = 123.149 deg; T1  -- T3  = 5.5449 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.4257 A
T2  - O2  - T1  - O3  - T3  = 104.299 deg; T2  -- T3  = 4.8648 A
T2  - O2  - T1  - O4  - T1  =  90.101 deg; T2  -- T1  = 4.3263 A
T3  - O3  - T1  - O4  - T1  = 113.822 deg; T3  -- T1  = 5.1408 A

T1  - O3  - T2  - O5  - T3  = 128.581 deg; T1  -- T3  = 5.4732 A
T1  - O3  - T2  - O7  - T2  =  89.899 deg; T1  -- T2  = 4.3263 A
T1  - O3  - T2  - O6  - T3  = 133.216 deg; T1  -- T3  = 5.5880 A
T3  - O5  - T2  - O7  - T2  = 114.439 deg; T3  -- T2  = 5.0952 A
T3  - O5  - T2  - O6  - T3  =  78.656 deg; T3  -- T3  = 3.8184 A
T2  - O7  - T2  - O6  - T3  = 114.319 deg; T2  -- T3  = 5.1034 A

T1  - O4  - T3  - O6  - T3  = 113.822 deg; T1  -- T3  = 5.1271 A
T1  - O4  - T3  - O8  - T2  = 105.267 deg; T1  -- T2  = 4.8463 A
T1  - O4  - T3  - O7  - T2  = 122.229 deg; T1  -- T2  = 5.3511 A
T3  - O6  - T3  - O8  - T2  = 114.439 deg; T3  -- T2  = 5.0722 A
T3  - O6  - T3  - O7  - T2  = 114.319 deg; T3  -- T2  = 5.0804 A
T2  - O8  - T3  - O7  - T2  =  81.717 deg; T2  -- T2  = 3.9414 A

        T-T-T SUMMARY
          Range  = 78.6564 deg <--> 133.2160 deg
          Mean   = 108.3466 deg
          StdDev = 16.0155 deg

        T--T SUMMARY
          Range  = 3.8184 A <--> 5.6363 A
          Mean   = 4.9111 A
          StdDev = 0.5320 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 139.494 deg ; T1  -- T1   3.0439 A

T1  -- O2  -- T1  = 167.387 deg ; T1  -- T1   3.2128 A

T1  -- O3  -- T2  = 142.926 deg ; T1  -- T2   3.0690 A

T1  -- O4  -- T3  = 145.612 deg ; T1  -- T3   3.0919 A

T2  -- O5  -- T2  = 141.281 deg ; T2  -- T2   3.0547 A

T2  -- O6  -- T3  = 137.211 deg ; T2  -- T3   3.0194 A

T2  -- O7  -- T3  = 135.847 deg ; T2  -- T3   3.0055 A

T3  -- O8  -- T3  = 138.014 deg ; T3  -- T3   3.0274 A


        T-O-T SUMMARY
          Range  = 135.8470° <--> 167.3868 deg
          Mean   = 143.4714 deg
          StdDev = 9.5920 deg

        T--T SUMMARY
          Range  = 3.0055 A <--> 3.2128 A
          Mean   = 3.0656 A
          StdDev = 0.0619 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 22 39 58 81 110 146 187 229 274 327 388 451 514 582
TD10 = 887
Circuit symbol = 4.6.4.8_{4}.6.6_{2}
Weight = 22
Vertex symbol  = 4.6.4.8_{2}.6_{2}.8
Weight = 27

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 20 37 61 84 108 145 191 234 273 320 386 457 518 578
TD10 = 895
Circuit symbol = 4.4.6.6_{3}.6_{3}.8_{6}
Weight = 24
Vertex symbol  = 4.4.6.6_{3}.6_{3}.8_{2}
Weight = 24

T3 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 22 36 57 85 115 146 181 227 281 333 385 442 512 591
TD10 = 885
Circuit symbol = 4.8_{4}.6.6_{2}.6_{2}.6_{2}
Weight = 26
Vertex symbol  = 4.8_{4}.6.6_{2}.6_{2}.6_{2}
Weight = 26

<TD10> = 889.000
Average ring size = 5.9520